Aims. The risk of mechanical failure of modular revision hip stems is frequently mentioned in the literature, but little is currently known about the actual clinical failure rates of this type of prosthesis. The current retrospective long-term analysis examines the distal and modular failure patterns of the Prevision hip stem from 18 years of clinical use. A design improvement of the modular taper was introduced in 2008, and the data could also be used to compare the original and the current design of the modular connection. Methods. We performed an analysis of the Prevision modular hip stem using the manufacturer’s vigilance database and investigated different mechanical failure patterns of the hip stem from January 2004 to December 2022. Results. Two mechanical failure patterns were identified: fractures in the area of the distal fluted profile (distal stem fracture) and failure of the modular taper (modular fracture). A failure rate of 0.07% was observed for distal stem fracture, and modular fracture rates of 1.74% for the original and 0.013% for the current taper design. Conclusion. A low risk of mechanical failure for both fracture types was observed compared to other known complications in revision hip arthroplasty. In addition, the data show that a design change did significantly reduce the risk of a modular fracture. Cite this article: Bone Joint J 2024;106-B(2):151–157

Aims. Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Methods. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti. 12. Mo. 6. Zr. 2. Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients. Results. A total of 20 ALTRs were identified on MRI, with an incidence of 26%. Patients with ALTR had significantly higher median Co levels compared with those without ALTR (2.96 μg/l (interquartile range (IQR) 1.35 to 4.98) vs 1.44 μg/l (IQR 0.79 to 2.5); p = 0.019). Radiological evidence of osteolysis was also significantly associated with ALTR (p = 0.014). Median Cr levels were not significantly higher in those with ALTR compared with those without one (0.97 μg/l (IQR 0.72 to 1.9) v 0.67 μg/l (IQR 0.5 to 1.19; p = 0.080). BMI, sex, age, type of femoral component, head length, the inclination of the acetabular component, and heterotopic ossification formation showed no significant relationship with ALTR. Conclusion. Due to the high incidence of local ALTR in our cohort after more than ten years postoperatively, we recommend regular follow-up investigation even in asymptomatic patients with V40 taper and metal heads. As cobalt levels correlate with ALTR occurrence, routine metal ion screening and consecutive MRI investigation upon elevation could be discussed. Cite this article: Bone Joint J 2022;104-B(7):852–858

Aims. We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system. Patients and Methods. We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy. Results. After adjustment for other factors, CoCr stem tapers were found to have significantly greater volumetric material loss than the equivalent Ti stem tapers. Conclusion. When taper junction damage is identified during revision of a LD MoM hip, it should be suspected that a male taper composed of a standard CoCr alloy has sustained significant changes to the taper cone geometry which are likely to be more extensive than those affecting a Ti alloy stem. Cite this article: Bone Joint J 2017;99-B:1304–12

Aims. The aim of this study was to evaluate the suitability of the tapered cone stem in total hip arthroplasty (THA) in patients with excessive femoral anteversion and after femoral osteotomy. Methods. We included patients who underwent THA using Wagner Cone due to proximal femur anatomical abnormalities between August 2014 and January 2019 at a single institution. We investigated implant survival time using the endpoint of dislocation and revision, and compared the prevalence of prosthetic impingements between the Wagner Cone, a tapered cone stem, and the Taperloc, a tapered wedge stem, through simulation. We also collected Oxford Hip Score (OHS), visual analogue scale (VAS) satisfaction, and VAS pain by postal survey in August 2023 and explored variables associated with those scores. Results. Of the 58 patients (62 hips), two (two hips) presented with dislocation or reoperation, and Kaplan-Meier analysis indicated a five-year survival rate of 96.7% (95% CI 92.4 to 100). Mean stem anteversion was 35.2° (SD 18.2°) for the Taperloc stem and 29.8° (SD 7.9°) for the Wagner Cone stem; mean reduction from Taperloc to Wagner Cone was 5.4° (SD 18.8°). Overall, 55 hips (52 patients) were simulated, and the prevalence of prosthetic impingement was lower for the Wagner Cone (5.5%, 3/55) compared with the Taperloc (20.0%, 11/55) stem, with an odds ratio of 0.20 (p = 0.038). Among the 33 respondents to the postal survey (36 hips), the mean scores were VAS pain 10.9, VAS satisfaction 86.9, and OHS 44.7. A multivariable analysis revealed that reduction of stem anteversion from Taperloc to Wagner Cone was more favourable for VAS pain (p = 0.029) and VAS satisfaction (p = 0.002). Conclusion. The mid-term survival rate for THA using the Wagner Cone stem was high, which may be supported by a reduction in prosthetic impingement. The reduction in excessive stem anteversion by using a tapered cone stem was associated with reduced pain and increased patient satisfaction. Cite this article: Bone Jt Open 2024;5(10):858–867

Aims. United Classification System (UCS) B2 and B3 periprosthetic fractures in total hip arthroplasties (THAs) have been commonly managed with modular tapered stems. No study has evaluated the use of monoblock fluted tapered titanium stems for this indication. This study aimed to evaluate the effects of a monoblock stems on implant survivorship, postoperative outcomes, radiological outcomes, and osseointegration following treatment of THA UCS B2 and B3 periprosthetic fractures. Methods. A retrospective review was conducted of all patients who underwent revision THA (rTHA) for periprosthetic UCS B2 and B3 periprosthetic fracture who received a single design monoblock fluted tapered titanium stem at two large, tertiary care, academic hospitals. A total of 72 patients met inclusion and exclusion criteria (68 UCS B2, and four UCS B3 fractures). Primary outcomes of interest were radiological stem subsidence (> 5 mm), radiological osseointegration, and fracture union. Sub-analysis was also done for 46 patients with minimum one-year follow-up. Results. For the total cohort, stem osseointegration, fracture union, and stem subsidence were 98.6%, 98.6%, and 6.9%, respectively, at latest follow-up (mean follow-up 27.0 months (SD 22.4)). For patients with minimum one-year of follow-up, stem osseointegration, fracture union, and stem subsidence were 97.8%, 97.8%, and 6.5%, respectively. Conclusion. Monoblock fluted stems can be an acceptable modality for the management of UCS B2 periprosthetic fractures in rTHAs due to high rates of stem osseointegration and survival, and the low rates of stem subsidence, and revision. Further research on the use of this stem for UCS B3 periprosthetic fractures is warranted to determine if the same conclusion can be made for this fracture pattern. Cite this article: Bone Jt Open 2023;4(8):551–558

Aims. This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. Methods. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth. Results. Overall, 36 mm heads had lower corrosion onset load (p = 0.009) and change in open circuit potential (OCP) during simulated gait with (p = 0.006) and without joint movement (p = 0.004). Discontinuing gait’s joint movement decreased corrosion currents (p = 0.042); however, wear testing showed no significant effect of joint movement on taper damage. In addition, 36 mm heads had greater corrosion area (p = 0.050), but no significant difference was found for maximum linear wear depth (p = 0.155). Conclusion. Larger heads are more susceptible to taper corrosion; however, not due to frictional torque as hypothesized. An alternative hypothesis of taper flexural rigidity differential is proposed. Further studies are necessary to investigate the clinical significance and underlying mechanism of this finding. Cite this article: Bone Jt Open 2021;2(11):1004–1016

