We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging. Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies

Objectives. We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. Methods. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood. Results. A CoCr JFR > 1 showed a specificity of 83% (77% to 88%) and sensitivity of 63% (55% to 70%) for the detection of severe ALVAL and/or SOTP. In patients with CoCr JFRs > 1, the median blood Cr to serum Cr ratio was 0.99, compared with 0.71 in patients with CoCr JFRs < 1 (p < 0.001). Regression analysis demonstrated that the blood Cr to serum Cr value was positively associated with the JF Co concentration (p = 0.011) and inversely related to the JF Cr concentration (p < 0.001). Conclusion. Elevations in CoCr JFRs are associated with adverse biological (severe ALVAL) or tribocorrosive processes (SOTP). Comparison of serum Cr with blood Cr concentrations may be a useful additional clinical tool to help to identify these conditions. Cite this article: D. J. Langton, S. Natu, C. F. Harrington, J. G. Bowsher, A. V. F. Nargol. Is the synovial fluid cobalt-to-chromium ratio related to the serum partitioning of metal debris following metal-on-metal hip arthroplasty? Bone Joint Res 2019;8:146–155. DOI: 10.1302/2046-3758.83.BJR-2018-0049.R1

Aims. Periprosthetic joint infections (PJIs) with prior multiple failed surgery for reinfection represent a huge challenge for surgeons because of poor vascular supply and biofilm formation. This study aims to determine the results of single-stage revision using intra-articular antibiotic infusion in treating this condition. Methods. A retrospective analysis included 78 PJI patients (29 hips; 49 knees) who had undergone multiple prior surgical interventions. Our cohort was treated with single-stage revision using a supplementary intra-articular antibiotic infusion. Of these 78 patients, 59 had undergone more than two prior failed debridement and implant retentions, 12 patients had a failed arthroplasty resection, three hips had previously undergone failed two-stage revision, and four had a failed one-stage revision before their single-stage revision. Previous failure was defined as infection recurrence requiring surgical intervention. Besides intravenous pathogen-sensitive agents, an intra-articular infusion of vancomycin, imipenem, or voriconazole was performed postoperatively. The antibiotic solution was soaked into the joint for 24 hours for a mean of 16 days (12 to 21), then extracted before next injection. Recurrence of infection and clinical outcomes were evaluated. Results. A total of 68 patients (87.1%) were free of infection at a mean follow-up time of 85 months (24 to 133). The seven-year infection-free survival was 87.6% (95% confidence interval (CI) 79.4 to 95.8). No significant difference in infection-free survival was observed between hip and knee PJIs (91.5% (95% CI 79.9 to 100) vs 84.7% (95% CI 73.1 to 96.3); p = 0.648). The mean postoperative Harris Hip Score was 76.1 points (63.2 to 92.4) and Hospital for Special Surgery score was 78. 2 (63.2 to 92.4) at the most recent assessment. Polymicrobial and fungal infections accounted for 14.1% (11/78) and 9.0% (7/78) of all cases, respectively. Conclusion. Single-stage revision with intra-articular antibiotic infusion can provide high antibiotic concentration in synovial fluid, thereby overcoming reduced vascular supply and biofilm formation. This supplementary route of administration may be a viable option in treating PJI after multiple failed prior surgeries for reinfection. Cite this article: Bone Joint J 2022;104-B(7):867–874

Objectives. T-cells are considered to play an important role in the inflammatory response causing arthroplasty failure. The study objectives were to investigate the composition and distribution of CD4+ T-cell phenotypes in the peripheral blood (PB) and synovial fluid (SF) of patients undergoing revision surgery for failed metal-on-metal (MoM) and metal-on-polyethylene (MoP) hip arthroplasties, and in patients awaiting total hip arthroplasty. Methods. In this prospective case-control study, PB and SF were obtained from 22 patients (23 hips) undergoing revision of MoM (n = 14) and MoP (n = 9) hip arthroplasties, with eight controls provided from primary hip osteoarthritis cases awaiting arthroplasty. Lymphocyte subtypes in samples were analysed using flow cytometry. Results. The percentages of CD4+ T-cell subtypes in PB were not different between groups. The CD4+ T-cells in the SF of MoM hips showed a completely different distribution of phenotypes compared with that found in the PB in the same patients, including significantly decreased CD4+ T-central memory cells (p < 0.05) and increased T-effector memory cells (p < 0.0001) in the SF. Inducible co-stimulator (ICOS) was the only co-stimulatory molecule with different expression on CD4+ CD28+ cells between groups. In PB, ICOS expression was increased in MoM (p < 0.001) and MoP (p < 0.05) cases compared with the controls. In SF, ICOS expression was increased in MoM hips compared with MoP hips (p < 0.05). Conclusions. Increased expression of ICOS on CD4+ T-cells in PB and SF of patients with failed arthroplasties suggests that these cells are activated and involved in generating immune responses. Variations in ICOS expression between MoM and MoP hips may indicate different modes of arthroplasty failure. Cite this article: Professor P. A. Revell. Increased expression of inducible co-stimulator on CD4+ T-cells in the peripheral blood and synovial fluid of patients with failed hip arthroplasties. Bone Joint Res 2016;5:52–60. doi: 10.1302/2046-3758.52.2000574

