Wear of polyethylene is associated with aseptic loosening of orthopaedic implants and has been observed in hip and knee prostheses and anatomical implants for the shoulder. The reversed shoulder prostheses have not been assessed as yet. We investigated the volumetric polyethylene wear of the reversed and anatomical Aequalis shoulder prostheses using a mathematical musculoskeletal model. Movement and joint stability were achieved by EMG-controlled activation of the muscles. A non-constant wear factor was considered. Simulated activities of daily living were estimated from in vivo recorded data. After one year of use, the volumetric wear was 8.4 mm. 3. for the anatomical prosthesis, but 44.6 mm. 3. for the reversed version. For the anatomical prosthesis the predictions for contact pressure and wear were consistent with biomechanical and clinical data. The abrasive wear of the polyethylene in reversed prostheses should not be underestimated, and further analysis, both experimental and clinical, is required

There are many methods for analysing wear volume in failed polyethylene acetabular components. We compared a radiological technique with three recognised ex vivo methods of measurement. We tested 18 ultra-high-molecular-weight polyethylene acetabular components revised for wear and aseptic loosening, of which 13 had pre-revision radiographs, from which the wear volume was calculated based upon the linear wear. We used a shadowgraph technique on silicone casts of all of the retrievals and a coordinate measuring method on the components directly. For these techniques, the wear vector was calculated for each component and the wear volume extrapolated using mathematical equations. The volumetric wear was also measured directly using a fluid-displacement method. The results of each technique were compared. The series had high wear volumes (mean 1385 mm. 3. ; 730 to 1850) and high wear rates (mean 205 mm. 3. /year; 92 to 363). There were wide variations in the measurements of wear volume between the radiological and the other techniques. Radiograph-derived wear volume correlated poorly with that of the fluid-displacement method, co-ordinate measuring method and shadowgraph methods, becoming less accurate as the wear increased. The mean overestimation in radiological wear volume was 47.7% of the fluid-displacement method wear volume. Fluid-displacement method, coordinate measuring method and shadowgraph determinations of wear volume were all better than that of the radiograph-derived linear measurements since they took into account the direction of wear. However, only radiological techniques can be used in vivo and remain useful for monitoring linear wear in the clinical setting. Interpretation of radiological measurements of acetabular wear must be done judiciously in the clinical setting. In vitro laboratory techniques, in particular the fluid-displacement method, remain the most accurate and reliable methods of assessing the wear of acetabular polyethylene

Nanometre-sized particles of ultra-high molecular weight polyethylene have been identified in the lubricants retrieved from hip simulators. Tissue samples were taken from seven failed Charnley total hip replacements, digested using strong alkali and analysed using high-resolution field emission gun-scanning electron microscopy to determine whether nanometre-sized particles of polyethylene debris were generated in vivo. A randomised method of analysis was used to quantify and characterise all the polyethylene particles isolated. We isolated nanometre-sized particles from the retrieved tissue samples. The smallest identified was 30 nm and the majority were in the 0.1 μm to 0.99 μm size range. Particles in the 1.0 μm to 9.99 μm size range represented the highest proportion of the wear volume of the tissue samples, with 35% to 98% of the total wear volume comprised of particles of this size. The number of nanometre-sized particles isolated from the tissues accounted for only a small proportion of the total wear volume. Further work is required to assess the biological response to nanometre-sized polyethylene particles

Our aim was to analyse the influence of the size, shape and number of particles on the pathogenesis of osteolysis. We obtained peri-implant tissues from 18 patients having revision surgery for aseptically loosened Freeman total knee replacements (10), Charnley total hip replacements (3) and Imperial College/London Hospital double-cup surface hip replacements (5). The size and shape of the polyethylene particles were characterised using SEM and their concentration was calculated. The results were analysed with reference to the presence of radiological osteolysis. The concentration of polyethylene particles in 6 areas with osteolysis was significantly higher than that in 12 areas without osteolysis. There were no significant differences between the size and shape of the particles in these two groups. We conclude that the most critical factor in the pathogenesis of osteolysis is the concentration of polyethylene particles accumulated in the tissue