Aims. When performing revision total hip arthroplasty using diaphyseal-engaging titanium tapered stems (TTS), the recommended 3 to 4 cm of stem-cortical diaphyseal contact may not be available. In challenging cases such as these with only 2 cm of contact, can sufficient axial stability be achieved and what is the benefit of a prophylactic cable? This study sought to determine, first, whether a prophylactic cable allows for sufficient axial stability when the contact length is 2 cm, and second, if differing TTS taper angles (2° vs 3.5°) impact these results. Methods. A biomechanical matched-pair cadaveric study was designed using six matched pairs of human fresh cadaveric femora prepared so that 2 cm of diaphyseal bone engaged with 2° (right femora) or 3.5° (left femora) TTS. Before impaction, three matched pairs received a single 100 lb-tensioned prophylactic beaded cable; the remaining three matched pairs received no cable adjuncts. Specimens underwent stepwise axial loading to 2600 N or until failure, defined as stem subsidence > 5 mm. Results. All specimens without cable adjuncts (6/6 femora) failed during axial testing, while all specimens with a prophylactic cable (6/6) successfully resisted axial load, regardless of taper angle. In total, four of the failed specimens experienced proximal longitudinal fractures, three of which occurred with the higher 3.5° TTS. One fracture occurred in a 3.5° TTS with a prophylactic cable yet passed axial testing, subsiding < 5 mm. Among specimens with a prophylactic cable, the 3.5° TTS resulted in lower mean subsidence (0.5 mm (SD 0.8)) compared with the 2° TTS (2.4 mm (SD 1.8)). Conclusion. A single prophylactic beaded cable dramatically improved initial axial stability when stem-cortex contact length was 2 cm. All implants failed secondary to fracture or subsidence > 5 mm when a prophylactic cable was not used. A higher taper angle appears to decrease the magnitude of subsidence but increased the fracture risk. The fracture risk was mitigated by the use of a prophylactic cable. Cite this article: Bone Jt Open 2023;4(7):472–477

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

Aims. The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Methods. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour. Results. The model compared well to deformed microgrooves from the retrieved implants, predicting changes in microgroove height (mean 1.1 μm (0.2 to 1.3)) and width (mean 7.5 μm (1.0 to 18.5)) within the range of measured changes in height (mean 1.4 μm (0.4 to 2.3); p = 0.109) and width (mean 12.0 μm (1.5 to 25.4); p = 0.470). Consistent with benchtop studies, our model found that increasing assembly load magnitude led to increased taper engagement, contact pressure, and permanent deformation of the stem taper microgrooves. Interestingly, our model found assemblies using three hits at low loads (4 kN) led to decreased taper engagement, contact pressures and microgroove deformations throughout the stem taper compared with tapers assembled with one hit at the same magnitude. Conclusion. These findings suggest additional assembly hits at low loads lead to inferior taper interlock strength compared with one firm hit, which may be influenced by loading rate or material strain hardening. These unique models can estimate microgroove deformations representative of real contact mechanics seen on retrievals, which will enable us to better understand how both surgeon assembly techniques and implant design affect taper interlock strength. Cite this article: Bone Joint J 2020;102-B(7 Supple B):33–40

Aims. Revision total hip arthroplasty in patients with Vancouver type B3 fractures with Paprosky type IIIA, IIIB, and IV femoral defects are difficult to treat. One option for Paprovsky type IIIB and IV defects involves modular cementless, tapered, revision femoral components in conjunction with distal interlocking screws. The aim of this study was to analyze the rate of reoperations and complications and union of the fracture, subsidence of the stem, mortality, and the clinical outcomes in these patients. Methods. A total of 46 femoral components in patients with Vancouver B3 fractures (23 with Paprosky type IIIA, 19 with type IIIB, and four with type IV defects) in 46 patients were revised with a transfemoral approach using a modular, tapered, cementless revision Revitan curved femoral component with distal cone-in-cone fixation and prospectively followed for a mean of 48.8 months (SD 23.9; 24 to 112). The mean age of the patients was 80.4 years (66 to 100). Additional distal interlocking was also used in 23 fractures in which distal cone-in-cone fixation in the isthmus was < 3 cm. Results. One patient (2.2%) died during the first postoperative year. After six months, 43 patients (93.5%) had osseous, and three had fibrous consolidation of the fracture and the bony flap, 42 (91.3%) had bony ingrowth and four had stable fibrous fixation of the stem. No patient had radiolucency around the interlocking screws and no screw broke. One patient had non-progressive subsidence and two had a dislocation. The mean Harris Hip Score increased from of 57.8 points (SD 7.9) three months postoperatively to 76.1 points (SD 10.7) 24 months postoperatively. Conclusion. The 2° tapered, fluted revision femoral component with distal cone-in-cone-fixation, combined with additional distal interlocking in patients with bony deficiency at the isthmus, led to reproducibly good results in patients with a Vancouver B3 fracture and Paprosky type IIIA, IIIB, and IV defects with regard to union of the fracture, subsidence or loosening of the stem, and clinical outcomes. Cite this article: Bone Joint J 2024;106-B(4):344–351

If a surgeon is faced with altered lesser trochanter anatomy when revising the femoral component in revision total hip replacement, a peri-prosthetic fracture, or Paprosky type IIIb or type IV femoral bone loss, a modular tapered stem offers the advantages of accurately controlling femoral version and length. The splines of the taper allow rotational control, and improve the fit in femoral canals with diaphyseal bone loss. In general, two centimetres of diaphyseal contact is all that is needed to gain stability with modular tapered stems. By allowing the proximal body trial to rotate on a well-fixed distal segment during trial reduction, appropriate anteversion can be obtained in order to improve intra-operative stability, and decrease the dislocation risk. However, modular stems should not be used for all femoral revisions, as implant fracture and corrosion at modular junctions can still occur. Cite this article: Bone Joint J 2013;95-B, Supple A:95–7

Aims. The purpose of this study is to report our updated results at a minimum follow-up of 30 years using a first generation uncemented tapered femoral component in primary total hip arthroplasty (THA). Methods. The original cohort consisted of 145 consecutive THAs performed by a single surgeon in 138 patients. A total of 37 patients (40 hips) survived a minimum of 30 years, and are the focus of this review. The femoral component used in all cases was a first-generation Taperloc with a non-modular 28 mm femoral head. Clinical follow-up at a minimum of 30 years was obtained on every living patient. Radiological follow-up at 30 years was obtained on all but four. Results. Seven femoral components (18%) required revision, and none for septic loosening. Four well fixed stems were removed during acetabular revision and three were revised for late infection. One femoral component (3%) was loose by radiological criteria. The mean Harris Hip Score improved from 47 points (SD 4.62) preoperatively to 83 points (SD 9.27) at final follow-up. With revision for any reason as the endpoint, survival of the femoral component was 80% (95% confidence interval (CI) 61% to 90%) at 32 years. With revision for aseptic loosing femoral component, survival was 99% (95% CI 93% to 99%). Conclusion. With regards to aseptic loosening, the Taperloc femoral component provides excellent fixation at a mean follow-up of 32 years. Cite this article: Bone Jt Open 2023;4(2):79–86

