Ten acetabular cups coated with hydroxyapatite (HA) had originally been inserted in five primary and five revision total hip replacements. The thickness of the HA was 155 ± 35 μm. The cups, which were well-fixed, were retrieved, with their adherent tissue, at reoperation after 0.3 to 5.8 years because of infection (five hips), wear of polyethylene (three hips), and instability (two hips). Undecalcified sections showed a direct contact between bone and osteoid-like tissue which had formed directly onto the HA coating. The area within the threads and their mirror images, as well as the implant-tissue interfaces consisted of similar amounts of bone and soft tissue. Degradation of HA was seen in all hips. The mean thickness of the remaining HA coating was 97 μm (95% CI 94 to 101). The metal interface comprised 66% HA. The HA-tissue interface contained more bone than soft tissue (p = 0.001), whereas the metal-tissue interface included more soft tissue than bone (p = 0.019). Soft tissue at the implant interface and poor replacement of HA by bone may interfere with long-term fixation

Aims

Second-generation metal-on-metal (MoM) articulations in total hip arthroplasty (THA) were introduced in order to reduce wear-related complications. The current study reports on the serum cobalt levels and the clinical outcome at a minimum of 20 years following THA with a MoM (Metasul) or a ceramic-on-polyethylene (CoP) bearing.

We retrieved 159 femoral heads at revision surgery to determine changes in surface configuration. Macroscopic wear of the head was observed in three bipolar hip prostheses as a result of three-body wear. There was a considerable change in surface roughness in the internal articulation of bipolar hip prostheses. Roughness in alumina heads was almost the same as that in new cobalt-chromium heads. The annual linear wear rate of polyethylene cups with alumina heads was less than that of cups with cobalt-chromium alloy heads. Polyethylene wear was increased in the prostheses which had increased roughness of the head

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured. The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm. 3. /year for the 32 mm head, which was significantly higher than the 41.5 mm. 3. /year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates

We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads. In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles. Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs. Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements

We used radiostereometric analysis to compare wear rates between uncemented porous sockets and cemented all-polyethylene sockets in a series of 102 hips randomised for either a Harris-Galante or a Charnley cup. Wear was evaluated in 95 hips at a mean of five years (2 to 7). All hips had a cemented, 22 mm head mono-bloc Charnley stem. The mean annual wear rate was 0.09 mm in the Charnley sockets and 0.10 mm in the Harris-Galante sockets, with no statistically significant differences in wear, migration or rotation. We conclude that, up to five years, the wear characteristics of the modular and porous Harris-Galante socket resemble that of the Charnley socket

We made a semiquantitative study of the comparative histology of pseudomembranes from 12 loose cemented ceramic-ceramic and 18 metal-polyethylene total hip replacements. We found no significant difference in cellular reaction between the two groups, but there was a major difference in the origin of the particulate debris. In the metal-polyethylene group, polyethylene of articular origin was predominant, while in the ceramic-ceramic group the cellular reaction appeared to be a response to zirconia ceramic particles used to opacify cement used for fixation. Isolation and characterisation of the debris showed that the zirconia particles formed the greatest proportion (76%) in ceramic-ceramic hips, while alumina debris of articular origin formed only 12%. Our study has indicated that aseptic loosening of ceramic cups is not due to a response to debris generated at the articular interface, but to mechanical factors which lead to fragmentation of the cement

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

We analysed revised Mathys isoelastic polyacetal femoral stems with stainless-steel heads and polyethylene acetabular cups from eight patients in order to differentiate various types of particle of wear debris. Loosening of isoelastic femoral stems is associated with the formation of polyacetal wear particles as well as those of polyethylene and metal. All three types of particle were isolated simultaneously by tissue digestion followed by sucrose gradient centrifugation. Polyacetal particles were either elongated, ranging from 10 to 150 μm in size, or shred-like and up to 100 μm in size. Polyethylene particles were elongated or granules, and were typically submicron or micronsized. Polyacetal and polyethylene polymer particles were differentiated by the presence of BaSO. 4. , which is added as a radiopaque agent to polyacetal but not to polyethylene. This was easily detectable by back-scattered SEM analysis and verified by energy dispersive x-ray analysis. Two types of foreign-body giant cell (FBGC) were recognised in the histological specimens. Extremely large FBGCs with irregular polygonal particles showing an uneven, spotty birefringence in polarised light were ascribed to polyacetal debris. Smaller FBGCs with slender elongated particles shining uniformly brightly in polarisation were related to polyethylene. Mononucleated histiocytes containing both types of particle were also present. Our findings offer a better understanding of the processes involved in the loosening of polyacetal stems and indicate why the idea of ‘isoelasticity’ proved to be unsuccessful in clinical practice

