We aimed to highlight the relationship between age and the architectural properties of trabecular bone, to outline the patterns in which the variations in these properties take place, and to investigate the influence of the architecture on the mechanical properties of trabecular bone in growing animals. We studied 30 lambs in three age groups and 20 sheep in two age groups. Cubes of subchondral bone were cut from the proximal tibia according to a standardised protocol. They were serially sectioned and their architectural properties were determined. Similar cubes were obtained from the identical anatomical position of the contralateral tibia and their compressive mechanical properties measured. The values obtained from the skeletally immature and mature individuals were compared. Multiple regression analyses were performed between the architectural and the mechanical properties.

The bone volume fraction, the mean trabecular volume, the architectural and the mechanical anisotropy, the elastic modulus, the bone strength, the energy absorption to failure, and the elastic energy correlated positively with increasing age whereas the connectivity density, the bone surface density, the ultimate strain, the absorption of viscoelastic energy and the relative loss of energy correlated inversely. The values of all variables were significantly different in the skeletally mature and immature groups. We determined the patterns in which the variations took place. The bone volume fraction of the trabecular bone tissue was found to be the major predictor of its compressive mechanical properties. Together with the mean trabecular volume and the bone surface density, it explained 81% of the variations in the compressive elastic modulus of specimens obtained from the contralateral tibiae.

Our aim was to determine the relationship between age and the mechanical and physical properties of trabecular bone, to describe the patterns in which the variations in these properties take place, and to investigate the influence of the physical properties on the mechanical characteristics of trabecular bone during growth. We used 30 lambs in three age groups and 20 sheep in two age groups. Cubes of subchondral bone were cut from the proximal tibia according to a standardised protocol. We performed non-destructive compression tests of the specimens in three orthogonal directions and compression tests to failure in the axial direction. The physical properties of the specimens were also determined. The data were correlated with age and compared in skeletally immature and mature animals. Multiple regression analyses were performed between the mechanical and the physical properties.

Age correlated positively with elastic modulus, bone strength, energy absorption to failure, elastic energy, mechanical anisotropy ratio, tissue density, apparent density, apparent ash density, and bone mineral content, and inversely with ultimate strain, viscoelastic energy absorption, relative energy loss, the collagen content of bone and the percentage porosity. The values of all variables were significantly different in the skeletally mature and immature groups. The apparent density of trabecular bone tissue was found to be the major predictor of its compressive mechanical properties. Together with the content of bone muscle and bone collagen, the apparent density could explain 84% of the variation in the elastic modulus, whereas only a small portion of the variation in ultimate strain could be explained by the variation in apparent density.

We tested in compression specimens of human proximal tibial trabecular bone from 31 normal donors aged from 16 to 83 years and determined the mechanical properties, density and mineral and collagen content.

Young’s modulus and ultimate stress were highest between 40 and 50 years, whereas ultimate strain and failure energy showed maxima at younger ages. These age-related variations (except for failure energy) were non-linear.

Tissue density and mineral concentration were constant throughout life, whereas apparent density (the amount of bone) varied with ultimate stress. Collagen density (the amount of collagen) varied with failure energy. Collagen concentration was maximal at younger ages but varied little with age.

Our results suggest that the decrease in mechanical properties of trabecular bone such as Young’s modulus and ultimate stress is mainly a consequence of the loss of trabecular bone substance, rather than a decrease in the quality of the substance itself. Linear regression analysis showed that collagen density was consistently the single best predictor of failure energy, and collagen concentration was the only predictor of ultimate strain.