Aims. Highly cross-linked polyethylene (HXLPE) greatly reduces wear in total hip arthroplasty, compared to conventional polyethylene (CPE). Cross-linking is commonly achieved by irradiation. This study aimed to compare the degree of cross-linking and in vitro wear rates across a cohort of retrieved and unused polyethylene cups/liners from various brands. Methods. Polyethylene acetabular cups/liners were collected at one centre from 1 April 2021 to 30 April 2022. The trans-vinylene index (TVI) and oxidation index (OI) were determined by Fourier-transform infrared spectrometry. Wear was measured using a pin-on-disk test. Results. A total of 47 specimens from ten brands were included. The TVI was independent of time in vivo. A linear correlation (R. 2. = 0.995) was observed between the old and current TVI standards, except for vitamin E-containing polyethylene. The absorbed irradiation dose calculated from the TVI corresponded to product specifications for all but two products. For one electron beam-irradiated HXLPE, a mean dose of 241% (SD 18%) of specifications was determined. For another, gamma-irradiated HXLPE, a mean 41% (SD 13%) of specifications was determined. Lower wear was observed for higher TVI. Conclusion. The TVI is a reliable measure of the absorbed irradiation dose and does not alter over time in vivo. The products of various brands differ by manufacturing details and consequently cross-linking characteristics. Absorption and penetration of electron radiation and gamma radiation differ, potentially leading to higher degrees of cross-linking for electron radiation. There is a non-linear, inverse correlation between TVI and in vitro wear. The wear resistance of the HXLPE with low TVI was reduced and more comparable to CPE. Cite this article: Bone Joint Res 2024;13(11):682–693

Aims. The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components. Methods. A total of 81 metal-on-metal Pinnacle hips paired with 12/14 stems were included in this study. Geometrical analysis was performed on each component, using coordinate and roundness measuring machines. The relationship between their as-manufactured diametrical clearance and volumetric wear was investigated. The Mann-Whitney U test and unpaired t-test were used, in addition to calculating the non-parametric Spearman's correlation coefficient, to statistically evaluate the acquired data. Results. The hips in this study were found to have had a median unworn diametrical clearance of 90.31 μm (interquartile range (IQR) 77.59 to 97.40); 32% (n = 26) were found to have been below the manufacturing tolerance. There was no correlation found between clearance and bearing (r. s. = -0.0004, p = 0.997) or taper (r. s. = 0.0048, p = 0.966) wear rates. The wear performance of hips manufactured within and below these specifications was not significantly different (bearing: p = 0.395; taper: p = 0.653). Pinnacles manufactured from 2007 onwards had a greater prevalence of bearing clearance below tolerance (p = 0.004). Conclusion. The diametrical clearance of Pinnacle hips did not influence their wear performance, even when below the manufacturing tolerance. The optimum clearance for minimizing hip implant wear remains unclear. Cite this article: Bone Joint Res 2020;9(8):515–523

Objectives. Unicompartmental knee arthroplasty (UKA) is an alternative to total knee arthroplasty with isolated medial or lateral compartment osteoarthritis. However, polyethylene wear can significantly reduce the lifespan of UKA. Different bearing designs and materials for UKA have been developed to change the rate of polyethylene wear. Therefore, the objective of this study is to investigate the effect of insert conformity and material on the predicted wear in mobile-bearing UKA using a previously developed computational wear method. Methods. Two different designs were tested with the same femoral component under identical kinematic input: anatomy mimetic design (AMD) and conforming design inserts with different conformity levels. The insert materials were standard or crosslinked ultra-high-molecular-weight polyethylene (UHMWPE). We evaluated the contact pressure, contact area, wear rate, wear depth, and volumetric wear under gait cycle loading conditions. Results. Conforming design inserts had the lower contact pressure and larger contact area. However, they also had the higher wear rate and volumetric wear. The improved wear performance was found with AMD inserts. In addition, the computationally predicted volumetric wear of crosslinked UHMWPE inserts was less than half that of standard UHMWPE inserts. Conclusion. Our results showed that increasing conformity may not be the sole predictor of wear performance; highly crosslinked mobile-bearing polyethylene inserts can also provide improvement in wear performance. These results provide improvements in design and materials to reduce wear in mobile-bearing UKA. Cite this article: Bone Joint Res 2019;8:563–569