Aims. The aim of this study was to radiologically evaluate the quality of cement mantle and alignment achieved with a polished tapered cemented femoral stem inserted through the anterior approach and compared with the posterior approach. Methods. A comparative retrospective study of 115 consecutive hybrid total hip arthroplasties or cemented hemiarthroplasties in 110 patients, performed through anterior (n = 58) or posterior approach (n = 57) using a collarless polished taper-slip femoral stem, was conducted. Cement mantle quality and thickness were assessed in both planes. Radiological outcomes were compared between groups. Results. No significant differences were identified between groups in Barrack grade on the anteroposterior (AP) (p = 0.640) or lateral views (p = 0.306), or for alignment on the AP (p = 0.603) or lateral views (p = 0.254). An adequate cement mantle (Barrack A or B) was achieved in 77.6% (anterior group, n = 45) and in 86% (posterior group, n = 49), respectively. Multivariate analysis revealed factors associated with unsatisfactory cement mantle (Barrack C or D) included higher BMI, left side, and Dorr Type C morphology. A mean cement mantle thickness of ≥ 2 mm was achieved in all Gruen zones for both approaches. The mean cement mantle was thicker in zone 7 (p < 0.001) and thinner in zone 9 for the anterior approach (p = 0.032). Incidence of cement mantle defects between groups was similar (6.9% (n = 4) vs 8.8% (n = 5), respectively; p = 0.489). Conclusion. An adequate cement mantle and good alignment can be achieved using a collarless polished tapered femoral component inserted through the anterior approach. Cite this article: Bone Joint J 2021;103-B(7 Supple B):46–52

Objectives. An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer. Methods. Analysis was carried out using highly accurate coordinate measuring to calculate volumetric and linear rates of the articular bearing surfaces and also the surfaces of the taper junctions. The relationship between taper wear rates and a number of variables, including bearing diameter and orientation of the acetabular component, was investigated. Results. The measured rates of wear and distribution of material loss from the taper surfaces appeared to show that the primary factor leading to taper failure is the increased lever arm acting on this junction in contemporary large-diameter metal-on-metal hip replacements. Conclusions. Our analysis suggests that varus stems, laterally engaging taper systems and larger head diameters all contribute to taper failure

Aims. The aim of this prospective cohort study was to evaluate the early migration of the TriFit cementless proximally coated tapered femoral stem using radiostereometric analysis (RSA). Methods. A total of 21 patients (eight men and 13 women) undergoing primary total hip arthroplasty (THA) for osteoarthritis of the hip were recruited in this study and followed up for two years. Two patients were lost to follow-up. All patients received a TriFit stem and Trinity Cup with a vitamin E-infused highly cross-linked ultra-high molecular weight polyethylene liner. Radiographs for RSA were taken postoperatively and then at three, 12, and 24 months. Oxford Hip Score (OHS), EuroQol five-dimension questionnaire (EQ-5D), and adverse events were reported. Results. At two years, the mean subsidence of the head and tip for the TriFit stem was 0.38 mm (SD 0.32) and 0.52 mm (SD 0.36), respectively. The total migration of the head and tip was 0.55 mm (SD 0.32) and 0.71 mm (SD 0.38), respectively. There were no statistically significant differences between the three to 12 months' migration (p = 0.105) and 12 to 24 months' migration (p = 0.694). The OHS and EQ-5D showed significant improvements at two years. Conclusion. The results of this study suggest that the TriFit femoral stem achieves initial stability and is likely to be stable in the mid and long term. A long-term outcome study is required to assess late mechanisms of failure and the effects of bone mineral density (BMD) related changes. Cite this article: Bone Joint J 2021;103-B(4):644–649

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507

Objectives. Favourable results for collarless polished tapered stems have been reported, and cement creep due to taper slip may be a contributing factor. However, the ideal cement thickness around polished stems remains unknown. We investigated the influence of cement thickness on stem subsidence and cement creep. Methods. We cemented six collarless polished tapered (CPT) stems (two stems each of small, medium and large sizes) into composite femurs that had been reamed with a large CPT rasp to achieve various thicknesses of the cement mantle. Two or three tantalum balls were implanted in the proximal cement in each femur. A cyclic loading test was then performed for each stem. The migration of the balls was measured three-dimensionally, using a micro-computed tomography (CT) scanner, before and after loading. A digital displacement gauge was positioned at the stem shoulder, and stem subsidence was measured continuously by the gauge. Final stem subsidence was measured at the balls at the end of each stem. Results. A strong positive correlation was observed between mean cement thickness and stem subsidence in the CT slices on the balls. In the small stems, the balls moved downward to almost the same extent as the stem. There was a significant negative correlation between cement thickness and the horizontal:downward ratio of ball movement. Conclusion. Collarless polished tapered stems with thicker cement mantles resulted in greater subsidence of both stem and cement. This suggests that excessive thickness of the cement mantle may interfere with effective radial cement creep. Cite this article: E. Takahashi, A. Kaneuji, R. Tsuda, Y. Numata, T. Ichiseki, K. Fukui, N. Kawahara. The influence of cement thickness on stem subsidence and cement creep in a collarless polished tapered stem: When are thick cement mantles detrimental? Bone Joint Res 2017;6:–357. DOI: 10.1302/2046-3758.65.BJR-2017-0028.R1

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Aims. The aims of this study were to evaluate the incidence of reoperation (all cause and specifically for periprosthetic femoral fracture (PFF)) and mortality, and associated risk factors, following a hemiarthroplasty incorporating a cemented collarless polished taper slip stem (PTS) for management of an intracapsular hip fracture. Methods. This retrospective study included hip fracture patients aged 50 years and older treated with Exeter (PTS) bipolar hemiarthroplasty between 2019 and 2022. Patient demographics, place of domicile, fracture type, delirium status, American Society of Anesthesiologists (ASA) grade, length of stay, and mortality were collected. Reoperation and mortality were recorded up to a median follow-up of 29.5 months (interquartile range 12 to 51.4). Cox regression was performed to evaluate independent risk factors associated with reoperation and mortality. Results. The cohort consisted of 1,619 patients with a mean age of 82.2 years (50 to 104), of whom 1,100 (67.9%) were female. In total, 29 patients (1.8%) underwent a reoperation; 12 patients (0.7%) sustained a PFF during the observation period (United Classification System (UCS)-A n = 2; UCS-B n = 5; UCS-C n = 5), of whom ten underwent surgical management. Perioperative delirium was independently associated with the occurrence of PFF (hazard ratio (HR) 5.92; p = 0.013) and surgery for UCS-B PFF (HR 21.7; p = 0.022). Neither all-cause reoperation nor PFF-related surgery was independently associated with mortality (HR 0.66; p = 0.217 and HR 0.38; p = 0.170, respectively). Perioperative delirium, male sex, older age, higher ASA grade, and pre-fracture residential status were independently associated with increased mortality risk following hemiarthroplasty (p < 0.001). Conclusion. The cumulative incidence of PFF at four years was 1.1% in elderly patients following cemented PTS hemiarthroplasty for a hip fracture. Perioperative delirium was independently associated with a PFF. However, reoperation for PPF was not independently associated with patient mortality after adjusting for patient-specific factors. Cite this article: Bone Jt Open 2024;5(4):269–276