The aim of this study was to assess the role of synovial C-reactive protein (CRP) in the diagnosis of chronic periprosthetic hip infection. We prospectively collected synovial fluid from 89 patients undergoing revision hip arthroplasty and measured synovial CRP, serum CRP, erythrocyte sedimentation rate (ESR), synovial white blood cell (WBC) count and synovial percentages of polymorphonuclear neutrophils (PMN). Patients were classified as septic or aseptic by means of clinical, microbiological, serum and synovial fluid findings. The high viscosity of the synovial fluid precluded the analyses in nine patients permitting the results in 80 patients to be studied. There was a significant difference in synovial CRP levels between the septic (n = 21) and the aseptic (n = 59) cohort. According to the receiver operating characteristic curve, a synovial CRP threshold of 2.5 mg/l had a sensitivity of 95.5% and specificity of 93.3%. The area under the curve was 0.96. Compared with serum CRP and ESR, synovial CRP showed a high diagnostic value. According to these preliminary results, synovial CRP may be a useful parameter in diagnosing chronic periprosthetic hip infection. Cite this article: Bone Joint J 2015; 97-B:173–6

Objectives. We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). Patients and Methods. We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties. Results. In the resurfacing cohort (n = 76), the statistical modelling indicated that the presence of severe ALVAL and a large fluid collection were associated with greater joint fluid Co concentrations after adjustment for volumetric wear rates (p = 0.005). These findings were replicated in the mixed implant group (n = 178), where the presence of severe ALVAL and a large fluid collection were significantly associated with greater fluid Co concentrations (p < 0.001). Conclusion. The development of severe ALVAL is associated with elevations in metal ion concentrations far beyond those expected from the volumetric loss from the prosthetic surfaces. This finding may aid the understanding of the sequence of events leading to soft-tissue reactions following MoM hip arthroplasties. Cite this article: D. J. Langton, R. P. Sidaginamale, T. J. Joyce, J. G. Bowsher, J. P. Holland, D. Deehan, A. V. F. Nargol, S. Natu. Aseptic lymphocyte-dominated vasculitis-associated lesions are related to changes in metal ion handling in the joint capsules of metal-on-metal hip arthroplasties. Bone Joint Res 2018;7:388–396. DOI: 10.1302/2046-3758.76.BJR-2018-0037

Aims. To evaluate the effect of ultrasound-targeted simvastatin-loaded microbubble destruction (UTMDSV) for alleviation of the progression of osteoarthritis (OA) in rabbits through modulation of the peroxisome proliferator-activated receptor (PPARγ). Methods. In vitro, OA chondrocytes were treated with ultrasound (US), US-targeted microbubble destruction (UTMD), simvastatin (SV), and UTMDSV on alternate days for four weeks. Chondrocytes were also treated with PPARγ inhibitor, PPARγ inhibitor+ UTMDSV, and UTMDSV. The cholesterol efflux rate and triglyceride levels were measured using an assay kit and oil red O staining, respectively. In vivo, the OA rabbits were treated with a single intra-articular injection of UTMD, SV, and UTMDSV every seven days for four weeks. Cartilage histopathology was assessed by safranin-O staining and the Mankin score. Total cholesterol (TC) and high-density lipoprotein-cholesterol (HDL-C) in rabbit knee synovial fluid were detected by enzyme-marker assay. Aggrecan, collagen II, and PPARγ expression levels were analyzed by Western blotting (WB). Results. In vitro, UTMDSV significantly increased the cholesterol efflux rate and aggrecan, collagen II, and PPARγ levels in OA chondrocytes; these effects were blocked by the PPARγ inhibitor. In vivo, UTMD. SV. significantly increased aggrecan, collagen II, PPARγ, and HDL-C levels, while TC levels and Mankin scores were decreased compared with the UTMD, SV, OA, and control groups. Conclusion. UTMDSV promotes cartilage extracellular matrix synthesis by modulating the PPARγ-mediated cholesterol efflux pathway in OA rabbits. Cite this article: Bone Joint Res 2021;10(10):693–703

