Seven psoas bursae filled with purulent fluid and inspissated debris were revealed at revision operations for failed resurfacing hip arthroplasties, an incidence of 5.8% in such revisions. Histological and microbiological investigations demonstrated that the psoas bursa collections resulted from the tissue response to polyethylene wear debris. None was due to infection

Aims

Adult patients with history of childhood infection pose a surgical challenge for total hip arthroplasty (THA) due to distorted bony anatomy, soft-tissue contractures, risk of reinfection, and relatively younger age. Therefore, the purpose of the present study was to determine clinical outcome, reinfection rate, and complications in patients with septic sequelae after THA.

We retrieved 159 femoral heads at revision surgery to determine changes in surface configuration. Macroscopic wear of the head was observed in three bipolar hip prostheses as a result of three-body wear. There was a considerable change in surface roughness in the internal articulation of bipolar hip prostheses. Roughness in alumina heads was almost the same as that in new cobalt-chromium heads. The annual linear wear rate of polyethylene cups with alumina heads was less than that of cups with cobalt-chromium alloy heads. Polyethylene wear was increased in the prostheses which had increased roughness of the head

Aims

Return to sport following undergoing total (TKA) and unicompartmental knee arthroplasty (UKA) has been researched with meta-analyses and systematic reviews of varying quality. The aim of this study is to create an umbrella review to consolidate the data into consensus guidelines for returning to sports following TKA and UKA.

At yearly intervals we compared the radiological wear characteristics of 81 alumina ceramic femoral heads with a well-matched group of 43 cobalt-chrome femoral heads. Using a computer-assisted measurement system we assessed two-dimensional penetration of the head into the polyethylene liner. We used linear regression analysis of temporal data of the penetration of the head to calculate the true rates of polyethylene wear for both groups. At a mean of seven years the true rate of wear of the ceramic group was slightly greater (0.09 mm/year, SD 0.07) than that of the cobalt-chrome group (0.07 mm/year, SD 0.04). Despite the numerous theoretical advantages of ceramic over cobalt-chrome femoral heads, the wear performance in vivo of these components was similar

We report a high rate of failure of the Ring polyethylene cementless cup caused largely by granulomatous osteolysis. We have reviewed 126 prostheses inserted from 1986 to 1992 at from 11 to 90 months after surgery. There was radiological evidence of osteolytic granulomas adjacent to the external surface of the cup in 32%, appearing on average at three years from operation. In a subgroup of 59 prostheses followed for at least four years the incidence of such changes was 54%. A total of 27 cups (22%) have required revision, 21 for granulomatous loosening at an average follow-up of five years. In the retrieved prostheses there was obvious polyethylene abrasion and histological examination confirmed the presence of polyethylene wear debris. We found no significant correlation of osteolysis with cup size, although smaller cups were predominant among those having revision

Dislocation following total hip arthroplasty (THA) is a well-known and potentially devastating complication. Clinicians have used many strategies in attempts to prevent dislocation since the introduction of THA. While the importance of postoperative care cannot be ignored, particular emphasis has been placed on preoperative planning in the prevention of dislocation. The strategies have progressed from more traditional approaches, including modular implants, the size of the femoral head, and augmentation of the offset, to newer concepts, including patient-specific component positioning combined with computer navigation, robotics, and the use of dual-mobility implants. As clinicians continue to pursue improved outcomes and reduced complications, these concepts will lay the foundation for future innovation in THA and ultimately improved outcomes.

Cite this article: Bone Joint J 2022;104-B(1):8–11.

We present a prospective review of the outcome of 76 Lubinus patellofemoral arthroplasties carried out in 59 patients between 1989 and 1995. At a mean follow-up of 7.5 years, 62 knees in the 48 patients were reviewed; 11 patients (14 knees) had died. None was lost to follow-up. The clinical outcome using the Bristol Knee Scoring system was satisfactory in 45% of the cases. Maltracking of the patella, resulting in lateral tilt, subluxation and polyethylene wear, was the most common complication (32%). Revision surgery was carried out in 21 knees (28%) giving a cumulative survival rate of 65% (confidence interval (CI) 49 to 77) at eight years. The survival rate for revision and moderate pain was 48% (CI 36 to 59) at six years. Progression of arthritis was seen in seven cases (9%). In five of these (6.5%), the symptoms were severe enough to need revision surgery. Due to the high proportion of unsatisfactory results, we have discontinued the use of this prosthesis

Aims

Medial pivot (MP) total knee arthroplasties (TKAs) were designed to mimic native knee kinematics with their deep medial congruent fitting of the tibia to the femur almost like a ball-on-socket, and a flat lateral part. GMK Sphere is a novel MP implant. Our primary aim was to study the migration pattern of the tibial tray of this TKA.

We compared wear particles from two different designs of total hip arthroplasty with polycrystalline alumina-ceramic bearings of different production periods (group 1, before ISO 6474: group 2, according to ISO 6474). The neocapsules and interfacial connective tissue membranes were retrieved after mean implantation times of 131 months and 38 months, respectively. Specimen blocks were freed from embedding media, either methylmethacrylate or paraffin and digested in concentrated nitric acid. Particles were then counted and their sizes and composition determined by SEM and energy-dispersive x-ray analysis (EDXA). The mean numbers and sizes of most alumina wear particles did not differ for both production periods, but the larger sizes of particle in group 1 point to more severe surface destruction. The increased metal wear in group 2 was apparently due to alumina-induced abrasion of the stems. In this study the concentrations of particles in the periprosthetic tissues were 2 to 22 times lower than those observed previously with polyethylene and alumina/polyethylene wear couples