Revision total hip arthroplasty (THA) is challenging when there is severe loss of bone in the proximal femur. The purpose of this study was to evaluate the clinical and radiographic outcomes of revision THA in patients with severe proximal femoral bone loss treated with a fluted, tapered, modular femoral component. Between January 1998 and December 2004, 92 revision THAs were performed in 92 patients using a single fluted, tapered, modular femoral stem design. Pre-operative diagnoses included aseptic loosening, infection and peri-prosthetic fracture. Bone loss was categorised pre-operatively as Paprosky types III-IV, or Vancouver B3 in patients with a peri-prosthetic fracture. The mean clinical follow-up was 6.4 years (2 to 12). A total of 47 patients had peri-operative complications, 27 of whom required further surgery. However, most of these further operations involved retention of a well-fixed femoral stem, and 88/92 femoral components (97%) remained in situ. Of the four components requiring revision, three were revised for infection and were well fixed at the time of revision; only one (1%) was revised for aseptic loosening. The most common complications were post-operative instability (17 hips, 19%) and intra-operative femoral fracture during insertion of the stem (11 hips, 12%). Diaphyseal stress shielding was noted in 20 hips (22%). There were no fractures of the femoral component. At the final follow-up 78% of patients had minimal or no pain. . Revision THA in patients with extensive proximal femoral bone loss using the Link MP fluted, tapered, modular stem led to a high rate of osseointegration of the stem at mid-term follow-up. Cite this article: Bone Joint J 2015; 97-B:312–17

Periprosthetic femoral fracture (PFF) is a potentially devastating complication after total hip arthroplasty, with historically high rates of complication and failure because of the technical challenges of surgery, as well as the prevalence of advanced age and comorbidity in the patients at risk. This study describes the short-term outcome after revision arthroplasty using a modular, titanium, tapered, conical stem for PFF in a series of 38 fractures in 37 patients. The mean age of the cohort was 77 years (47 to 96). A total of 27 patients had an American Society of Anesthesiologists grade of at least 3. At a mean follow-up of 35 months (4 to 66) the mean Oxford Hip Score (OHS) was 35 (15 to 48) and comorbidity was significantly associated with a poorer OHS. All fractures united and no stem needed to be revised. Three hips in three patients required further surgery for infection, recurrent PFF and recurrent dislocation and three other patients required closed manipulation for a single dislocation. One stem subsided more than 5 mm but then stabilised and required no further intervention. . In this series, a modular, tapered, conical stem provided a versatile reconstruction solution with a low rate of complications. Cite this article: Bone Joint J 2015;97-B:1031–7

Aims. The aim of this study was to compare early functional and health related quality of life outcomes (HRQoL) in patients who have undergone total hip arthroplasty (THA) using a bone conserving short stem femoral component and those in whom a conventional length uncemented component was used. Outcome was assessed using a validated performance based outcome instrument as well as patient reported outcome measures (PROMs). Patients and Methods. We prospectively analysed 33 patients whose THA involved a contemporary proximally porous coated tapered short stem femoral component and 53 patients with a standard conventional femoral component, at a minimum follow-up of two years. The mean follow-up was 31.4 months (24 to 39). Patients with poor proximal femoral bone quality were excluded. The mean age of the patients was 66.6 years (59 to 77) and the mean body mass index was 30.2 kg/m. 2. (24.1 to 41.0). Outcome was assessed using the Oxford Hip Score (OHS) and the University College Hospital (UCH) hip score which is a validated performance based instrument. HRQoL was assessed using the EuroQol 5D (EQ-5D). Results. There were no major peri-operative complications. There was no difference in the mean post-operative OHS, EQ-5D or function subscale of the UCH hip scores between the two groups. The mean pre-operative OHS and EQ-5D scores improved significantly (all p <  0.001). The mean functional component of the UCH hip score at final follow-up was 42.5 and 40.6 in the short stem and conventional stem groups, respectively. There was no statistically significant difference between the groups (p = 0.42). A total of seven patients (21.2%) in the short stem group and nine (16.98%) in the conventional group achieved a ceiling effect using the OHS; none did using the function subscale of the UCH hip score. Conclusion. The proximally porous coated tapered short stem femoral component achieves comparable short-term functional outcomes when compared with a conventional longer stem uncemented femoral component when THA is undertaken in patients with good bone quality. Cite this article: Bone Joint J 2017;99-B(4 Supple B):49–55

Aims. Although good clinical outcomes have been reported for monolithic tapered, fluted, titanium stems (TFTS), early results showed high rates of subsidence. Advances in stem design may mitigate these concerns. This study reports on the use of a current monolithic TFTS for a variety of indications. Methods. A multi-institutional retrospective study of all consecutive total hip arthroplasty (THA) and revision total hip arthroplasty (rTHA) patients who received the monolithic TFTS was conducted. Surgery was performed by eight fellowship-trained arthroplasty surgeons at four institutions. A total of 157 hips in 153 patients at a mean follow-up of 11.6 months (SD7.8) were included. Mean patient age at the time of surgery was 67.4 years (SD 13.3) and mean body mass index (BMI) was 28.9 kg/m. 2. (SD 6.5). Outcomes included intraoperative complications, one-year all-cause re-revisions, and subsidence at postoperative time intervals (two weeks, six weeks, six months, nine months, and one year). Results. There were eight intraoperative complications (4.9%), six of which were intraoperative fractures; none occurred during stem insertion. Six hips (3.7%) underwent re-revision within one year; only one procedure involved removal of the prosthesis due to infection. Mean total subsidence at latest follow-up was 1.64 mm (SD 2.47). Overall, 17 of 144 stems (11.8%) on which measurements could be performed had >5 mm of subsidence, and 3/144 (2.1%) had >10 mm of subsidence within one year. A univariate regression analysis found that additional subsidence after three months was minimal. A multivariate regression analysis found that subsidence was not significantly associated with periprosthetic fracture as an indication for surgery, the presence of an extended trochanteric osteotomy (ETO), Paprosky classification of femoral bone loss, stem length, or type of procedure performed (i.e. full revision vs conversion/primary). Conclusion. Advances in implant design, improved trials, a range of stem lengths and diameters, and high offset options mitigate concerns of early subsidence and dislocation with monolithic TFTS, making them a valuable option for femoral revision. Cite this article: Bone Joint J 2020;102-B(2):191–197

