Aims. Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted
Cemented titanium stems in hip arthroplasty are associated with proximal cement-stem debonding and early failure. This was well publicised with the 3M Capital hip. However, corrosion in this setting has been reported with only one stem design and is less widely accepted. We present a series of 12 cemented titanium Furlong Straight Stems which required revision at a mean of 78 months for thigh pain. At revision the stems were severely corroded in a pattern which was typical of
Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti12Mo6Zr2Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients.Aims
Methods
We have investigated nine patients with cemented Furlong (JRI, London, UK) titanium hip replacements who presented with early pain despite a well-fixed, aseptic prosthesis. All were followed up clinically and radiologically at regular intervals. Pain was located in the thigh and was worse at night. Radiographs showed cortical hypertrophy of the femur around the tip of the stem. Eight of the nine patients subsequently required single-stage revision using an uncemented prosthesis, which relieved the pain. At revision, the pH of the tip of the stem was found to be highly acidic with macroscopic evidence of corrosion consisting of multiple layers of titanium oxides when studied by X-ray dispersive analysis. Cemented titanium implants have a potential for
This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth.Aims
Methods
Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m2, and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported.Aims
Methods
This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber. For the clinical arm of the study, observers independently reviewed postoperative radiographs of 551 primary THAs using MDM constructs from a single manufacturer over a three-year period, to identify the incidence of MDM liner-shell malseating. Multivariable logistic regression analysis was performed to identify risk factors including age, sex, body mass index (BMI), cup design, cup size, and the MDM case volume of the surgeon. For the in vitro arm, six pristine MDM implants with cobalt-chrome liners were tested in a simulated corrosion chamber. Three were well-seated and three were malseated with 6° of canting. The liner-shell couples underwent cyclic loading of increasing magnitudes. Fretting current was measured throughout testing and the onset of fretting load was determined by analyzing the increase in average current.Aims
Methods
This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys. Murine peritoneal macrophages were cultured and placed on stainless steel, CoCrMo, and Ti6Al4V discs into a 96-well plate. Cells were activated with interferon gamma and lipopolysaccharide. Macrophages on stainless steel discs produced significantly more nitric oxide (NO) compared to their control counterparts after eight to ten days and remained elevated for the duration of the experiment.Aims
Methods
The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour.Aims
Methods
We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time.Aims
Methods
We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a retrieval analysis of the fractured implants, performed by the manufacturer, were available for evaluation.Aims
Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
We sought to determine whether cobalt-chromium alloy (CoCr) femoral
stem tapers (trunnions) wear more than titanium (Ti) alloy stem
tapers (trunnions) when used in a large diameter (LD) metal-on-metal
(MoM) hip arthroplasty system. We performed explant analysis using validated methodology to
determine the volumetric material loss at the taper surfaces of
explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy
(n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs
with a rough male taper surface and a nominal included angle close
to 5.666° were included. Multiple regression modelling was undertaken
using taper angle, taper roughness, bearing diameter (horizontal
lever arm) as independent variables. Material loss was mapped using
a coordinate measuring machine, profilometry and scanning electron
microscopy.Aims
Patients and Methods
The aim of this study was to assess the effect
of frictional torque and bending moment on fretting corrosion at
the taper interface of a modular femoral component and to investigate
whether different combinations of material also had an effect. The
combinations we examined were 1) cobalt–chromium (CoCr) heads on
CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic
heads on CoCr stems. In test 1 increasing torque was imposed by offsetting the stem
in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and
8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14
Nm and 18 Nm. In test 2 we investigated the effect of increasing the bending
moment by offsetting the application of axial load from the midline
in the mediolateral plane. Increments of offset equivalent to head
+ 0 mm, head + 7 mm and head + 14 mm were used. Significantly higher currents and amplitudes were seen with increasing
torque for all combinations of material. However, Ti stems showed
the highest corrosion currents. Increased bending moments associated
with using larger offset heads produced more corrosion: Ti stems