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

In ten male rats we inserted ceramic ‘drawing-pin’ implants in weight-bearing positions within the right proximal tibia. Two animals were killed 6 weeks after surgery and two more 14 weeks after surgery. The remaining six received intra-articular injections of either high-density polyethylene (4 rats) or saline (2 rats) at 8, 10 and 12 weeks after surgery. These animals were killed two weeks after the last injection. Histological examination of the bone-implant interface in the control animals showed appositional bone growth around the implant at both 6 and 14 weeks. Polyethylene, but not saline, caused a chronic inflammatory response with numerous foreign-body giant cells in periprosthetic tissues. Our model of a stable, weight-bearing bone-implant interface provides a simple and reliable system in which to study in vivo the effects of particulate materials used in orthopaedic surgery

We used a rat model in vivo to study the effects of the concentration of polyethylene particles on the bone-implant interface around stable implants in the proximal tibia. Intra-articular injections of 10. 4. , 10. 6. or 10. 8. high-density polyethylene (HDPE) particles per joint were given 8, 10 and 12 weeks after surgery. The animals were killed after 14 and 26 weeks and the response at the interface determined. Fibrous tissue was seen at the bone-implant interface when the head of the implant was flush with the top of the tibia but not when it was sunk below the tibial plateau. In the latter case the implant was completely surrounded by a shell of bone. The area of fibrous tissue and that of the gap between the implant and bone was related to the concentration of particles in the 14-week group (p < 0.05). Foreign-body granulomas containing HDPE particles were seen at the bone-implant interface in animals given 10. 8. particles. The pathology resembles that seen around prostheses with aseptic loosening and we suggest that this is a useful model by which to study this process

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured. The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm. 3. /year for the 32 mm head, which was significantly higher than the 41.5 mm. 3. /year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates

We have investigated whether the presence of polyethylene (PE) alone is sufficient to cause an aggressive periprosthetic tissue response, or whether certain mechanical interface conditions can allow bone to grow while in the presence of PE. An experimental implant was loaded in the presence and absence of particulate PE under stable and unstable conditions. Bone with a thin, discontinuous fibrous membrane formed in both groups of stable implants, either in the presence or absence of PE. By contrast, a continuous fibrous membrane consistently formed in both groups of unstable implants. The membrane consisted of loose fibrous connective tissue when PE was absent, and dense connective tissue with macrophages and a synovial lining when PE was present. In this model, if the interface was stable, the presence of PE was not sufficient to prevent the formation of bone or to produce a phagocytic tissue response. Only when the interface was unstable did a fibrous membrane form, and only then in the presence of PE

Although the response of macrophages to polyethylene debris has been widely studied, it has never been compared with the cellular response to ceramic debris. Our aim was to investigate the cytotoxicity of ceramic particles (Al. 2. O. 3. and ZrO. 2. ) and to analyse their ability to stimulate the release of inflammatory mediators compared with that of high-density polyethylene particles (HDP). We analysed the effects of particle size, concentration and composition using an in vitro model. The J774 mouse macrophage cell line was exposed to commercial particles in the phagocytosable range (up to 4.5 μm). Al. 2. O. 3. was compared with ZrO. 2. at 0.6 μm and with HDP at 4.5 μm. Cytotoxicity tests were performed using flow cytometry and macrophage cytokine release was measured by ELISA. Cell mortality increased with the size and concentration of Al. 2. O. 3. particles. When comparing Al. 2. O. 3. and ZrO. 2. at 0.6 μm, we did not detect any significant difference at the concentrations analysed (up to 2500 particles per macrophage), and mortality remained very low (less than 10%). Release of TNF-α also increased with the size and concentration of Al. 2. O. 3. particles, reaching 195% of control (165 pg/ml v 84 pg/ml) at 2.4 μm and 350 particles per cell (p < 0.05). Release of TNF-α was higher with HDP than with Al. 2. O. 3. particles at 4.5 μm. However, we did not detect any significant difference in the release of TNF-α between Al. 2. O. 3. and ZrO. 2. at 0.6 μm (p > 0.05). We saw no evidence of release of interleukin-1α or interleukin-1ß after exposure to ceramic or HDP particles

