We describe two cases of fracture of Corin Taper-Fit stems used for cement-in-cement revision of congenital dysplasia of the hip. Both prostheses were implanted in patients in their 50s, with high offsets (+7.5 mm and +3.5 mm), one with a large diameter (48 mm) head and one with a constrained acetabular component. Fracture of the stems took place at nine months and three years post-operatively following low-demand activity. Both fractures occurred at the most medial of the two stem introducer holes in the neck of the prosthesis, a design feature that is unique to the Taper-Fit stem. We would urge caution in the use of these particular stems for cement-in-cement revisions.

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.

This is a longitudinal study of the daily urinary output and the concentrations in whole blood of cobalt and chromium in patients with metal-on-metal resurfacings over a period of four years.

Twelve-hour urine collections and whole blood specimens were collected before and periodically after a Birmingham hip resurfacing in 26 patients. All ion analyses were carried out using a high-resolution inductively-coupled plasma mass spectrometer. Clinical and radiological assessment, hip function scoring and activity level assessment revealed excellent hip function.

There was a significant early increase in urinary metal output, reaching a peak at six months for cobalt and one year for chromium post-operatively. There was thereafter a steady decrease in the median urinary output of cobalt over the following three years, although the differences are not statistically significant. The mean whole blood levels of cobalt and chromium also showed a significant increase between the pre-operative and one-year post-operative periods. The blood levels then decreased to a lower level at four years, compared with the one-year levels. This late reduction was statistically significant for chromium but not for cobalt.

The effects of systemic metal ion exposure in patients with metal-on-metal resurfacing arthroplasties continue to be a matter of concern. The levels in this study provide a baseline against which the in vivo wear performance of newer bearings can be compared.

Primary uncemented femoral stems reported to the Norwegian arthroplasty register between 1987 and 2005 were included in this prospective observational study. There were 11 516 hips (9679 patients) and 14 different designs of stem. Kaplan-Meier survival probabilities and Cox regression were used to analyse the data.

With aseptic loosening as the end-point, all currently used designs performed excellently with survival of 96% to 100% at ten years. With the end-point as stem revision for any cause, the long-term results of the different designs varied from poor to excellent, with survival at 15 years ranging between 29% and 97%. Follow-up for longer than seven years was needed to identify some of the poorly-performing designs. There were differences between the stems; the Corail, used in 5456 hips, was the most frequently used stem with a survival of 97% at 15 years. Male gender was associated with an increased risk of revision of × 1.3 (95% confidence interval 1.05 to 1.52), but age and diagnosis had no influence on the results. Overall, modern uncemented femoral stems performed well.

Moderate differences in survival between well-performing stems should be interpreted with caution since the differences may be caused by factors other than the stem itself.