generally performed worse than CoCr stems. Using ceramic heads did
not prevent corrosion, but reduced it significantly in all loading
configurations. Cite this article:
The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables.Objectives
Methods
Fretting and corrosion at the modular head/neck junction, known
as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse
reaction to metal debris (ARMD). We describe the outcome of revision
of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis
with emphasis on the risk of major complications. A total of 36 patients with a MoP THA who underwent revision
for ARMD due to trunnionosis were identified. Three were excluded
as their revision had been to another metal head. The remaining
33 were revised to a ceramic head with a titanium sleeve. We describe
the presentation, revision findings, and risk of complications in
these patients.Aims
Patients and Methods
Tribocorrosion at the head–neck taper interface
– so-called ‘taperosis’ – may be a source of metal ions and particulate
debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and
corrosion in retrieved head–neck tapers Head length was observed to affect fretting (p = 0.03), with
28 mm + 8 mm femoral heads showing greater total fretting scores
than all other head lengths. The central zone of the femoral head
bore taper was subject to increased fretting damage (p = 0.01),
regardless of head length or stem offset. High-offset femoral stems
were associated with greater total fretting of the bore taper (p
= 0.04). Increased fretting damage is seen with longer head lengths and
high-offset femoral stems, and occurs within a central concentric
zone of the femoral head bore taper. Further investigation is required
to determine the effect of increased head size, and variations in
head–neck taper design. Cite this article:
Many case reports and small studies have suggested that cobalt
ions are a potential cause of cardiac complications, specifically
cardiomyopathy, after metal-on-metal (MoM) total hip arthroplasty
(THA). The impact of metal ions on the incidence of cardiac disease
after MoM THA has not been evaluated in large studies. The aim of
this study was to compare the rate of onset of new cardiac symptoms
in patients who have undergone MoM THA with those who have undergone
metal-on-polyethylene (MoP) THA. Data were extracted from the Standard Analytics Files database
for patients who underwent MoM THA between 2005 and 2012. Bearing
surface was selected using International Classification of Diseases
ninth revision codes. Patients with a minimum five-year follow-up
were selected. An age and gender-matched cohort of patients who underwent
MoP THA served as a comparison group. New diagnoses of cardiac disease
were collected during the follow-up period. Comorbidities and demographics
were identified and routine descriptive statistics were used.Aims
Patients and Methods
Following the recall of modular neck hip stems
in July 2012, research into femoral modularity will intensify over
the next few years. This review aims to provide surgeons with an
up-to-date summary of the clinically relevant evidence. The development
of femoral modularity, and a classification system, is described.
The theoretical rationale for modularity is summarised and the clinical
outcomes are explored. The review also examines the clinically relevant problems
reported following the use of femoral stems with a modular neck. Joint replacement registries in the United Kingdom and Australia
have provided data on the failure rates of modular devices but cannot
identify the mechanism of failure. This information is needed to
determine whether modular neck femoral stems will be used in the
future, and how we should monitor patients who already have them implanted. Cite this article:
We present a series of 35 patients (19 men and
16 women) with a mean age of 64 years (36.7 to 75.9), who underwent
total hip replacement using the ESKA dual-modular short stem with
metal on-polyethylene bearing surfaces. This implant has a modular
neck section in addition to the modular head. Of these patients,
three presented with increasing post-operative pain due to pseudotumour
formation that resulted from corrosion at the modular neck-stem
junction. These patients underwent further surgery and aseptic lymphocytic
vaculitis associated lesions were demonstrated on histological analysis. Retrieval analysis of two modular necks showed corrosion at the
neck-stem taper. Blood cobalt and chromium levels were measured
at a mean of nine months (3 to 28) following surgery. These were
compared with the levels in seven control patients (three men and
four women) with a mean age of 53.4 years (32.1 to 64.1), who had
an identical prosthesis and articulation but with a prosthesis that
had no modularity at neck-stem junction. The mean blood levels of
cobalt in the study group were raised at 50.75 nmol/l (5 to 145)
compared with 5.6 nmol/l (2 to 13) in control patients. Corrosion at neck-stem tapers has been identified as an important
source of metal ion release and pseudotumour formation requiring
revision surgery. Finite element modelling of the dual modular stem
demonstrated high stresses at the modular stem-neck junction. Dual
modular cobalt-chrome hip prostheses should be used with caution
due to these concerns.