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Aims. Leucocyte esterase (LE) has been shown to be an accurate marker of prosthetic joint infection (PJI), and has been proposed as an alternative to frozen section (FS) histology for intraoperative diagnosis. In this study, the intraoperative assessment of LE was compared with FS histology for the diagnosis of prosthetic hip infection. Patients and Methods. A total of 119 patients undergoing revision total hip arthroplasty (THA) between June 2015 and December 2017 were included in the study. There were 56 men and 63 women with a mean age of 66.2 years (27 to 88). Synovial fluid was collected before arthrotomy for the assessment of LE using enzymatic colourimetric strips. Between five and six samples were stained with haematoxylin and eosin for FS histology, and considered suggestive of infection when at least five polymorphonuclear leucocytes were found in five high-power fields. Results. The sensitivity and specificity of the LE assay were 100% and 93.8%, respectively; the positive (PPV) and the negative (NPV) predictive values were 79.3% and 100%, respectively. The mean time between the collection of the sample and the result being known was 20.1 minutes (. sd. 4.4). The sensitivity and specificity of FS histology were 78.3% and 96.9%, respectively; the PPV and the NPV were 85.7% and 94.9%, respectively. The mean time between the collection of the sample and the result being known was 27.2 minutes (. sd. 6.9). Conclusion. The sensitivity of LE assay was higher, with similar specificity and diagnostic accuracy, compared with FS histology. The faster turnaround time, its ease of use, and low costs make LE assay a valuable alternative to FS histology. We now use it routinely for the intraoperative diagnosis of PJI. Cite this article: Bone Joint J 2019;101-B:372–377

Aims

A revision for periprosthetic joint infection (PJI) in total hip arthroplasty (THA) has a major effect on the patient’s quality of life, including walking capacity. The objective of this case control study was to investigate the histological and ultrastructural changes to the gluteus medius tendon (GMED) in patients revised due to a PJI, and to compare it with revision THAs without infection performed using the same lateral approach.

Aims

The number of revision arthroplasties being performed in the elderly is expected to rise, including revision for infection. The primary aim of this study was to measure the treatment success rate for octogenarians undergoing revision total hip arthroplasty (THA) for periprosthetic joint infection (PJI) compared to a younger cohort. Secondary outcomes were complications and mortality.

Aims

The aims of this study were to determine the incidence and factors for developing periprosthetic joint infection (PJI) following hemiarthroplasty (HA) for hip fracture, and to evaluate treatment outcome and identify factors associated with treatment outcome.

In this study of 41 patients, we used proteomic, Western blot and immunohistochemical analyses to show that several reactive oxygen species scavenging enzymes are expressed differentially in patients with primary osteoarthritis and those with non-loosening and aseptic loosening after total hip replacement (THR). The patients were grouped as A (n = 16, primary THR), B (n = 10, fixed THR but requiring revision for polyethylene wear) and C (n = 15, requiring revision due to aseptic loosening) to verify the involvement of the identified targets in aseptic loosening. When compared with Groups A and B, Group C patients exhibited significant up-regulation of transthyretin and superoxide dismutase 3, but down-regulation of glutathione peroxidase 2 in their hip synovial fluids. Also, higher levels of superoxide dismutase 2 and peroxiredoxin 2, but not superoxide dismutase 1, catalase and glutathione perioxidase 1, were consistently detected in the hip capsules of Group C patients. We propose that dysregulated reactive oxygen species-related enzymes may play an important role in the pathogenesis and progression of aseptic loosening after THR