Tapered fluted titanium stems are increasingly used for femoral revision arthroplasty. They are available in modular and non-modular forms. Modularity has advantages when the bone loss is severe, the proximal femur is mis shapen or the surgeon is unfamiliar with the implant, but it introduces the risk of fracture of the stem at the junction between it and the proximal body segment. For that reason, and while awaiting intermediate-term results of more recently introduced designs of this junction, non-modularity has attracted attention, at least for straightforward revision cases. . We review the risks and causes of fracture of tapered titanium modular revision stems and present an argument in favour of the more selective use of modular designs. Cite this article: Bone Joint J 2016;98-B(1 Suppl A):50–3

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision

We retrospectively reviewed 175 patients (191 hips) who had undergone primary cemented total hip replacement between November 1992 and November 1995 using a collarless polished double-tapered femoral component after a minimum of ten years (mean 11.08; 10 to 12.8). All stems were implanted using contemporary cementing techniques with a distal cement restrictor, pressurised lavage, retrograde cementing with a gun and proximal pressurisation. Clinical outcome was assessed using the Harris Hip score. Radiological analysis was performed on calibrated plain radiographs taken in two planes. Complete radiological data on 110 patients (120 hips) and clinical follow-up on all the surviving 111 patients (122 hips) was available. The fate of all the hips was known. At final follow-up, the mean Harris Hip score was 86 (47 to 100), and 87 of 116 patients (75%) had good or excellent scores. Survival with revision of the stem for aseptic loosening as the endpoint was 100%; and survival with revision of the stem for any reason was 95.9% (95% confidence interval 87.8 to 96.8) at ten years. All the stems subsided vertically at the stem-cement interface in a predictable pattern, at an overall mean rate of 0.18 mm per year (0.02 to 2.16), but with a mean rate of 0.80 mm (0.02 to 2.5) during the first year. The mean total subsidence was 1.95 mm (0.21 to 24). Only three stems loosened at the cement-bone interface. There was excellent preservation of proximal femoral bone stock. There was a high incidence of Brooker III and IV heterotopic ossification affecting 25 patients (22%). The collarless polished tapered stem has an excellent clinical and radiological outcome at a minimum of ten years’ follow-up. The pattern and magnitude of subsidence of the stem within the cement mantle occurred in a predictable pattern, consistent with the design philosophy

We prospectively followed 191 consecutive collarless polished tapered (CPT) femoral stems, implanted in 175 patients who had a mean age at operation of 64.5 years (21 to 85). At a mean follow-up of 15.9 years (14 to 17.5), 86 patients (95 hips) were still alive. The fate of all original stems is known. The 16-year survivorship with re-operation for any reason was 80.7% (95% confidence interval 72 to 89.4). There was no loss to follow-up, with clinical data available on all 95 hips and radiological assessment performed on 90 hips (95%). At latest follow-up, the mean Harris hip score was 78 (28 to 100) and the mean Oxford hip score was 36 (15 to 48). Stems subsided within the cement mantle, with a mean subsidence of 2.1 mm (0.4 to 19.2). Among the original cohort, only one stem (0.5%) has been revised due to aseptic loosening. In total seven stems were revised for any cause, of which four revisions were required for infection following revision of the acetabular component. A total of 21 patients (11%) required some sort of revision procedure; all except three of these resulted from failure of the acetabular component. Cemented acetabular components had a significantly lower revision burden (three hips, 2.7%) than Harris Galante uncemented components (17 hips, 21.8%) (p < 0.001). The CPT stem continues to provide excellent radiological and clinical outcomes at 15 years following implantation. Its results are consistent with other polished tapered stem designs

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems. In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm. In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used. Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations. Cite this article: Bone Joint J 2015;97-B:463–72

The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used. The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm. 3. (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis. Cite this article: Bone Joint J 2015;97-B:1350–7

We carried out a clinical and radiological review of 103 cementless primary hip arthroplasties with a tapered rectangular grit-blasted titanium press-fit femoral component and a threaded conical titanium acetabular component at a mean follow-up of 14.4 years (10.2 to 17.1). The mean Harris hip score at the last follow-up was 89.2 (32 to 100). No early loosening and no fracture of the implant were found. One patient needed revision surgery because of a late deep infection. In 11 hips (10.7%), the reason for revision was progressive wear of the polyethylene liner. Exchange of the acetabular component because of aseptic loosening without detectable liner wear was carried out in three hips (2.9%). After 15 years the survivorship with aseptic loosening as the definition for failure was 95.6% for the acetabular component and 100% for the femoral component

Polished, tapered stems are now widely used for cemented total hip replacement and many such designs have been introduced. However, a change in stem geometry may have a profound influence on stability. Stems with a wide, rectangular proximal section may be more stable than those which are narrower proximally. We examined the influence of proximal geometry on stability by comparing the two-year migration of the Exeter stem with a more recent design, the CPS-Plus, which has a wider shoulder and a more rectangular cross-section. The hypothesis was that these design features would increase rotational stability. Both stems subsided approximately 1 mm relative to the femur during the first two years after implantation. The Exeter stem was found to rotate into valgus (mean 0.2°, . sd. 0.42°) and internally rotate (mean 1.28°, . sd. 0.99°). The CPS-Plus showed no significant valgus rotation (mean 0.2°, . sd. 0.42°) or internal rotation (mean −0.03°, . sd. 0.75°). A wider, more rectangular cross-section improves rotational stability and may have a better long-term outcome

Tapered, fluted, modular, titanium stems have a long history in Europe and are increasing in popularity in North America. We have reviewed the results at our institution looking at stem survival and clinical outcomes. Radiological outcomes and quality of life assessments have been performed and compared to cylindrical non-modular cobalt chromium stems. Survival at five years was 94%. This fell to 85% at ten years due to stem breakage with older designs. Review of radiology showed maintenance or improvement of bone stock in 87% of cases. Outcome scores were superior in tapered stems despite worse pre-operative femoral deficiency. Tapered stems have proved to be a useful alternative in revision total hip arthroplasty across the spectrum of femoral bone deficiency

Femoral impaction bone allografting has been developed as a means of restoring bone stock in revision total hip replacement. We report the results of 75 consecutive patients (75 hips) with a mean age of 68 years (35 to 87) who underwent impaction grafting using the Exeter collarless, polished, tapered femoral stem between 1992 and 1998. The mean follow-up period was 10.5 years (6.3 to 14.1). The median pre-operative bone defect score was 3 (interquartile range (IQR) 2 to 3) using the Endo-Klinik classification. The median subsidence at one year post-operatively was 2 mm (IQR 1 to 3). At the final review the median Harris hip score was 80.6 (IQR 67.6 to 88.9) and the median subsidence 2 mm (IQR 1 to 4). Incorporation of the allograft into trabecular bone and secondary remodelling were noted radiologically at the final follow-up in 87% (393 of 452 zones) and 40% (181 of 452 zones), respectively. Subsidence of the Exeter stem correlated with the pre-operative Endo-Klinik bone loss score (p = 0.037). The degree of subsidence at one year had a strong association with long-term subsidence (p < 0.001). There was a significant correlation between previous revision surgery and a poor Harris Hip score (p = 0.028), and those who had undergone previous revision surgery for infection had a higher risk of complications (p = 0.048). Survivorship at 10.5 years with any further femoral operation as the end-point was 92% (95% confidence interval 82 to 97)

Aims

Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes.