Wear particles commonly used for experiments may carry adherent endotoxin on their surfaces, which may be responsible for the observed effects. In this study, we attached titanium plates to the tibiae of 20 rats. After osseointegration, endotoxin-contaminated or uncontaminated high-density-polyethylene (HDPE) particles were applied. Contaminated specimens showed a dramatic resorption of bone after seven days but new bone filled the site again at 21 days. Uncontaminated specimens showed no resorption. In 18 rats we implanted intramuscularly discs of ultra-high-molecular-weight polyethylene (UHMWPE) with baseline or excess contamination of endotoxin. Excess endotoxin disappeared within 24 hours and the amount of endotoxin remained at baseline level (contamination from production). Uncontaminated titanium discs did not adsorb endotoxin in vivo. The endotoxin was measured by analytical chemistry. Locally-applied endotoxin stimulated bone resorption similarly to that in experiments with wear particles. Endotoxin on the surface of implants and particles appeared to be inactivated in situ. A clean implant surface did not adsorb endotoxin. Our results suggest that endotoxin adhering to orthopaedic implants is not a major cause for concern

We implanted bone harvest chambers (BHCs) bilaterally in ten mature male New Zealand white rabbits. Polyethylene particles (0.3 ± 0.1 −m in diameter, 6.4×10. 12. particles/ml) were implanted for two, four or six weeks bilaterally in the BHCs, with subsequent removal of the ingrown tissue after each treatment. In addition to the particles, one side also received 1.5 −g of recombinant transforming growth factor ß1 (TGFβ1). At two weeks, the bone area as a percentage of total area was less in chambers containing TGFβ compared with those with particles alone (7.8 ± 1.3% v 16.9 ± 2.7% respectively; 95% confidence interval (CI) for difference -14.0 to -4.30; p = 0.002). At four weeks, the percentage area of bone was greater in chambers containing TGFβ compared with those with particles alone (31.2 ± 3.4% v 22.5 ± 2.0% respectively; 95% CI for difference 1.0 to 16.4; p = 0.03). There were no statistical differences at six weeks, despite a higher mean value with TGFβ treatment (38.2 ± 3.9% v 28.8 ± 3.5%; 95% CI for difference -4.6 to 23.3; p = 0.16). The number of vitronectin-receptor-positive cells (osteoclast-like cells) was greater in the treatment group with TGFβ compared with that with particles alone; most of these positive cells were located in the interstitium, rather than adjacent to bone. TGFβ1 is a pleotropic growth factor which can modulate cellular events in the musculoskeletal system in a time- and concentration-dependent manner. Our data suggest that there is an early window at between two and six weeks, in which TGFβ may favourably affect bone ingrowth in the BHC model. Exogenous growth factors such as TGFβ may be a useful adjunct in obtaining osseointegration and bone ingrowth, especially in revisions when there is compromised bone stock and residual particulate debris

Sterilisation by gamma irradiation in the presence of air causes free radicals generated in polyethylene (PE) to react with oxygen, which could lead to loss of physical properties and reduction in fatigue strength. Tissue retrieved from failed total hip replacements often has large quantities of particulate PE and most particles associated with peri-implant osteolysis are oxidised. Consequently, an understanding of the cellular responses of oxidised PE particles may lead to clarification of the pathogenesis of osteolysis and aseptic loosening. We have used the agarose system to demonstrate the differential effects of oxidised and non-oxidised PE particles on the release of proinflammatory products such as interleukin-1β (IL-1β), IL-6, and tumour necrosis factor-α (TNF-α) from monocytes/ macrophages (M/M). Oxidised PE particles were shown to stimulate human M/M to phagocytose and to release cytokines. Oxidation may alter the surface chemistry of the particles and enhance the response to specific membrane receptors on macrophages, such as scavenger-type receptors

We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads. In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles. Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs. Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements

We used radiostereometric analysis to compare wear rates between uncemented porous sockets and cemented all-polyethylene sockets in a series of 102 hips randomised for either a Harris-Galante or a Charnley cup. Wear was evaluated in 95 hips at a mean of five years (2 to 7). All hips had a cemented, 22 mm head mono-bloc Charnley stem.

The mean annual wear rate was 0.09 mm in the Charnley sockets and 0.10 mm in the Harris-Galante sockets, with no statistically significant differences in wear, migration or rotation.

We conclude that, up to five years, the wear characteristics of the modular and porous Harris-Galante socket resemble that of the Charnley socket.

