Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it.

From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown.

Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively).

The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001).

We carried out a retrospective review of 47 intra-articular fractures of the calcaneum treated by open reduction and internal fixation in 45 patients by a single surgeon between 1993 and 2001. The fractures were evaluated before operation by plain radiographs and a CT scan using Sanders’ classification. Osteosynthesis involved a lateral approach and the use of the AO calcaneal plate. The mean follow-up was for ten years (7 to 15). Clinical assessment included the American Orthopaedic Foot and Ankle Society Score (AOFAS), the Creighton-Nebraska Score, the Kerr, Prothero, Atkins Score and the SF-36 Health Questionnaire. The radiological evaluation consisted of lateral and axial views of the os calcis. Arthritic changes in the subtalar joint were assessed with an internal oblique view and were graded using the Morrey and Wiedeman scale.

There were 18 excellent (38.3%), 17 good (36.2%), three fair (6.3%) and nine poor (19.2%) results. Five patients had a superficial wound infection and five others eventually had a subtalar arthrodesis because of continuing pain. Restoration of Böhler’s angle was associated with a better outcome. The degree of arthritic change in the subtalar joint did not correlate with the outcome scores or Sanders’ classification. Prompt osteosynthesis should be considered for intra-articular fractures of the calcaneum in order to restore the shape of the hindfoot and Böhler’s angle.

We systematically reviewed the peer-reviewed literature to relate the survival of hybrid metal-on-metal hip resurfacing arthroplasty devices to a National Institute of Clinical Excellence (NICE) benchmark for choosing a primary total hip replacement, which is a survival rate of 90% at a follow-up of ten years.

A total of 29 articles (10 621 resurfaced hips) met the inclusion criteria. The mean follow-up ranged from 0.6 to 10.5 years and the survival of the implant ranged from 84% to 100%. Of the 10 621 hips, 370 were revised (3.5%), with aseptic loosening as the most frequent mode of failure.

None of the hip resurfacing arthroplasty implants used to date met the full ten-year NICE benchmark of survival. A total of 13 studies showed satisfactory survival compared with the three-year NICE benchmark.

As metal-on-metal arthroplasty becomes more widespread, concerns are being raised about the potential dangers of metal particulate debris. We present the case of a benign psoas mass secondary to the presence of such particles. The mass was excised and the hip resurfacing subsequently revised to a total hip replacement.

We have updated our previous randomised controlled trial comparing release of chromium (Cr) and cobalt (Co) ions and included levels of titanium (Ti) ions. We have compared the findings from 28 mm metal-on-metal total hip replacement, performed using titanium CLS/Spotorno femoral components and titanium AlloFit acetabular components with Metasul bearings, with Durom hip resurfacing using a Metasul articulation or bearing and a titanium plasma-sprayed coating for fixation of the acetabular component.

Although significantly higher blood ion levels of Cr and Co were observed at three months in the resurfaced group than in total hip replacement, no significant difference was found at two years post-operatively for Cr, 1.58 μg/L and 1.62 μg/L respectively (p = 0.819) and for Co, 0.67 μg/L and 0.94 μg/L respectively (p = 0.207). A steady state was reached at one year in the resurfaced group and after three months in the total hip replacement group. Interestingly, Ti, which is not part of the bearing surfaces with its release resulting from metal corrosion, had significantly elevated ion levels after implantation in both groups. The hip resurfacing group had significantly higher Ti levels than the total hip replacement group for all periods of follow-up. At two years the mean blood levels of Ti ions were 1.87 μg/L in hip resurfacing and and 1.30 μg/L in total hip replacement (p = 0.001).

The study confirms even with different bearing diameters and clearances, hip replacement and 28 mm metal-on-metal total hip replacement produced similar Cr and Co metal ion levels in this randomised controlled trial study design, but apart from wear on bearing surfaces, passive corrosion of exposed metallic surfaces is a factor which influences ion concentrations. Ti plasma spray coating the acetabular components for hip resurfacing produces significantly higher release of Ti than Ti grit-blasted surfaces in total hip replacement.

Between April 1999 and April 2004, 3497 Birmingham hips were inserted by 89 surgeons. Fracture of the neck of the femur occurred in 50 patients, an incidence of 1.46%. Complete data were available for 45 patients in whom the incidence was 1.91% for women and 0.98% for men. The relative risk of fracture for women vs men was 1.94961 and this was statistically significant (p < 0.01).

The mean time to fracture was 15.4 weeks. In women the fractures occurred at a mean of 18.5 weeks and were more likely to have been preceded by a pro-dromal phase of pain and limping. In men the mean time to fracture was 13.5 weeks.

Significant varus placement of the femoral component, intra-operative notching of the femoral neck and technical problems were common factors in 85% of cases.

The management of patients with a painful total knee replacement requires careful assessment and a stepwise approach in order to diagnose the underlying pathology accurately. The management should include a multidisciplinary approach to the patient’s pain as well as addressing the underlying aetiology. Pain should be treated with appropriate analgesia, according to the analgesic ladder of the World Health Organisation. Special measures should be taken to identify and to treat any neuropathic pain. There are a number of intrinsic and extrinsic causes of a painful knee replacement which should be identified and treated early. Patients with unexplained pain and without any recognised pathology should be treated conservatively since they may improve over a period of time and rarely do so after a revision operation.

