We compared and quantified the modes of failure and patterns of wear of 11 Mittelmeier and 11 Ceraver-Ostal retrieved alumina-alumina hip prostheses with reference to the corresponding clinical and radiological histories. Macroscopic wear was assessed using a three-dimensional co-ordinate measuring machine. Talysurf contacting profilometry was used to measure surface roughness on a microscopic scale and SEM to determine mechanisms of wear at the submicron level. The components were classified into one of three categories of wear: low (no visible/measurable wear), stripe (elliptical wear stripe on the heads and larger worn areas on the cups) and severe (macroscopic wear, large volumes of material lost). Overall, the volumetric wear of the alumina-alumina prostheses was substantially less than the widely used metal and ceramic-on-polyethylene combinations. By identifying and eliminating the factors which accelerate wear, it is expected that the lifetime of these devices can be further increased.
We performed a histological and histomorphometric examination in five cadaver specimens of the femoral and acetabular components and the associated tissue which had been recovered between 3.3 and 6.2 years after primary total hip arthroplasty (THA) using a proximal hydroxyapatite (HA)-coated titanium alloy implant. All had functioned well during the patients’ life. All the stems were fixed in the femur and showed osseointegration of both the proximal and distal parts. The amount of residual HA was greatest in the distal metaphyseal sections, indicating that the rate of bone remodelling may be the main factor causing loss of HA. The level of activity of the patient was the only clinical factor which correlated with loss of coating. The percentage of bone-implant osseointegration was almost constant, regardless of the amount of HA residue, periprosthetic bone density or the time of implantation. HA debris was seldom observed and if present did not cause any adverse or inflammatory reaction. Partial debonding did occur in one case as a result of a polyethylene-induced inflammatory reaction.