Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart. Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design. Bone Joint Res 2017;6:–350. DOI: 10.1302/2046-3758.65.BJR-2016-0325.R1

Cemented femoral stems with force closed fixation designs have shown good clinical results despite high early subsidence. A new triple-tapered stem in this category (C-stem AMT) was introduced in 2005. This study compares this new stem with an established stem of similar design (Exeter) in terms of migration (as measured using radiostereometric analysis), peri-prosthetic bone remodelling (measured using dual energy x-ray densitometry, DXA), Oxford Hip Score, and plain radiographs.

A total of 70 patients (70 hips) with a mean age of 66 years (53 to 78) were followed for two years. Owing to missing data of miscellaneous reasons, the final analysis represents data from 51 (RSA) and 65 (DXA) patients. Both stems showed a typical pattern of migration: Subsidence and retroversion that primarily occurred during the first three months. C-stem AMT subsided less during the first three months (p = 0.01), before stabilising at a subsidence rate similar to the Exeter stem from years one to two. The rate of migration into retroversion was slightly higher for C-stem AMT during the second year (p = 0.03). Whilst there were slight differences in movement patterns between the stems, the C-stem AMT exhibits good early clinical outcomes and displays a pattern of migration and bone remodelling that predicts good clinical performance.

Cite this article: Bone Joint J 2015;97-B:755–61.

Aims

Periprosthetic hip fractures (PPFs) after total hip arthroplasty are difficult to treat. Therefore, it is important to identify modifiable risk factors such as stem selection to reduce the occurrence of PPFs. This study aimed to clarify differences in fracture torque, surface strain, and fracture type analysis between three different types of cemented stems.

Aims

Periprosthetic fracture (PF) after primary total hip arthroplasty (THA) is an uncommon but potentially devastating complication. This study aims to investigate the influence of cemented stem designs on the risk of needing a revision for a PF.

Aims. Highly polished stems with force-closed design have shown satisfactory clinical results despite being related to relatively high early migration. It has been suggested that the minimal thickness of cement mantles surrounding the femoral stem should be 2 mm to 4 mm to avoid aseptic loosening. The line-to-line cementing technique of the femoral stem, designed to achieve stem press-fit, challenges this opinion. We compared the migration of a highly polished stem with force-closed design by standard and line-to-line cementing to investigate whether differences in early migration of the stems occur in a clinical study. Methods. In this single-blind, randomized controlled, clinical radiostereometric analysis (RSA) study, the migration pattern of the cemented Corail hip stem was compared between line-to-line and standard cementing in 48 arthroplasties. The primary outcome measure was femoral stem migration in terms of rotation and translation around and along with the X-, Y-, and Z- axes measured using model-based RSA at three, 12, and 24 months. A linear mixed-effects model was used for statistical analysis. Results. Results from mixed model analyses revealed a lower mean retroversion for line-to-line (0.72° (95% confidence interval (CI) 0.38° to 1.07°; p < 0.001), but no significant differences in subsidence between the techniques (-0.15 mm (95% CI -0.53 to 0.227; p = 0.429) at 24 months. Radiolucent lines measuring < 2 mm wide were found in three and five arthroplasties cemented by the standard and line-to-line method, respectively. Conclusion. The cemented Corail stem with a force-closed design seems to settle earlier and better with the line-to-line cementing method, although for subsidence the difference was not significant. However, the lower rate of migration into retroversion may reduce the wear and cement deformation, contributing to good long-term fixation and implant survival. Cite this article: Bone Joint J 2022;104-B(1):19–26

Aims. The Exeter short stem was designed for patients with Dorr type A femora and short-term results are promising. The aim of this study was to evaluate the minimum five-year stem migration pattern of Exeter short stems in comparison with Exeter standard stems. Methods. In this case-control study, 25 patients (22 female) at mean age of 78 years (70 to 89) received cemented Exeter short stem (case group). Cases were selected based on Dorr type A femora and matched first by Dorr type A and then age to a control cohort of 21 patients (11 female) at mean age of 74 years (70 to 89) who received with cemented Exeter standard stems (control group). Preoperatively, all patients had primary hip osteoarthritis and no osteoporosis as confirmed by dual X-ray absorptiometry scanning. Patients were followed with radiostereometry for evaluation of stem migration (primary endpoint), evaluation of cement quality, and Oxford Hip Score. Measurements were taken preoperatively, and at three, 12, and 24 months and a minimum five-year follow-up. Results. At three months, subsidence of the short stem -0.87 mm (95% confidence interval (CI) -1.07 to -0.67) was lower compared to the standard stem -1.59 mm (95% CI -1.82 to -1.36; p < 0.001). Both stems continued a similar pattern of subsidence until five-year follow-up. At five-year follow-up, the short stem had subsided mean -1.67 mm (95% CI -1.98 to -1.36) compared to mean -2.67 mm (95% CI -3.03 to -2.32) for the standard stem (p < 0.001). Subsidence was not influenced by preoperative bone quality (osteopenia vs normal) or cement mantle thickness. Conclusion. The standard Exeter stem had more early subsidence compared with the short Exeter stem in patients with Dorr type A femora, but thereafter a similar migration pattern of subsidence until minimum five years follow-up. Both the standard and the short Exeter stems subside. The standard stem subsides more compared to the short stem in Dorr type A femurs. Subsidence of the Exeter stems was not affected by cement mantle thickness. Cite this article: Bone Jt Open 2023;4(7):507–515