We carried out weight-bearing video radiological studies on 40 patients with a total knee arthroplasty (TKA), to determine the presence and magnitude of femoral condylar lift-off. Half (20) had posterior-cruciate-retaining (PCR) and half (20) posterior-cruciate-substituting (PS) prostheses. The selected patients had successful arthroplasties with no pain or instability. Each carried out successive weight-bearing knee bends to maximum flexion, and the radiological video tapes were analysed using an interactive model-fitting technique. Femoral lift-off was seen at some increment of knee flexion in 75% of patients (PCR TKA 70%; PS TKA 80%). The mean values for lift-off were 1.2 mm with a PCR TKA and 1.4 mm with a PS TKA. Lift-off occurred mostly laterally with the PCR TKA, and both medially and laterally with the PS TKA. Separation between the femoral condyles and the articular surface of the tibia was recorded at 0°, 30°, 60° and 90° of flexion. Femoral condylar lift-off may contribute to eccentric polyethylene wear, particularly in designs of TKA which have flatter condyles. Coronal conformity is an important consideration in the design of a TKA

Aims

This study aimed to investigate the relationship between changes in patellar height and clinical outcomes at a mean follow-up of 7.7 years (5 to 10) after fixed-bearing posterior-stabilized total knee arthroplasty (PS-TKA).

Retrieval studies have shown that the use of fully congruent meniscal bearings reduces wear in knee replacements. We report the outcome of 143 knees with anteromedial osteoarthritis and normal anterior cruciate ligaments treated by unicompartmental arthroplasty using fully congruous mobile polyethylene bearings. At review, 34 knees were in patients who had died and 109 were in those who were still living. The mean elapsed time since operation was 7.6 years (maximum 13.8). We established the status of all but one knee. There had been five revision operations giving a cumulative prosthetic survival rate at ten years (33 knees at risk) of 98% (95% CI 93% to 100%). Considering the knee lost to follow-up as a failure, the ‘worst-case’ survival rate was 97%. No failures were due to polyethylene wear or aseptic loosening of the tibial component. One bearing which dislocated at four years was reduced by closed manipulation. The ten-year survival rate is the best of those reported for unicompartmental arthroplasty and not significantly different from the best rates for total knee replacement

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

In laboratory tests, the ultra-high molecular weight polyethylene used for the acetabular cups of Charnley hip prostheses has a very low wear rate against steel. In the body radiographic measurements indicate that the polyethylene wears more rapidly. In order to investigate this higher wear rate, the sockets of acetabular cups removed at post-mortem have been examined using optical and electron microscopy. It has been shown that a socket wears predominantly on its superior part and that this is a direct consequence of the orientation of the cup in the body and the direction of loading of the hip. In the worn region the femoral head in effect bores out a new socket for itself, a process which is visible with the naked eye after approximately eight years. Electron microscopy shows that the predominant wear mechanism is adhesion, but after about eight years the appearance of surface cracks suggests that surface fatigue is taking place in addition to this. Laboratory wear tests have shown that pure surface fatigue is not sufficient to account for the high clinical wear rate. Other deformation processes are suggested and discussed with regard to the higher clinical wear rate

We analysed in-vivo migration and wear over a long period of all-polyethylene acetabular cups which had not been affected by mechanical loosening. The selection criteria of regular radiological follow-up, good clinical outcome (Charnley score of 5 or 6), continued walking without crutches and no radiological signs of loosening of the acetabular cups were fulfilled by 25 Charnley total hip arthroplasties. Mean migration, measured by the Nunn method, was 0.6 mm in the medial and 0.2 mm in the cranial direction. The mean yearly rate of wear was 0.05 mm and 0.04 mm, with six and two cups having no detectable wear, as measured by the Livermore and Charnley-Cupic methods, respectively. The maximal detected wear was 3.7 mm. There were no changes in the rate of wear with time. Computerised Ein Bild Röntgen Analyse (single-image radiological analysis) measurements of 20 hips indicated plastic deformation of the cups. We conclude that long-term successful cups do not migrate and have a very low rate of wear which was not affected by ageing of the polyethylene. There was no evidence that polyethylene wear alone caused mechanical loosening of the cup but high rates of wear seem to have an adverse prognostic value in terms of the long-term survival of the prosthesis

From 1981 to 1983, we implanted Bioceram type-4 and type-5 prostheses in 61 hips in 54 patients with osteoarthritis secondary to acetabular dysplasia, congenital subluxation, or congenital dislocation of the hip. Fifty-seven hips in 50 patients were followed for a mean of 11.1 years (10 to 13). The mean age of the patients at operation was 53 years (31 to 70). Functional evaluation using the Merle d'Aubigne and Postel hip score showed a 77% success rate. Radiological loosening occurred in three femoral (5%) and 16 acetabular components (28%). Autologous femoral head grafts were used in 18 hips and became incorporated, giving mechanical support to the socket except for one which occupied a large weight-bearing area and eventually collapsed. The mean polyethylene wear was 1.1 mm (0 to 3.6) and the mean wear rate was 0.10 mm/year (0 to 0.31). A high rate of wear correlated with calcar resorption (p > 0.002) but not with acetabular loosening. There was no breakage of a ceramic head. Study of the ceramic heads and polyethylene sockets retrieved after ten years showed excellent surface roughness, sphericity, and bending strength for the heads but scratches and voids were seen on the sockets

Aims

The aim of our study was to investigate the effect of asymmetric crosslinked polyethylene liner use on the risk of revision of cementless and hybrid total hip arthroplasties (THAs).