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

Objectives

Third-body wear is believed to be one trigger for adverse results with metal-on-metal (MOM) bearings. Impingement and subluxation may release metal particles from MOM replacements. We therefore challenged MOM bearings with relevant debris types of cobalt–chrome alloy (CoCr), titanium alloy (Ti6Al4V) and polymethylmethacrylate bone cement (PMMA).

Objectives

Our study aimed to examine not only the incidence but also the impact of noise from two types of total hip replacement articulations: ceramic-on-ceramic and ceramic-on-polyethylene.

Finite element analysis was used to examine the initial stability after hip resurfacing and the effect of the procedure on the contact mechanics at the articulating surfaces. Models were created with the components positioned anatomically and loaded physiologically through major muscle forces. Total micromovement of less than 10 μm was predicted for the press-fit acetabular components models, much below the 50 μm limit required to encourage osseointegration. Relatively high compressive acetabular and contact stresses were observed in these models. The press-fit procedure showed a moderate influence on the contact mechanics at the bearing surfaces, but produced marked deformation of the acetabular components. No edge contact was predicted for the acetabular components studied.

It is concluded that the frictional compressive stresses generated by the 1 mm to 2 mm interference-fit acetabular components, together with the minimal micromovement, would provide adequate stability for the implant, at least in the immediate post-operative situation.

There are many methods for analysing wear volume in failed polyethylene acetabular components. We compared a radiological technique with three recognised ex vivo methods of measurement.

We tested 18 ultra-high-molecular-weight polyethylene acetabular components revised for wear and aseptic loosening, of which 13 had pre-revision radiographs, from which the wear volume was calculated based upon the linear wear. We used a shadowgraph technique on silicone casts of all of the retrievals and a coordinate measuring method on the components directly. For these techniques, the wear vector was calculated for each component and the wear volume extrapolated using mathematical equations. The volumetric wear was also measured directly using a fluid-displacement method. The results of each technique were compared.

The series had high wear volumes (mean 1385 mm³; 730 to 1850) and high wear rates (mean 205 mm³/year; 92 to 363). There were wide variations in the measurements of wear volume between the radiological and the other techniques. Radiograph-derived wear volume correlated poorly with that of the fluid-displacement method, co-ordinate measuring method and shadowgraph methods, becoming less accurate as the wear increased. The mean overestimation in radiological wear volume was 47.7% of the fluid-displacement method wear volume.

Fluid-displacement method, coordinate measuring method and shadowgraph determinations of wear volume were all better than that of the radiograph-derived linear measurements since they took into account the direction of wear. However, only radiological techniques can be used in vivo and remain useful for monitoring linear wear in the clinical setting.

Interpretation of radiological measurements of acetabular wear must be done judiciously in the clinical setting. In vitro laboratory techniques, in particular the fluid-displacement method, remain the most accurate and reliable methods of assessing the wear of acetabular polyethylene.

The complications of impaction bone grafting in revision hip replacement includes fracture of the femur and subsidence of the prosthesis. In this in vitro study we aimed to investigate whether the use of vibration, combined with a perforated tamp during the compaction of morsellised allograft would reduce peak loads and hoop strains in the femur as a surrogate marker of the risk of fracture and whether it would also improve graft compaction and prosthetic stability.

We found that the peak loads and hoop strains transmitted to the femoral cortex during graft compaction and subsidence of the stem in subsequent mechanical testing were reduced. This innovative technique has the potential to reduce the risk of intra-operative fracture and to improve graft compaction and therefore prosthetic stability.