The peri-prosthetic tissue response to wear debris is complex and influenced by various factors including the size, area and number of particles. We hypothesised that the ‘biologically active area’ of all metal wear particles may predict the type of peri-prosthetic tissue response. . Peri-prosthetic tissue was sampled from 21 patients undergoing revision of a small diameter metal-on-metal (MoM) total hip arthroplasty (THA) for aseptic loosening. An enzymatic protocol was used for tissue digestion and scanning electron microscope was used to characterise particles. Equivalent circle diameters and particle areas were calculated. Histomorphometric analyses were performed on all tissue specimens. Aspirates of synovial fluid were collected for analysis of the cytokine profile analysis, and compared with a control group of patients undergoing primary THA (n = 11) and revision of a failed ceramic-on-polyethylene arthroplasty (n = 6). . The overall distribution of the size and area of the particles in both lymphocyte and non-lymphocyte-dominated responses were similar; however, the subgroup with lymphocyte-dominated peri-prosthetic tissue responses had a significantly larger total number of particles. . 14 cytokines (interleukin (IL)-1ß, IL-2, IL-4, IL-5, IL-6, IL-10, IL-13, IL-17, interferon (IFN)-γ, and IFN-gamma-inducible protein 10), chemokines (macrophage inflammatory protein (MIP)-1α and MIP-1ß), and growth factors (granulocyte macrophage colony stimulating factor (GM-CSF) and platelet derived growth factor) were detected at significantly higher levels in patients with metal wear debris compared with the control group. . Significantly higher levels for IL-1ß, IL-5, IL-10 and GM-CSF were found in the subgroup of tissues from failed MoM THAs with a lymphocyte-dominated peri-prosthetic response compared with those without this response. . These results suggest that the ‘biologically active area’ predicts the type of peri-prosthetic tissue response. The cytokines IL-1ß, IL-5, IL-10, and GM-CSF are associated with lymphocyte-dominated tissue responses from failed small-diameter MoM THA. Cite this article: Bone Joint J 2015;97-B:917–23

Aims

BoneMaster is a thin electrochemically applied hydroxyapatite (HA) coating for orthopaedic implants that is quickly resorbed during osseointegration. Early stabilization is a surrogacy marker of good survival of femoral stems. The hypothesis of this study was that a BoneMaster coating yields a fast early and lasting fixation of stems.

Bone cement containing gentamicin may release antibiotic when fractured during revision operations. Tissue samples taken during surgery may be contaminated by gentamicin and give inaccurate microbiological assessment. We studied five patients in whom cement containing gentamicin had been used in the primary procedure. During revision hip replacement, samples of joint fluid, tissues and cement were taken both before and after disruption of the cement. With the exception of one sample of joint fluid, low concentrations of gentamicin were recorded in the samples taken before the cement was disrupted, but after disruption the specimens contained gentamicin at concentrations high enough to inhibit or prevent growth of sensitive organisms. The cement contained very high levels up to ten years after insertion. Our findings suggest that no reliance can be placed on the microbiological assessment of specimens taken once cement splitting has started and that specimens should therefore be taken as early as possible

Aims

The purpose of this study was to evaluate unexpected positive cultures in total hip arthroplasty (THA) revisions for presumed aseptic loosening, to assess the prevalence of low-grade infection using two definition criteria, and to analyze its impact on implant survival after revision.

Aims

This study uses prospective registry data to compare early patient outcomes following arthroscopic repair or debridement of the acetabular labrum.

Aims

Septic arthritis of the hip often leads to irreversible osteoarthritis (OA) and the requirement for total hip arthroplasty (THA). The aim of this study was to report the mid-term risk of any infection, periprosthetic joint infection (PJI), aseptic revision, and reoperation in patients with a past history of septic arthritis who underwent THA, compared with a control group of patients who underwent THA for OA.

Aims

One-stage revision hip arthroplasty for periprosthetic joint infection (PJI) has several advantages; however, resection of the proximal femur might be necessary to achieve higher success rates. We investigated the risk factors for resection and re-revisions, and assessed complications and subsequent re-revisions.

Aims

Rotational acetabular osteotomy (RAO) has been reported to be effective in improving symptoms and preventing osteoarthritis (OA) progression in patients with mild to severe develomental dysplasia of the hip (DDH). However, some patients develop secondary OA even when the preoperative joint space is normal; determining who will progress to OA is difficult. We evaluated whether the preoperative cartilage condition may predict OA progression following surgery using T2 mapping MRI.

Aims

Surgical treatment of young femoral neck fractures often requires an open approach to achieve an anatomical reduction. The application of a calcar plate has recently been described to aid in femoral neck fracture reduction and to augment fixation. However, application of a plate may potentially compromise the regional vascularity of the femoral head and neck. The purpose of this study was to investigate the effect of calcar femoral neck plating on the vascularity of the femoral head and neck.