Objectives. Unicompartmental knee arthroplasty (UKA) is an alternative to total knee arthroplasty for patients who require treatment of single-compartment osteoarthritis, especially for young patients. To satisfy this requirement, new patient-specific prosthetic designs have been introduced. The patient-specific UKA is designed on the basis of data from preoperative medical images. In general, knee implant design with increased conformity has been developed to provide lower contact stress and reduced wear on the tibial insert compared with flat knee designs. The different tibiofemoral conformity may provide designers the opportunity to address both wear and kinematic design goals simultaneously. The aim of this study was to evaluate wear prediction with respect to tibiofemoral conformity design in patient-specific UKA under gait loading conditions by using a previously validated computational wear method. Methods. Three designs with different conformities were developed with the same femoral component: a flat design normally used in fixed-bearing UKA, a tibia plateau anatomy mimetic (AM) design, and an increased conforming design. We investigated the kinematics, contact stress, contact area, wear rate, and volumetric wear of the three different tibial insert designs. Results. Conforming increased design showed a lower contact stress and increased contact area. In addition, increased conformity resulted in a reduction of the wear rate and volumetric wear. However, the increased conformity design showed limited kinematics. Conclusion. Our results indicated that increased conformity provided improvements in wear but resulted in limited kinematics. Therefore, increased conformity should be avoided in fixed-bearing patient-specific UKA design. We recommend a flat or plateau AM tibial insert design in patient-specific UKA. Cite this article: Y-G. Koh, K-M. Park, H-Y. Lee, K-T. Kang. Influence of tibiofemoral congruency design on the wear of patient-specific unicompartmental knee arthroplasty using finite element analysis. Bone Joint Res 2019;8:156–164. DOI: 10.1302/2046-3758.83.BJR-2018-0193.R1

Objectives. The determination of the volumetric polyethylene wear on explanted material requires complicated equipment, which is not available in many research institutions. Our aim in this study was to present and validate a method that only requires a set of polyetheretherketone balls and a laboratory balance to determine wear. Methods. The insert to be measured was placed on a balance, and a ball of the appropriate diameter was inserted. The cavity remaining between the ball and insert caused by wear was filled with contrast medium and the weight of the contrast medium was recorded. The volume was calculated from the known density of the liquid. The precision, inter- and intraobserver reliability, were determined by four investigators on four days using nine inserts with specified wear (0.094 ml to 1.626 ml), and the intra-class correlation coefficient was calculated. The feasibility of using this method in routine clinical practice and the time required for measurement were tested on 84 explanted inserts by one investigator. Results. In order to get the mean for all investigators and determinations, the deviation between the measured and specified wear was -0.08 ml . (sd. 0.12; -0.21 to 0.11). The interobserver reliability was 0.989 ml (95% confidence interval (CI) 0.964 to 0.997) and the intraobserver reliability was 0.941 for observer 1 (95% CI 0.846 to 0.985), 0.983 for observer 2 (95% CI 0.956 to 0.995), 0.939 for observer 3 (95% CI 0.855 to 0.984), and 0.934 for observer 4 (95% CI 0.790 to 0.984). The mean time required to examine the samples was two minutes . (sd. 2; 1 to 5). Conclusion. The method presented here was shown to be sufficiently precise for many settings and is a cost-effective and quick method of determining the volumetric wear of explanted acetabular components. However, the measurement of wear for scientific purposes will probably continue to involve more accurate and dedicated laboratory equipment. Cite this article: Bone Joint Res 2017;6:530–534