We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM).

Cemented femoral stems with force closed fixation designs have shown good clinical results despite high early subsidence. A new triple-tapered stem in this category (C-stem AMT) was introduced in 2005. This study compares this new stem with an established stem of similar design (Exeter) in terms of migration (as measured using radiostereometric analysis), peri-prosthetic bone remodelling (measured using dual energy x-ray densitometry, DXA), Oxford Hip Score, and plain radiographs.

A total of 70 patients (70 hips) with a mean age of 66 years (53 to 78) were followed for two years. Owing to missing data of miscellaneous reasons, the final analysis represents data from 51 (RSA) and 65 (DXA) patients. Both stems showed a typical pattern of migration: Subsidence and retroversion that primarily occurred during the first three months. C-stem AMT subsided less during the first three months (p = 0.01), before stabilising at a subsidence rate similar to the Exeter stem from years one to two. The rate of migration into retroversion was slightly higher for C-stem AMT during the second year (p = 0.03). Whilst there were slight differences in movement patterns between the stems, the C-stem AMT exhibits good early clinical outcomes and displays a pattern of migration and bone remodelling that predicts good clinical performance.

Cite this article: Bone Joint J 2015;97-B:755–61.

Aims

To evaluate the hypothesis that failed osteosynthesis of periprosthetic Vancouver type B1 fractures can be treated successfully with stem revision using a transfemoral approach and a cementless, modular, tapered revision stem with reproducible rates of fracture healing, stability of the revision stem, and clinically good results.

We report our experience of revision total hip replacement (THR) using the Revitan curved modular titanium fluted revision stem in patients with a full spectrum of proximal femoral defects. A total of 112 patients (116 revisions) with a mean age of 73.4 years (39 to 90) were included in the study. The mean follow-up was 7.5 years (5.3 to 9.1). A total of 12 patients (12 hips) died but their data were included in the survival analysis, and four patients (4 hips) were lost to follow-up. The clinical outcome, proximal bone regeneration and subsidence were assessed for 101 hips.

The mean Harris Hip Score was 88.2 (45.8 to 100) after five years and there was an increase of the mean Barnett and Nordin-Score, a measure of the proximal bone regeneration, of 20.8 (-3.1 to 52.7). Five stems had to be revised (4.3%), three (2.9%) showed subsidence, five (4.3%) a dislocation and two of 85 aseptic revisions (2.3%) a periprosthetic infection.

At the latest follow-up, the survival with revision of the stem as the endpoint was 95.7% (95% confidence interval 91.9% to 99.4%) and with aseptic loosening as the endpoint, was 100%. Peri-prosthetic fractures were not observed.

We report excellent results with respect to subsidence, the risk of fracture, and loosening after femoral revision using a modular curved revision stem with distal cone-in-cone fixation. A successful outcome depends on careful pre-operative planning and the use of a transfemoral approach when the anatomy is distorted or a fracture is imminent, or residual cement or a partially-secured existing stem cannot be removed. The shortest appropriate stem should, in our opinion, be used and secured with > 3 cm fixation at the femoral isthmus, and distal interlocking screws should be used for additional stability when this goal cannot be realised.

Cite this article: Bone Joint J 2014;96-B:889–95.

Aims. Periprosthetic hip fractures (PPFs) after total hip arthroplasty are difficult to treat. Therefore, it is important to identify modifiable risk factors such as stem selection to reduce the occurrence of PPFs. This study aimed to clarify differences in fracture torque, surface strain, and fracture type analysis between three different types of cemented stems. Methods. We conducted biomechanical testing of bone analogues using six cemented stems of three different types: collarless polished tapered (CPT) stem, Versys Advocate (Versys) stem, and Charnley-Marcel-Kerboull (CMK) stem. Experienced surgeons implanted each of these types of stems into six bone analogues, and the analogues were compressed and internally rotated until failure. Torque to fracture and fracture type were recorded. We also measured surface strain distribution using triaxial rosettes. Results. There was a significant difference in fracture torque between the three stem types (p = 0.036). Particularly, the median fracture torque for the CPT stem was significantly lower than that for the CMK stem (CPT vs CMK: 164.5 Nm vs 200.5 Nm; p = 0.046). The strain values for the CPT stem were higher than those for the other two stems at the most proximal site. The fracture pattern of the CPT and Versys stems was Vancouver type B, whereas that of the CMK stem was type C. Conclusion. Our study suggested that the cobalt-chromium alloy material, polished surface finish, acute-square proximal form, and the absence of a collar may be associated with lower fracture torque, which may be related to PPF. Cite this article: Bone Joint Res 2022;11(5):270–277

Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart. Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design. Bone Joint Res 2017;6:–350. DOI: 10.1302/2046-3758.65.BJR-2016-0325.R1

Aims. The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components. Methods. A total of 81 metal-on-metal Pinnacle hips paired with 12/14 stems were included in this study. Geometrical analysis was performed on each component, using coordinate and roundness measuring machines. The relationship between their as-manufactured diametrical clearance and volumetric wear was investigated. The Mann-Whitney U test and unpaired t-test were used, in addition to calculating the non-parametric Spearman's correlation coefficient, to statistically evaluate the acquired data. Results. The hips in this study were found to have had a median unworn diametrical clearance of 90.31 μm (interquartile range (IQR) 77.59 to 97.40); 32% (n = 26) were found to have been below the manufacturing tolerance. There was no correlation found between clearance and bearing (r. s. = -0.0004, p = 0.997) or taper (r. s. = 0.0048, p = 0.966) wear rates. The wear performance of hips manufactured within and below these specifications was not significantly different (bearing: p = 0.395; taper: p = 0.653). Pinnacles manufactured from 2007 onwards had a greater prevalence of bearing clearance below tolerance (p = 0.004). Conclusion. The diametrical clearance of Pinnacle hips did not influence their wear performance, even when below the manufacturing tolerance. The optimum clearance for minimizing hip implant wear remains unclear. Cite this article: Bone Joint Res 2020;9(8):515–523