We analysed revised Mathys isoelastic polyacetal femoral stems with stainless-steel heads and polyethylene acetabular cups from eight patients in order to differentiate various types of particle of wear debris. Loosening of isoelastic femoral stems is associated with the formation of polyacetal wear particles as well as those of polyethylene and metal. All three types of particle were isolated simultaneously by tissue digestion followed by sucrose gradient centrifugation. Polyacetal particles were either elongated, ranging from 10 to 150 μm in size, or shred-like and up to 100 μm in size. Polyethylene particles were elongated or granules, and were typically submicron or micronsized. Polyacetal and polyethylene polymer particles were differentiated by the presence of BaSO. 4. , which is added as a radiopaque agent to polyacetal but not to polyethylene. This was easily detectable by back-scattered SEM analysis and verified by energy dispersive x-ray analysis. Two types of foreign-body giant cell (FBGC) were recognised in the histological specimens. Extremely large FBGCs with irregular polygonal particles showing an uneven, spotty birefringence in polarised light were ascribed to polyacetal debris. Smaller FBGCs with slender elongated particles shining uniformly brightly in polarisation were related to polyethylene. Mononucleated histiocytes containing both types of particle were also present. Our findings offer a better understanding of the processes involved in the loosening of polyacetal stems and indicate why the idea of ‘isoelasticity’ proved to be unsuccessful in clinical practice

Ultra-high-molecular-weight polyethylene (UHMWPE) components for total joint replacement generate wear particles which cause adverse biological tissue reactions leading to osteolysis and loosening. Sterilisation of UHMWPE components by gamma irradiation in air causes chain scissions which initiate a long-term oxidative process that degrades the chemical and mechanical properties of the polyethylene. Using a tri-pin-on-disc tribometer we studied the effect of ageing for ten years after gamma irradiation in air on the volumetric wear, particle size distribution and the number of particles produced by UHMWPE when sliding against a stainless-steel counterface. The aged and irradiated material produced six times more volumetric wear and 34 times more wear particles per unit load per unit sliding distance than non-sterilised UHMWPE. Our findings indicate that oxidative degradation of polyethylene after gamma irradiation in air with ageing produces more wear

We retrieved 159 femoral heads at revision surgery to determine changes in surface configuration. Macroscopic wear of the head was observed in three bipolar hip prostheses as a result of three-body wear. There was a considerable change in surface roughness in the internal articulation of bipolar hip prostheses. Roughness in alumina heads was almost the same as that in new cobalt-chromium heads. The annual linear wear rate of polyethylene cups with alumina heads was less than that of cups with cobalt-chromium alloy heads. Polyethylene wear was increased in the prostheses which had increased roughness of the head

Little is known about the tissue reactions to various implant materials which coincide with an inflammatory reaction. We used the avridine arthritis rat model to evaluate the tissue response in the synovial, interstitial and subcutaneous tissues after implant insertion. Quantitative immunohistochemistry showed that normal joint synovial tissue is dominated by ED2-positive resident macrophages. Polyethylene implants induced a much stronger foreign-body reaction than titanium implants, as measured by the number of interfacial ED1-positive macrophages. The tissue response to titanium and polyethylene was also vastly different in arthritic synovial tissue compared with control tissue. It is likely that these biomaterials interact differently with inflammatory cells or intermediary compounds. It may be that arthritic synovial tissue produces reactive oxygen intermediates (free radicals) with which titanium has a unique anti-inflammatory interaction in vitro

We compared wear particles from two different designs of total hip arthroplasty with polycrystalline alumina-ceramic bearings of different production periods (group 1, before ISO 6474: group 2, according to ISO 6474). The neocapsules and interfacial connective tissue membranes were retrieved after mean implantation times of 131 months and 38 months, respectively. Specimen blocks were freed from embedding media, either methylmethacrylate or paraffin and digested in concentrated nitric acid. Particles were then counted and their sizes and composition determined by SEM and energy-dispersive x-ray analysis (EDXA). The mean numbers and sizes of most alumina wear particles did not differ for both production periods, but the larger sizes of particle in group 1 point to more severe surface destruction. The increased metal wear in group 2 was apparently due to alumina-induced abrasion of the stems. In this study the concentrations of particles in the periprosthetic tissues were 2 to 22 times lower than those observed previously with polyethylene and alumina/polyethylene wear couples