Aims

Developmental dysplasia of the hip (DDH) is a complex musculoskeletal disease that occurs mostly in children. This study aimed to investigate the molecular changes in the hip joint capsule of patients with DDH.

Aims

To find out if there is an inverse association between estimated glomerular filtration rate (eGFR) and whole blood cobalt (Co) and chromium (Cr) levels in patients with metal-on-metal (MoM) hip arthroplasties and renal insufficiency, suggesting that renal insufficiency could cause accumulation of Co and Cr in blood.

Aims

There is a paucity of long-term studies analyzing risk factors for failure after single-stage revision for periprosthetic joint infection (PJI) following total hip arthroplasty (THA). We report the mid- to long-term septic and non-septic failure rate of single-stage revision for PJI after THA.

Aims

To explore the effect of different types of articulating antibiotic-loaded cement spacers in two-stage revision for chronic hip prosthetic joint infection (PJI).

We have reviewed 202 consecutive primary hip replacements using a Freeman cemented femoral component after a mean period of follow-up of 64 months (23 to 113). There was only one revision for aseptic loosening. Retention of the femoral neck may act to reduce the torsional and shear forces at the implant-cement interface and may provide a seal against the migration of polyethylene-laden joint fluid in the potential joint space. The cemented Freeman femoral component with retention of the femoral neck was successful for up to nine years

Aims

We aimed to report the mid- to long-term rates of septic and aseptic failure after two-stage revision surgery for periprosthetic joint infection (PJI) following total hip arthroplasty (THA).

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Aims

This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys.

Aims

Single-stage revision is not widely pursued due to restrictive inclusion criteria. In this study, we evaluated the results of single-stage revision of chronically infected total hip arthroplasty (THA) using broad inclusion criteria and cementless implants.

Aims

In previous studies, we identified multiple factors influencing the survivorship of hip resurfacing arthroplasties (HRAs), such as initial anatomical conditions and surgical technique. In addition, the University of California, Los Angeles (UCLA) activity score presents a ceiling effect, so a better quantification of activity is important to determine which activities may be advisable or detrimental to the recovered patient. We aimed to determine the effect of specific groups of sporting activities on the survivorship free of aseptic failure of a large series of HRA.

Aims

The aims of this study were to characterize antibiotic choices for perioperative total knee arthroplasty (TKA) and total hip arthroplasty (THA) prophylaxis, assess antibiotic allergy testing efficacy, and determine rates of prosthetic joint infection (PJI) based on perioperative antibiotic regimen.

Objectives

The diagnosis of periprosthetic joint infection (PJI) is difficult and requires a battery of tests and clinical findings. The purpose of this review is to summarize all current evidence for common and new serum biomarkers utilized in the diagnosis of PJI.

Objectives

Legg–Calvé–Perthes’ disease (LCP) is an idiopathic osteonecrosis of the femoral head that is most common in children between four and eight years old. The factors that lead to the onset of LCP are still unclear; however, it is believed that interruption of the blood supply to the developing epiphysis is an important factor in the development of the condition.

Aims

We hypothesised that the synovial white blood cell (WBC) count in patients with a late periprosthetic joint infection (PJI) of the hip would depend on the duration of a patient’s symptoms, and that the optimal diagnostic threshold would also depend on this period of time.

Aims

There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs.

Aims

Fretting and corrosion at the modular head/neck junction, known as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse reaction to metal debris (ARMD). We describe the outcome of revision of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis with emphasis on the risk of major complications.

Aims

Early evidence has emerged suggesting that ceramic-on-ceramic articulations induce a different tissue reaction to ceramic-on-polyethylene and metal-on-metal bearings. Therefore, the aim of this study was to investigate the tissue reaction and cellular response to ceramic total hip arthroplasty (THA) materials in vitro, as well as the tissue reaction in capsular tissue after revision surgery of ceramic-on-ceramic THAs.

This review summarises the technique of impaction grafting with mesh augmentation for the treatment of uncontained acetabular defects in revision hip arthroplasty.