Aims. Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design. Patients and Methods. This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m. 2. and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (. sd. 6.5)) were enrolled. All patients had a minimum of two years’ clinical follow-up. Patient-reported outcome measures, whole blood metal ion levels (ug/l), and periprosthetic femoral BMD were measured at baseline, as well as at one and two years postoperatively. Power analysis indicated 40 patients necessary to demonstrate a five-fold increase in cobalt levels from baseline (alpha = 0.05, beta = 0.80). A mixed model with repeated measures was used for statistical analysis. Results. Mean Harris Hip Scores improved from 54.1 (. sd. 20.5) to 91.2 (. sd. 10.8) at two years postoperatively (p < 0.001). All patients had radiologically well-fixed components, no patients experienced any instability, and no patients required any further intervention. Mean cobalt levels increased from 0.065 ug/l (. sd. 0.03) preoperatively to 0.30 ug/l (. sd. 0.51) at one year postoperatively (p = 0.01) but decreased at two years postoperatively to 0.16 ug/l (. sd. 0.23; p = 0.2). Four patients (9.3%) had a cobalt level outside the reference range (0.03 ug/l to 0.29 ug/l) at two years postoperatively, with values from 0.32 ug/l to 0.94 ug/l. The mean femoral BMD ratio was maintained in Gruen zones 2 to 7 at both one and two years postoperatively using this stem design. At two years postoperatively, mean BMD in the medial calcar was 101.5% of the baseline value. Conclusion. Use of a modular DM prosthesis and cementless, tapered femoral stem has shown encouraging results in young, active patients undergoing primary THA. Elevation in mean cobalt levels and the presence of four patients outside the reference range at two years postoperatively demonstrates the necessity of continued surveillance in this cohort. Cite this article: Bone Joint J 2019;101-B:365–371

Cementless femoral stems are currently preferred for total hip replacement (THR) in the United States. Improvements in stem design, instrumentation and surgical technique have made this technology highly successful, reproducible, and applicable to the vast majority of patients requiring a THR. However, there are ongoing developments in some aspects of stem design that influence clinical results, the incidence of complications and their inherent adaptability in accommodating the needs of individual patients. Here we examine some of these design features. Cite this article: Bone Joint J 2013;95-B, Supple A:53–6

Aims. Although good clinical outcomes have been reported for monolithic tapered, fluted, titanium stems (TFTS), early results showed high rates of subsidence. Advances in stem design may mitigate these concerns. This study reports on the use of a current monolithic TFTS for a variety of indications. Methods. A multi-institutional retrospective study of all consecutive total hip arthroplasty (THA) and revision total hip arthroplasty (rTHA) patients who received the monolithic TFTS was conducted. Surgery was performed by eight fellowship-trained arthroplasty surgeons at four institutions. A total of 157 hips in 153 patients at a mean follow-up of 11.6 months (SD7.8) were included. Mean patient age at the time of surgery was 67.4 years (SD 13.3) and mean body mass index (BMI) was 28.9 kg/m. 2. (SD 6.5). Outcomes included intraoperative complications, one-year all-cause re-revisions, and subsidence at postoperative time intervals (two weeks, six weeks, six months, nine months, and one year). Results. There were eight intraoperative complications (4.9%), six of which were intraoperative fractures; none occurred during stem insertion. Six hips (3.7%) underwent re-revision within one year; only one procedure involved removal of the prosthesis due to infection. Mean total subsidence at latest follow-up was 1.64 mm (SD 2.47). Overall, 17 of 144 stems (11.8%) on which measurements could be performed had >5 mm of subsidence, and 3/144 (2.1%) had >10 mm of subsidence within one year. A univariate regression analysis found that additional subsidence after three months was minimal. A multivariate regression analysis found that subsidence was not significantly associated with periprosthetic fracture as an indication for surgery, the presence of an extended trochanteric osteotomy (ETO), Paprosky classification of femoral bone loss, stem length, or type of procedure performed (i.e. full revision vs conversion/primary). Conclusion. Advances in implant design, improved trials, a range of stem lengths and diameters, and high offset options mitigate concerns of early subsidence and dislocation with monolithic TFTS, making them a valuable option for femoral revision. Cite this article: Bone Joint J 2020;102-B(2):191–197