Malrotation of the femoral component is a cause of patellofemoral maltracking after total knee arthroplasty. Its precise effect on the patellofemoral mechanics has not been well quantified. We have developed an in vitro method to measure the influence of patellar maltracking on contact. Maltracking was induced by progressively rotating the femoral component either internally or externally. The contact mechanics were analysed using Tekscan. The results showed that excessive malrotation of the femoral component, both internally and externally, had a significant influence on the mechanics of contact. The contact area decreased with progressive maltracking, with a concomitant increase in contact pressure. The amount of contact area that carries more than the yield stress of ultra-high molecular weight polyethylene significantly increases with progressive maltracking. It is likely that the elevated pressures noted in malrotation could cause accelerated and excessive wear of the patellar button

Aims

Second-generation metal-on-metal (MoM) articulations in total hip arthroplasty (THA) were introduced in order to reduce wear-related complications. The current study reports on the serum cobalt levels and the clinical outcome at a minimum of 20 years following THA with a MoM (Metasul) or a ceramic-on-polyethylene (CoP) bearing.

Objectives

The Attune total knee arthroplasty (TKA) has been used in over 600 000 patients worldwide. Registry data show good clinical outcome; however, concerns over the cement-tibial interface have been reported. We used retrieval analysis to give further insight into this controversial topic.

We examined the cellular responses to various particles injected into the knees and the intramedullary femoral cavities of rats in the presence of polymethyl-methacrylate (PMMA) plugs. The intra-articular particles were mainly ingested by synovial fibroblasts. Increased numbers of macrophages were not detected and there was only a slight increase in synovial thickness. Cellular responses in the intramedullary space were similarly mild and bone resorption around the PMMA plug did not occur. Bone formation was inhibited only by polyethylene particles. In contrast to current views, our study shows that wear particles per se do not initiate bone resorption

Fixation of the glenoid component is critical to the outcome of total shoulder arthroplasty. In an in vitro study, we analysed the effect of surface design and thickness of the cement mantle on the pull-out strength of the polyethylene pegs which are considered essential for fixation of cemented glenoid components. The macrostructure and surface of the pegs and the thickness of the cement mantle were studied in human glenoid bone. The lowest pull-out forces, 20 ± 5 N, were for cylindrical pegs with a smooth surface fixed in the glenoid with a thin cement mantle. The highest values, 425 ± 7 N, were for threaded pegs fixed with a thicker cement mantle. Increasing the diameter of the hole into which the peg is inserted from 5.2 to 6.2 mm thereby increasing the thickness of the cement mantle, improved the mean pull-out force for the pegs tested

Using a rat model, we created a bone-to-titanium interface and applied phagocytosable high-density polyethylene pArticles between the bone and implant, either initially or when the interface had matured. No fibrous membrane developed and no bone resorption was found. If sliding movements were initiated at the interface after two weeks, there was formation of a fibrous membrane. The additional application of pArticles did not change the thickness of the membrane, and there were only minor qualitative changes. Creation of a membrane by movement followed by cessation of movement and the application of pArticles caused the membrane to persist, whereas in a pArticle-free control group bone-to-metal contact was re-established. Our findings suggest that mechanical stimuli are of primary importance for prosthetic loosening, and that pArticles may modulate the later stages of the loosening process

We made a semiquantitative study of the comparative histology of pseudomembranes from 12 loose cemented ceramic-ceramic and 18 metal-polyethylene total hip replacements. We found no significant difference in cellular reaction between the two groups, but there was a major difference in the origin of the particulate debris. In the metal-polyethylene group, polyethylene of articular origin was predominant, while in the ceramic-ceramic group the cellular reaction appeared to be a response to zirconia ceramic particles used to opacify cement used for fixation. Isolation and characterisation of the debris showed that the zirconia particles formed the greatest proportion (76%) in ceramic-ceramic hips, while alumina debris of articular origin formed only 12%. Our study has indicated that aseptic loosening of ceramic cups is not due to a response to debris generated at the articular interface, but to mechanical factors which lead to fragmentation of the cement