Tribocorrosion at the head–neck taper interface – so-called ‘taperosis’ – may be a source of metal ions and particulate debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and corrosion in retrieved head–neck tapers in vivo for a minimum of two years (mean 8.7 years; 2.6 to 15.9). A total of 56 femoral heads ranging from 28 mm to 3 mm to 28 mm + 8 mm, and 17 femoral stems featuring a single taper design were included in the study. Fretting and corrosion were scored in three horizontally oriented concentric zones of each taper by stereomicroscopy. Head length was observed to affect fretting (p = 0.03), with 28 mm + 8 mm femoral heads showing greater total fretting scores than all other head lengths. The central zone of the femoral head bore taper was subject to increased fretting damage (p = 0.01), regardless of head length or stem offset. High-offset femoral stems were associated with greater total fretting of the bore taper (p = 0.04). Increased fretting damage is seen with longer head lengths and high-offset femoral stems, and occurs within a central concentric zone of the femoral head bore taper. Further investigation is required to determine the effect of increased head size, and variations in head–neck taper design. Cite this article: Bone Joint J 2015; 97-B:911–16

Aims. Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine fretting and corrosion on MDM liners, to analyze the corrosion products, and to examine histologically the periprosthetic tissues. Methods. A total of 60 retrieved liners were subjectively scored for fretting and corrosion. The corrosion products from the three most severely corroded implants were removed from the implant surface, imaged using scanning electron microscopy, and analyzed using Fourier-transform infrared spectroscopy. Results. Fretting was present on 88% (53/60) of the retrieved liners, and corrosion was present on 97% (58/60). Fretting was most often found on the lip of the taper at the transition between the lip and the dome regions. Macrophages and particles reflecting an innate inflammatory reaction to corrosion debris were noted in six of the 48 cases for which periprosthetic tissues were examined, and all were associated with retrieved components that had high corrosion scores. Conclusion. Our results show that corrosion occurs at the interface between MDM liners and shells and that it can be associated with reactions in the local tissues, suggesting continued concern that this problem may become clinically important with longer-term use of these implants. Cite this article: Bone Joint J 2021;103-B(7):1238–1246

Aims. Cement-in-cement revision of the femoral component represents a widely practised technique for a variety of indications in revision total hip arthroplasty. In this study, we compare the clinical and radiological outcomes of two polished tapered femoral components. Methods. From our prospectively collated database, we identified all patients undergoing cement-in-cement revision from January 2005 to January 2013 who had a minimum of two years' follow-up. All cases were performed by the senior author using either an Exeter short revision stem or the C-Stem AMT high offset No. 1 prosthesis. Patients were followed-up annually with clinical and radiological assessment. Results. A total of 97 patients matched the inclusion criteria (50 Exeter and 47 C-Stem AMT components). There were no significant differences between the patient demographic data in either group. Mean follow-up was 9.7 years. A significant improvement in Oxford Hip Score (OHS), Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC), and 12-item Short-Form Survey (SF-12) scores was observed in both cohorts. Leg lengths were significantly shorter in the Exeter group, with a mean of -4 mm in this cohort compared with 0 mm in the C-Stem AMT group. One patient in the Exeter group had early evidence of radiological loosening. In total, 16 patients (15%) underwent further revision of the femoral component (seven in the C-Stem AMT group and nine in the Exeter group). No femoral components were revised for aseptic loosening. There were two cases of femoral component fracture in the Exeter group. Conclusion. Our series shows promising mid-term outcomes for the cement-in-cement revision technique using either the Exeter or C-Stem AMT components. These results demonstrate that cement-in-cement revision using a double or triple taper-slip design is a safe and reliable technique when used for the correct indications. Cite this article: Bone Joint J 2021;103-B(7):1215–1221

Aims. The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads. Patients and Methods. A total of 28 OxZr femoral heads were retrieved during revision total hip arthroplasty (THA) and matched to 28 retrieved CoCr heads according to patient demographics. The mean age at index was 56 years (46 to 83) in the OxZr group and 70 years (46 to 92) in the CoCr group. Fretting and corrosion scores of the female taper of the heads were measured according to the modified Goldberg scoring method. Results. The OxZr-retrieved femoral heads showed significantly lower mean corrosion scores than the CoCr heads (1.3 (1 to 2.75) vs 2.1 (1 to 4); p < 0.01). Mean fretting scores were also significantly lower in the OxZr cohort when compared with the CoCr cohort (1.3 (1 to 2) vs 1.5 (1 to 2.25); p = 0.02). OxZr heads had more damage in the proximal region compared with the distal region of the head. Location had no impact on damage of CoCr heads. A trend towards increased corrosion in large heads was seen only in the CoCr heads, although this was not statistically significant. Conclusion. Retrieval analysis of OxZr femoral heads showed a decreased amount of fretting and corrosion compared with CoCr femoral heads. OxZr seems to be effective at reducing taper damage. Cite this article: Bone Joint J 2019;101-B:386–389

Aims. The aim of this study was to determine whether fixation, as opposed to revision arthroplasty, can be safely used to treat reducible Vancouver B type fractures in association with a cemented collarless polished tapered femoral stem (the Exeter). Methods. This retrospective cohort study assessed 152 operatively managed consecutive unilateral Vancouver B fractures involving Exeter stems; 130 were managed with open reduction and internal fixation (ORIF) and 22 with revision arthroplasty. Mean follow-up was 6.5 years (SD 2.6; 3.2 to 12.1). The primary outcome measure was revision of at least one component. Kaplan–Meier survival analysis was performed. Regression analysis was used to identify risk factors for revision following ORIF. Secondary outcomes included any reoperation, complications, blood transfusion, length of hospital stay, and mortality. Results. Fractures (B1 n = 74 (49%); B2 n = 50 (33%); and B3 n = 28 (18%)) occurred at median of 4.2 years (interquartile range (IQR) 1.2 to 9.2) after primary total hip arthroplasty (THA) (n = 138) or hemiarthroplasty (n = 14). Rates of revision and reoperation were significantly higher following revision arthroplasty compared to ORIF for B2 (p = 0.001) and B3 fractures (p = 0.050). Five-year survival was significantly better following ORIF: 92% (95% confidence interval (CI) 86.4% to 97.4%) versus 63% (95% CI 41.7% to 83.3%), p < 0.001. ORIF was associated with reduced blood transfusion requirement and reoperations, but there were no differences in medical complications, hospital stay, or mortality between surgical groups. No independent predictors of revision following ORIF were identified: where the bone-cement interface was intact, fixation of B2 or B3 fractures was not associated with an increased risk of revision. Conclusion. When the bone-cement interface was intact and the fracture was anatomically reducible, all Vancouver B fractures around Exeter stems could be managed with fixation as opposed to revision arthroplasty. Fixation was associated with reduced need for blood transfusion and lower risk of revision surgery compared with revision arthroplasty. Cite this article: Bone Joint J 2021;103-B(2):309–320