Aims. The aim of this study was to estimate the 90-day risk of revision for periprosthetic femoral fracture associated with design features of cementless femoral stems, and to investigate the effect of a collar on this risk using a biomechanical in vitro model. Materials and Methods. A total of 337 647 primary total hip arthroplasties (THAs) from the United Kingdom National Joint Registry (NJR) were included in a multivariable survival and regression analysis to identify the adjusted hazard of revision for periprosthetic fracture following primary THA using a cementless stem. The effect of a collar in cementless THA on this risk was evaluated in an in vitro model using paired fresh frozen cadaveric femora. Results. The prevalence of early revision for periprosthetic fracture was 0.34% (1180/337 647) and 44.0% (520/1180) occurred within 90 days of surgery. Implant risk factors included: collarless stem, non-grit-blasted finish, and triple-tapered design. In the in vitro model, a medial calcar collar consistently improved the stability and resistance to fracture. Conclusion. Analysis of features of stem design in registry data is a useful method of identifying implant characteristics that affect the risk of early periprosthetic fracture around a cementless femoral stem. A collar on the calcar reduced the risk of an early periprosthetic fracture and this was confirmed by biomechanical testing. This approach may be useful in the analysis of other uncommon modes of failure after THA. Cite this article: Bone Joint J 2019;101-B:779–786

Aims

The aims of this study were to evaluate the incidence of reoperation (all cause and specifically for periprosthetic femoral fracture (PFF)) and mortality, and associated risk factors, following a hemiarthroplasty incorporating a cemented collarless polished taper slip stem (PTS) for management of an intracapsular hip fracture.

Aims

Instability is a common cause of failure after total hip arthroplasty. A novel reverse total hip has been developed, with a femoral cup and acetabular ball, creating enhanced mechanical stability. The purpose of this study was to assess the implant fixation using radiostereometric analysis (RSA), and the clinical safety and efficacy of this novel design.

Aims

Periprosthetic proximal femoral fractures (PFFs) are a major complication after total hip arthroplasty (THA). Health status after PFF is not specifically investigated. The aim of this study is to evaluate the health status pattern over two years after sustaining a PFF.

Aims

The Exeter V40 femoral stem is the most implanted stem in the National Joint Registry (NJR) for primary total hip arthroplasty (THA). In 2004, the 44/00/125 stem was released for use in ‘cement-in-cement’ revision cases. It has, however, been used ‘off-label’ as a primary stem when patient anatomy requires a smaller stem with a 44 mm offset. We aimed to investigate survival of this implant in comparison to others in the range when used in primary THAs recorded in the NJR.

Objectives. In total hip arthroplasty (THA), the cementless, tapered-wedge stem design contributes to achieving initial stability and providing optimal load transfer in the proximal femur. However, loading conditions on the femur following THA are also influenced by femoral structure. Therefore, we determined the effects of tapered-wedge stems on the load distribution of the femur using subject-specific finite element models of femurs with various canal shapes. Patients and Methods. We studied 20 femurs, including seven champagne flute-type femurs, five stovepipe-type femurs, and eight intermediate-type femurs, in patients who had undergone cementless THA using the Accolade TMZF stem at our institution. Subject–specific finite element (FE) models of pre- and post-operative femurs with stems were constructed and used to perform FE analyses (FEAs) to simulate single-leg stance. FEA predictions were compared with changes in bone mineral density (BMD) measured for each patient during the first post-operative year. Results. Stovepipe models implanted with large-size stems had significantly lower equivalent stress on the proximal-medial area of the femur compared with champagne-flute and intermediate models, with a significant loss of BMD in the corresponding area at one year post-operatively. Conclusions. The stovepipe femurs required a large-size stem to obtain an optimal fit of the stem. The FEA result and post-operative BMD change of the femur suggest that the combination of a large-size Accolade TMZF stem and stovepipe femur may be associated with proximal stress shielding. Cite this article: M. Oba, Y. Inaba, N. Kobayashi, H. Ike, T. Tezuka, T. Saito. Effect of femoral canal shape on mechanical stress distribution and adaptive bone remodelling around a cementless tapered-wedge stem. Bone Joint Res 2016;5:362–369. DOI: 10.1302/2046-3758.59.2000525

Aims

The aim of this study was to compare the pattern of initial fixation and changes in periprosthetic bone mineral density (BMD) between patients who underwent total hip arthroplasty (THA) using a traditional fully hydroxyapatite (HA)-coated stem (T-HA group) and those with a newly introduced fully HA-coated stem (N-HA group).

Aims

This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Aims

The aim of this study was to compare the mid-term patient-reported outcome, bone remodelling, and migration of a short stem (Collum Femoris Preserving; CFP) with a conventional uncemented stem (Corail).

Aims

Hip arthroplasty aims to accurately recreate joint biomechanics. Considerable attention has been paid to vertical and horizontal offset, but femoral head centre in the anteroposterior (AP) plane has received little attention. This study investigates the accuracy of restoration of joint centre of rotation in the AP plane.

Aims

To achieve the functional benefits of the direct anterior (DA) approach and the fixation benefits of cemented replacement, this study combined the two techniques posing the following questions: does the limited access of the DA approach adversely affect the cement technique?; and does such a cementing technique reduce the incidence of cementless complications?