Ten acetabular cups coated with hydroxyapatite (HA) had originally been inserted in five primary and five revision total hip replacements. The thickness of the HA was 155 ± 35 μm. The cups, which were well-fixed, were retrieved, with their adherent tissue, at reoperation after 0.3 to 5.8 years because of infection (five hips), wear of polyethylene (three hips), and instability (two hips). Undecalcified sections showed a direct contact between bone and osteoid-like tissue which had formed directly onto the HA coating. The area within the threads and their mirror images, as well as the implant-tissue interfaces consisted of similar amounts of bone and soft tissue. Degradation of HA was seen in all hips. The mean thickness of the remaining HA coating was 97 μm (95% CI 94 to 101). The metal interface comprised 66% HA. The HA-tissue interface contained more bone than soft tissue (p = 0.001), whereas the metal-tissue interface included more soft tissue than bone (p = 0.019). Soft tissue at the implant interface and poor replacement of HA by bone may interfere with long-term fixation

Estimates of knee joint loadings were calculated for 12 normal subjects from kinematic and kinetic measures obtained during both level and downhill walking. The maximum tibiofemoral compressive force reached an average load of 3.9 times body-weight (BW) for level walking and 8 times BW for downhill walking, in each instance during the early stance phase. Muscle forces contributed 80% of the maximum bone-on-bone force during downhill walking and 70% during level walking whereas the ground reaction forces contributed only 20% and 30% respectively. Most total knee designs provide a tibiofemoral contact area of 100 to 300 mm. 2. The yield point of these polyethylene inlays will therefore be exceeded with each step during downhill walking. Future evaluation of total knee designs should be based on a tibiofemoral joint load of 3.5 times BW at 20° knee flexion, 8 times BW at 40° and 6 times BW at 60°

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

We have studied the beneficial effects of a hydroxyapatite (HA) coating on the prevention of the migration of wear debris along the implant-bone interface. We implanted a loaded HA-coated implant and a non-coated grit-blasted titanium alloy (Ti) implant in each distal femoral condyle of eight Labrador dogs. The test implant was surrounded by a gap communicating with the joint space and allowing access of joint fluid to the implant-bone interface. We injected polyethylene (PE) particles into the right knee three weeks after surgery and repeated this weekly for the following five weeks. The left knee received sham injections. The animals were killed eight weeks after surgery. Specimens from the implant-bone interface were examined under plain and polarised light. Only a few particles were found around HA-coated implants, but around Ti implants there was a large amount of particles. HA-coated implants had approximately 35% bone ingrowth, whereas Ti implants had virtually no bone ingrowth and were surrounded by a fibrous membrane. Our findings suggest that HA coating of implants is able to inhibit peri-implant migration of PE particles by creating a seal of tightly-bonded bone on the surface of the implant

Proponents of the biological theory of aseptic loosening have in recent years tended to concentrate on the production and distribution of particulate ultra-high-molecular-weight polyethylene (UHMWPE) debris around the potential joint space. However, mechanical loading of cemented implants with the differing elastic moduli of metal stems, polymethylmethacrylate (PMMA) cement and bone can result in relative micromotion, implying the potential for production of metal and PMMA particles from the stem-cement interface by fretting wear. In order to investigate the production and biological reactivity of debris from this interface, PMMA and metal particulate debris was produced by sliding wear of PMMA pins containing barium sulphate and zirconium dioxide against a Vaquasheened stainless steel counterface. This debris was characterised by SEM, energy-dispersive analysis by X-ray (EDAX) and image analysis, then added to cell cultures of a human monocytic cell line, U937, and stimulation of pro-osteolytic cytokines measured by ELISA. Large quantities of PMMA cement debris were generated by the sliding wear of PMMA pins against Vaquasheened stainless steel plates in the method developed for this study. Both cements stimulated the release of pro-osteolytic TNFα from the U937 monocytic cell line, in a dose-dependent fashion. There was a trend towards greater TNFα release with Palacos cement than CMW cement at the same dose. Palacos particles also caused significant release of IL-6, another pro-osteolytic cytokine, while CMW did not. The particulate cement debris produced did not stimulate the release of GM-CSF or IL1β from the U937 cells. These results may explain the cytokine pathway responsible for bone resorption caused by particulate PMMA debris. Radio-opaque additives are of value in surgical practice and clinical studies to quantify the relevance of these in vitro findings are required before the use of cement containing radio-opacifier is constrained