Objectives. Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event. Methods. A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors. Results. There was no significant difference between the taper and bearing wear rates of the ‘pre-2007’ and ‘2007 onwards’ groups (p = 0.67 and p = 0.39, respectively). Pinnacles implanted from 2007 onwards were revised after a mean time of 50 months, which was significantly earlier than the ‘pre-2007’ hips (96 months) (p < 0.001). A reduction in the time to revision was present year on year from 2003 to 2011. Conclusion. We found no difference in the wear rate of these implants based on the year of implantation. The ‘pre-2007’ hips had a two-fold greater time to revision than those implanted after 2007; this may be due to the increased surveillance of MoM hips following UK regulatory advice and several high-profile failures. Interestingly, we observed a decreasing trend in the mean time to revision every year from 2003 onwards. Cite this article: S. Bergiers, H. S. Hothi, J. Henckel, A. Eskelinen, J. Skinner, A. Hart. Wear performance of retrieved metal-on-metal Pinnacle hip arthroplasties implanted before and after 2007. Bone Joint Res 2018;7:595–600. DOI: 10.1302/2046-3758.711.BJR-2018-0143.R1

Aims. Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. Methods. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m. 2. , and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported. Results. A total of 43 patients were enrolled. At minimum follow-up of five years, 23 (53.4%) returned for clinical and radiological review, 25 (58.1%) had metal ion analysis performed, 19 (44.2%) underwent dual energy x-ray absorptiometry scans, and 25 (58%) completed a pain-drawing questionnaire. The mean modified Harris Hip Scores improved significantly from 54.8 (SD 19) preoperatively to 93.08 (SD 10.5) five years postoperatively (p < 0.001). One patient was revised for aseptic acetabular loosening. The mean cobalt levels increased from 0.065 μg/l (SD 0.03) to 0.08 (SD 0.05) and the mean titanium levels increased from 0.35 (SD 0.13) to 0.78 (SD 0.29). The femoral BMD ratio decreased in Gruen Zone 1 (91.9%) at five years postoperatively compared with the baseline scores at six weeks potoperatively. The femoral BMD ratio was maintained in Gruen zones 2 to 7. Conclusion. The use of a modular DM component and a cementless, tapered femoral stem shows excellent mid-term survivorship with minimal concerns for corrosion and metal ion release in a cohort of young, active patients undergoing primary THA. Cite this article: Bone Joint J 2021;103-B(7 Supple B):73–77

Aims. Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell (vs a monoblock acetabular component) have the advantage of allowing supplementary screw fixation, but the potential for corrosion between the liner and acetabulum has raised concerns. While DM prostheses have shown improved stability in patients deemed ‘high-risk’ for dislocation undergoing total hip arthroplasty (THA), their performance in young, active patients has not been reported. This study’s purpose was to assess clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) in young, active patients receiving a modular DM acetabulum and recently introduced titanium, proximally coated, tapered femoral stem design. Patients and Methods. This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m. 2. and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (. sd. 6.5)) were enrolled. All patients had a minimum of two years’ clinical follow-up. Patient-reported outcome measures, whole blood metal ion levels (ug/l), and periprosthetic femoral BMD were measured at baseline, as well as at one and two years postoperatively. Power analysis indicated 40 patients necessary to demonstrate a five-fold increase in cobalt levels from baseline (alpha = 0.05, beta = 0.80). A mixed model with repeated measures was used for statistical analysis. Results. Mean Harris Hip Scores improved from 54.1 (. sd. 20.5) to 91.2 (. sd. 10.8) at two years postoperatively (p < 0.001). All patients had radiologically well-fixed components, no patients experienced any instability, and no patients required any further intervention. Mean cobalt levels increased from 0.065 ug/l (. sd. 0.03) preoperatively to 0.30 ug/l (. sd. 0.51) at one year postoperatively (p = 0.01) but decreased at two years postoperatively to 0.16 ug/l (. sd. 0.23; p = 0.2). Four patients (9.3%) had a cobalt level outside the reference range (0.03 ug/l to 0.29 ug/l) at two years postoperatively, with values from 0.32 ug/l to 0.94 ug/l. The mean femoral BMD ratio was maintained in Gruen zones 2 to 7 at both one and two years postoperatively using this stem design. At two years postoperatively, mean BMD in the medial calcar was 101.5% of the baseline value. Conclusion. Use of a modular DM prosthesis and cementless, tapered femoral stem has shown encouraging results in young, active patients undergoing primary THA. Elevation in mean cobalt levels and the presence of four patients outside the reference range at two years postoperatively demonstrates the necessity of continued surveillance in this cohort. Cite this article: Bone Joint J 2019;101-B:365–371

Aims. The Exeter V40 cemented polished tapered stem system has demonstrated excellent long-term outcomes. This paper presents a systematic review of the existing literature and reports on a large case series comparing implant fractures between the Exeter V40 series; 125 mm and conventional length stem systems. Methods. A systematic literature search was performed adhering to the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) criteria. In parallel, we performed a retrospective single centre study of Exeter V40 femoral stem prosthetic fractures between April 2003 and June 2020. Results. There are 25 reported cases of such prosthetic fractures confined to small case series and case reports within the literature. We report an additional 19 cases to the literature (mean age 66.3 years (SD 11.7); 12 (63%) females; BMI 32.9 kg/m. 2. (SD 5.9)). The mean time from index procedure to fracture was 7.8 years (SD 3.6; 2.5 to 16.3). Exeter V40 stem fracture incidence was 0.15% and 1.21% for primary and revision arthroplasty, respectively. Incidence was significantly higher in revision arthroplasty (p < 0.001) and 125 mm length stems compared to ≥ 150 mm length stems (1.25% vs 0.13%, respectively; p < 0.001). When comparing different stem length cohorts, 125 mm short-stems were associated with stem-body fractures (92% vs 29%; p = 0.0095), earlier time to fracture (6.2 years vs 11.0 years; p = 0.0018), younger patient age at time of fracture (62.7 years vs 72.6 years; p = 0.037), and female sex (75% vs 43%; p = 0.326). Conclusion. This complication remains rare, although we report a significantly higher incidence at up to 17 years follow-up than in the literature. Short 125 mm length Exeter V40 stems undoubtedly have a role in restoring anatomy and biomechanics in smaller femoral geometries, although the surgeon has to appreciate the higher risk of stem fracture and the associated predisposing factors which may necessitate particular attention to surgical technique and planning. Cite this article: Bone Jt Open 2021;2(6):443–456

Objectives. The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. Methods. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels. Results. The mean wear rate of the articulating surfaces of the heads and acetabular components of all six joints tested was found to be 6.1 mm. 3. /year (4.1 to 7.6). The mean wear rate of the femoral head tapers of the five THAs was 0.054 mm. 3. /year (0.021 to 0.128) with a mean maximum wear depth of 5.7 µm (4.3 to 8.5). Conclusion. Although the taper wear was relatively low, the wear from the articulating surfaces was sufficient to provide concern and was potentially large enough to have been the cause of failure of these joints. The authors believe that patients implanted with the ReCap system, whether the resurfacing prosthesis or the THA, should be closely monitored. Cite this article: S. C. Scholes, B. J. Hunt, V. M. Richardson, D. J. Langton, E. Smith, T. J. Joyce. Explant analysis of the Biomet Magnum/ReCap metal-on-metal hip joint. Bone Joint Res 2017;6:113–122. DOI: 10.1302/2046-3758.62.BJR-2016-0130.R2