The ideal acetabular revision should restore bone stock, use a small socket in the near-anatomic position, and provide durable fixation. Impaction bone grafting, which has been in use for over 40 years, offers the ability to achieve these goals in uncontained defects. The precepts of modern, revision impaction grafting are that the segmental or cavitary defects must be supported with a mesh; the contained cavity is filled with vigorously impacted morselised fresh-frozen allograft; and finally, acrylic cement is used to stabilise the graft and provide rigid, long-lasting fixation of the revised acetabular component.

Favourable results have been published with this technique. While having its limitations, it is a viable option to address large acetabular defects in revision arthroplasty.

Cite this article: Bone Joint J 2017;99-B(1 Supple A):25–30.

Aims

We present a case series of ten metal-on-polyethylene total hip arthroplasties (MoP THAs) with delayed dislocation associated with unrecognised adverse local tissue reaction due to corrosion at the trunnion and pseudotumour formation.

Objectives

The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces.

Aims

Acetabular dysplasia is frequently associated with intra-articular pathology such as labral tears, but whether labral tears should be treated at the time of periacetabular osteotomy (PAO) remains controversial. The purpose of this study was to compare the clinical outcomes and radiographic corrections of PAO for acetabular dysplasia between patients with and without labral tears pre-operatively.

The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used.

The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm³ (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis.

Cite this article: Bone Joint J 2015;97-B:1350–7.

Based on the first implementation of mixing antibiotics into bone cement in the 1970s, the Endo-Klinik has used one stage exchange for prosthetic joint infection (PJI) in over 85% of cases. Looking carefully at current literature and guidelines for PJI treatment, there is no clear evidence that a two stage procedure has a higher success rate than a one-stage approach. A cemented one-stage exchange potentially offers certain advantages, mainly based on the need for only one operative procedure, reduced antibiotics and hospitalisation time. In order to fulfill a one-stage approach, there are obligatory pre-, peri- and post-operative details that need to be meticulously respected, and are described in detail. Essential pre-operative diagnostic testing is based on the joint aspiration with an exact identification of any bacteria. The presence of a positive bacterial culture and respective antibiogram are essential, to specify the antibiotics to be loaded to the bone cement, which allows a high local antibiotic elution directly at the surgical side. A specific antibiotic treatment plan is generated by a microbiologist. The surgical success relies on the complete removal of all pre-existing hardware, including cement and restrictors and an aggressive and complete debridement of any infected soft tissues and bone material. Post-operative systemic antibiotic administration is usually completed after only ten to 14 days.

Cite this article: Bone Joint J 2013;95-B, Supple A:77–83.

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation.

We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series.

The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases.

Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange.

Cite this article: Bone Joint J 2015;97-B:1024–1030.

We investigated differences in the location and mode of labral tears between dysplastic hips and hips with femoroacetabular impingement (FAI). We also investigated the relationship between labral tear and adjacent cartilage damage. We retrospectively studied 72 symptomatic hips (in 68 patients: 19 men and 49 women) with radiological evidence of dysplasia or FAI on high-resolution CT arthrography. The incidence and location of labral tears and modes of tear associated with the base of the labrum (Mode 1) or body of the labrum (Mode 2) were compared among FAI, mildly dysplastic and severely dysplastic hips. The locations predominantly involved with labral tears were different in FAI and mild dysplastic hips (anterior and anterosuperior zones) and in severely dysplastic hips (anterosuperior and superior zones) around the acetabulum. Significant differences were observed in the prevalence of Mode 1 versus Mode 2 tears in FAI hips (72% (n = 13) vs 28% (n = 5)) and severe dysplastic hips (25% (n = 2) vs 75% (n = 6)). The frequency of cartilage damage adjacent to Mode 1 tears was significantly higher (42% (n = 14)) than that adjacent to Mode 2 tears (14% (n = 3)).

Hip pathology is significantly related to the locations and modes of labral tears. Mode 1 tears may be a risk factor for the development of adjacent acetabular cartilage damage.

Cite this article: Bone Joint J 2013;95-B:1320–5.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear.

Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.

We report serum metal ion level data in patients with unilateral and bilateral hip resurfacing over a ten-year period. In these patients there is an increase in both cobalt and chromium levels above the accepted reference ranges during the first 18 months after operation. Metal ion levels remain elevated, but decline slowly for up to five years. However, the levels then appear to start rising again in some patients up to the ten-year mark. There was no significant difference in cobalt or chromium levels between men and women. These findings appear to differ from much of the current literature.

The clinical significance of a raised metal ion level remains under investigation.

This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83).

Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem.

The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4).

This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.