We compared the peripheral blood and periprosthetic tissues of 53 patients at revision arthroplasty with those of 30 patients at primary arthroplasty to determine whether there is a systemic difference in lymphocytes in patients with worn hip implants. The absolute number and relative proportion of lymphocytes bearing CD2, CD3, CD4, CD8, CD16, CD19, HLA-DR, kappa and lambda antigens were compared with the levels of IL-1β, IL-6 and PGE. 2. in the pseudosynovial membrane as well as with a semiquantitative estimate of metal and polyethylene particles, necrosis and chronic inflammation and the total concentration of metals within the periprosthetic tissues. There was a significant increase in the relative proportion of CD2-positive T-cells and CD16-positive natural killer cells in the peripheral blood at revision arthroplasty compared with primary arthroplasty and an increased proportion of CD8-positive T-cells and a decreased ratio of CD4 to CD8 (helper inducer/suppressor cytotoxic cells). Three control patients, who went on to have revision surgery, had values at primary arthroplasty which were similar to those of patients at the time of revision surgery. These differences did not correlate with the local concentration of metal, plastic or cement or inflammatory response or the type of prosthesis. An inverse correlation was noted between the necrosis in the periprosthetic tissue and both the local production of IL-6 and the absolute numbers of T-cells in peripheral blood. We conclude that there may be several cell-mediated systemic immune responses to aseptic loosening, at least one of which may be directly related to events in the periprosthetic tissues. We cannot exclude the possibility that the changes in the proportion of CD8-positive cells reflected a predisposition, rather than a reaction, to loosening of the implant

Objectives

Preservation of both anterior and posterior cruciate ligaments in total knee arthroplasty (TKA) can lead to near-normal post-operative joint mechanics and improved knee function. We hypothesised that a patient-specific bicruciate-retaining prosthesis preserves near-normal kinematics better than standard off-the-shelf posterior cruciate-retaining and bicruciate-retaining prostheses in TKA.

Objectives

This study reports on a secondary exploratory analysis of the early clinical outcomes of a randomised clinical trial comparing robotic arm-assisted unicompartmental knee arthroplasty (UKA) for medial compartment osteoarthritis of the knee with manual UKA performed using traditional surgical jigs. This follows reporting of the primary outcomes of implant accuracy and gait analysis that showed significant advantages in the robotic arm-assisted group.

Objectives

Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues.

Objectives

Infection of implants is a major problem in elective and trauma surgery. Heating is an effective way to reduce the bacterial load in food preparation, and studies on hyperthermia treatment for cancer have shown that it is possible to heat metal objects with pulsed electromagnetic fields selectively (PEMF), also known as induction heating. We therefore set out to answer the following research question: is non-contact induction heating of metallic implants effective in reducing bacterial load in vitro?

Objectives

Surgeons face a substantial risk of infection because of the occupational exposure to blood-borne pathogens (BBPs) from patients undergoing high-risk orthopaedic procedures. This study aimed to determine the seroprevalence of four BBPs among patients undergoing joint arthroplasty in Shanghai, China. In addition, we evaluated the significance of pre-operative screening by calculating a cost-to-benefit ratio.

Objectives

All-suture anchors are increasingly used in rotator cuff repair procedures. Potential benefits include decreased bone damage. However, there is limited published evidence for the relative strength of fixation for all-suture anchors compared with traditional anchors.

Objectives

Mechanical wear and corrosion at the head-stem junction of total hip arthroplasties (THAs) (trunnionosis) have been implicated in their early revision, most commonly in metal-on-metal (MOM) hips. We can isolate the role of the head-stem junction as the predominant source of metal release by investigating non-MOM hips; this can help to identify clinically significant volumes of material loss and corrosion from these surfaces.

Objectives

Our study aimed to examine not only the incidence but also the impact of noise from two types of total hip replacement articulations: ceramic-on-ceramic and ceramic-on-polyethylene.

Objectives

Acetabular component orientation in total hip arthroplasty (THA) influences results. Intra-operatively, the natural arthritic acetabulum is often used as a reference to position the acetabular component. Detailed information regarding its orientation is therefore essential. The aim of this study was to identify the acetabular inclination and anteversion in arthritic hips.