We examined whether a selective cyclooxygenase-2 (COX-2) inhibitor (celecoxib) was as effective as a non-selective inhibitor (ibuprofen) for the prevention of heterotopic ossification following total hip replacement. A total of 250 patients were randomised to receive celecoxib (200 mg b/d) or ibuprofen (400 mg t.d.s) for ten days after surgery. Anteroposterior radiographs of the pelvis were examined for heterotopic ossification three months after surgery. Of the 250 patients, 240 were available for assessment. Heterotopic ossification was more common in the ibuprofen group (none 40.7% (50), Brooker class I 46.3% (57), classes II and III 13.0% (16)) than in the celecoxib group (none 59.0% (69), Brooker class I 35.9% (42), classes II and III 5.1% (6), p = 0.002). Celecoxib was more effective than ibuprofen in preventing heterotopic bone formation after total hip replacement.

This is a longitudinal study of the daily urinary output and the concentrations in whole blood of cobalt and chromium in patients with metal-on-metal resurfacings over a period of four years.

Twelve-hour urine collections and whole blood specimens were collected before and periodically after a Birmingham hip resurfacing in 26 patients. All ion analyses were carried out using a high-resolution inductively-coupled plasma mass spectrometer. Clinical and radiological assessment, hip function scoring and activity level assessment revealed excellent hip function.

There was a significant early increase in urinary metal output, reaching a peak at six months for cobalt and one year for chromium post-operatively. There was thereafter a steady decrease in the median urinary output of cobalt over the following three years, although the differences are not statistically significant. The mean whole blood levels of cobalt and chromium also showed a significant increase between the pre-operative and one-year post-operative periods. The blood levels then decreased to a lower level at four years, compared with the one-year levels. This late reduction was statistically significant for chromium but not for cobalt.

The effects of systemic metal ion exposure in patients with metal-on-metal resurfacing arthroplasties continue to be a matter of concern. The levels in this study provide a baseline against which the in vivo wear performance of newer bearings can be compared.

Evaluation of patients with painful total knee replacement requires a thorough clinical examination and relevant investigations in order to reach a diagnosis. Awareness of the common and uncommon problems leading to painful total knee replacement is useful in the diagnostic approach. This review article aims to act as a guide to the evaluation of patients with painful total knee replacement.

We prospectively studied the outcome of a protocol of prophylaxis for deep vein thrombosis (DVT) in 103 consecutive patients undergoing surgical stabilisation of pelvic and acetabular fractures. Low-molecular-weight heparin (LMWH) was administered within 24 hours of injury or on achieving haemodynamic stability. Patients were screened for proximal DVT by duplex ultrasonography performed ten to 14 days after surgery.

The incidence of proximal DVT was 10% and of pulmonary embolus 5%. Proximal DVT developed in two of 64 patients (3%) who had received LMWH within 24 hours of injury, but in eight of 36 patients (22%) who received LMWH more than 24 hours after the injury (p < 0.01). We conclude that LMWH, when begun without delay, is a safe and effective method of thromboprophylaxis in high-risk patients with major pelvic or acetabular fractures.

The effects of the method of fixation and interface conditions on the biomechanics of the femoral component of the Birmingham hip resurfacing arthroplasty were examined using a highly detailed three-dimensional computer model of the hip. Stresses and strains in the proximal femur were compared for the natural femur and for the femur resurfaced with the Birmingham hip resurfacing. A comparison of cemented versus uncemented fixation showed no advantage of either with regard to bone loading. When the Birmingham hip resurfacing femoral component was fixed to bone, proximal femoral stresses and strains were non-physiological. Bone resorption was predicted in the inferomedial and superolateral bone within the Birmingham hip resurfacing shell. Resorption was limited to the superolateral region when the stem was not fixed. The increased bone strain observed adjacent to the distal stem should stimulate an increase in bone density at that location. The remodelling of bone seen during revision of failed Birmingham hip resurfacing implants appears to be consistent with the predictions of our finite element analysis.

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant.

We evaluated the concentrations of chromium and cobalt ions in blood after metal-on-metal surface replacement arthroplasty using a wrought-forged, high carbon content chromium-cobalt alloy implant in 64 patients. At one year, mean whole blood ion levels were 1.61 μg/L (0.4 to 5.5) for chromium and 0.67 μg/L (0.23 to 2.09) for cobalt. The pre-operative ion levels, component size, female gender and the inclination of the acetabular component were inversely proportional to the values of chromium and/or cobalt ions at one year postoperatively. Other factors, such as age and level of activity, did not correlate with the levels of metal ions. We found that the levels of the ions in the serum were 1.39 and 1.37 times higher for chromium and cobalt respectively than those in the whole blood.

The levels of metal ions obtained may be specific to the hip resurfacing implant and reflect its manufacturing process.

Human bone-marrow mesenchymal stem cells have an important role in the repair of musculoskeletal tissues by migrating from the bone marrow into the injured site and undergoing differentiation. We investigated the use of autologous human serum as a substitute for fetal bovine serum in the ex vivo expansion medium to avoid the transmission of dangerous transfectants during clinical reconstruction procedures.

Autologous human serum was as effective in stimulating growth of bone-marrow stem cells as fetal bovine serum. Furthermore, medium supplemented with autologous human serum was more effective in promoting motility than medium with fetal bovine serum in all cases. Addition of B-fibroblast growth factor to medium with human serum stimulated growth, but not motility. Our results suggest that autologous human serum may provide sufficient ex vivo expansion of human bone-marrow mesenchymal stem cells possessing multidifferentiation potential and may be better than fetal bovine serum in preserving high motility.