Objectives

Third-body wear is believed to be one trigger for adverse results with metal-on-metal (MOM) bearings. Impingement and subluxation may release metal particles from MOM replacements. We therefore challenged MOM bearings with relevant debris types of cobalt–chrome alloy (CoCr), titanium alloy (Ti6Al4V) and polymethylmethacrylate bone cement (PMMA).

The biomechanics of the patellofemoral joint can become disturbed during total knee replacement by alterations induced by the position and shape of the different prosthetic components. The role of the patella and femoral trochlea has been well studied. We have examined the effect of anterior or posterior positioning of the tibial component on the mechanisms of patellofemoral contact in total knee replacement. The hypothesis was that placing the tibial component more posteriorly would reduce patellofemoral contact stress while providing a more efficient lever arm during extension of the knee.

We studied five different positions of the tibial component using a six degrees of freedom dynamic knee simulator system based on the Oxford rig, while simulating an active knee squat under physiological loading conditions. The patellofemoral contact force decreased at a mean of 2.2% for every millimetre of posterior translation of the tibial component. Anterior positions of the tibial component were associated with elevation of the patellofemoral joint pressure, which was particularly marked in flexion > 90°.

From our results we believe that more posterior positioning of the tibial component in total knee replacement would be beneficial to the patellofemoral joint.

This review is aimed at clinicians appraising preclinical trauma studies and researchers investigating compromised bone healing or novel treatments for fractures. It categorises the clinical scenarios of poor healing of fractures and attempts to match them with the appropriate animal models in the literature.

We performed an extensive literature search of animal models of long bone fracture repair/nonunion and grouped the resulting studies according to the clinical scenario they were attempting to reflect; we then scrutinised them for their reliability and accuracy in reproducing that clinical scenario.

Models for normal fracture repair (primary and secondary), delayed union, nonunion (atrophic and hypertrophic), segmental defects and fractures at risk of impaired healing were identified. Their accuracy in reflecting the clinical scenario ranged greatly and the reliability of reproducing the scenario ranged from 100% to 40%.

It is vital to know the limitations and success of each model when considering its application.

When performing the Scandinavian Total Ankle Replacement (STAR), the positioning of the talar component and the selection of mobile-bearing thickness are critical. A biomechanical experiment was undertaken to establish the effects of these variables on the range of movement (ROM) of the ankle.

Six cadaver ankles containing a specially-modified STAR prosthesis were subjected to ROM determination, under weight-bearing conditions, while monitoring the strain in the peri-ankle ligaments. Each specimen was tested with the talar component positions in neutral, as well as 3 and 6 mm of anterior and posterior displacement. The sequence was repeated with an anatomical bearing thickness, as well as at 2 mm reduced and increased thicknesses. The movement limits were defined as 10% strain in any ligament, bearing lift-off from the talar component or limitations of the hardware.

Both anterior talar component displacement and bearing thickness reduction caused a decrease in plantar flexion, which was associated with bearing lift-off. With increased bearing thickness, posterior displacement of the talar component decreased plantar flexion, whereas anterior displacement decreased dorsiflexion.

Using an osteotomy of the olecranon as a model of a transverse fracture in 22 cadaver elbows we determined the ability of three different types of suture and stainless steel wire to maintain reduction when using a tension-band technique to stabilise the bone. Physiological cyclical loading simulating passive elbow movement (15 N) and using the arms to push up from a chair (450 N) were applied using an Instron materials testing machine whilst monitoring the osteotomy site with a video extensometer. Each osteotomy was repaired by one of four materials, namely, Stainless Steel Wire (7), No 2 Ethibond (3), No 5 Ethibond (5), or No 2 FiberWire (7).

There were no failures (movement of > 2 mm) with stainless steel wire or FiberWire and no significant difference in the movements measured across the site of the osteotomy (p = 0.99). The No. 2 Ethibond failed at 450 N and two of the five of No. 5 Ethibond sutures had a separation of > 2 mm at 450 N.

FiberWire as the tension band in this model held the reduction as effectively as stainless steel wire and may reduce the incidence of discomfort from the hardware. On the basis of our findings we suggest that a clinical trial should be undertaken