Objectives. Computed tomography (CT) plays an important role in evaluating wear and periacetabular osteolysis (PAO) in total hip replacements. One concern with CT is the high radiation exposure since standard pelvic CT provides approximately 3.5 millisieverts (mSv) of radiation exposure, whereas a planar radiographic examination with three projections totals approximately 0.5 mSv. The objective of this study was to evaluate the lowest acceptable radiation dose for dual-energy CT (DECT) images when measuring wear and periacetabular osteolysis in uncemented metal components. Materials and Methods. A porcine pelvis with bilateral uncemented hip prostheses and with known linear wear and acetabular bone defects was examined in a third-generation multidetector DECT scanner. The examinations were performed with four different radiation levels both with and without iterative reconstruction techniques. From the high and low peak kilo voltage acquisitions, polychrmoatic images were created together with virtual monochromatic images of energies 100 kiloelectron volts (keV) and 150 keV. Results. We could assess wear and PAO while substantially lowering the effective radiation dose to 0.7 mSv for a total pelvic view with an accuracy of around 0.5 mm for linear wear and 2 mm to 3 mm for PAO. Conclusion. CT for detection of prosthetic wear and PAO could be used with clinically acceptable accuracy at a radiation exposure level equal to plain radiographic exposures. Cite this article: B. Sandgren, M. Skorpil, P. Nowik, H. Olivecrona, J. Crafoord, L. Weidenhielm, A. Persson. Assessment of wear and periacetabular osteolysis using dual energy computed tomography on a pig cadaver to identify the lowest acceptable radiation dose. Bone Joint Res 2016;5:307–313. DOI: 10.1302/2046-3758.57.2000566

Aims. The survival of humeral hemiarthroplasties in patients with relatively intact glenoid cartilage could theoretically be extended by minimizing the associated postoperative glenoid erosion. Ceramic has gained attention as an alternative to metal as a material for hemiarthroplasties because of its superior tribological properties. The aim of this study was to assess the in vitro wear performance of ceramic and metal humeral hemiarthroplasties on natural glenoids. Methods. Intact right cadaveric shoulders from donors aged between 50 and 65 years were assigned to a ceramic group (n = 8, four male cadavers) and a metal group (n = 9, four male cadavers). A dedicated shoulder wear simulator was used to simulate daily activity by replicating the relevant joint motion and loading profiles. During testing, the joint was kept lubricated with diluted calf serum at room temperature. Each test of wear was performed for 500,000 cycles at 1.2 Hz. At intervals of 125,000 cycles, micro-CT scans of each glenoid were taken to characterize and quantify glenoid wear by calculating the change in the thickness of its articular cartilage. Results. At the completion of the wear test, the total thickness of the cartilage had significantly decreased in both the ceramic and metal groups, by 27% (p = 0.019) and 29% (p = 0.008), respectively. However, the differences between the two were not significant (p = 0.606) and the patterns of wear in the specimens were unpredictable. No significant correlation was found between cartilage wear and various factors, including age, sex, the size of the humeral head, joint mismatch, the thickness of the native cartilage, and the surface roughness (all p > 0.05). Conclusion. Although ceramic has better tribological properties than metal, we did not find evidence that its use in hemiarthroplasty of the shoulder in patients with healthy cartilage is a better alternative than conventional metal humeral heads. Cite this article: Bone Joint J 2024;106-B(11):1273–1283

Aims. Limited implant survival due to aseptic cup loosening is most commonly responsible for revision total hip arthroplasty (THA). Advances in implant designs and materials have been crucial in addressing those challenges. Vitamin E-infused highly cross-linked polyethylene (VEPE) promises strong wear resistance, high oxidative stability, and superior mechanical strength. Although VEPE monoblock cups have shown good mid-term performance and excellent wear patterns, long-term results remain unclear. This study evaluated migration and wear patterns and clinical and radiological outcomes at a minimum of ten years’ follow-up. Methods. This prospective observational study investigated 101 cases of primary THA over a mean duration of 129 months (120 to 149). At last follow-up, 57 cases with complete clinical and radiological outcomes were evaluated. In all cases, the acetabular component comprised an uncemented titanium particle-coated VEPE monoblock cup. Patients were assessed clinically and radiologically using the Harris Hip Score, visual analogue scale (pain and satisfaction), and an anteroposterior radiograph. Cup migration and polyethylene wear were measured using Einzel-Bild-Röntgen-Analyze software. All complications and associated treatments were documented until final follow-up. Results. Clinical assessment showed persistent major improvement in all scores. On radiological assessment, only one case showed a lucent line (without symptoms). At last follow-up, wear and migration were below the critical thresholds. No cup-related revisions were needed, indicating an outstanding survival rate of 100%. Conclusion. Isoelastic VEPE cups offer high success rates and may prevent osteolysis, aseptic loosening, and the need for revision surgeries in the long term. However, longer follow-up is needed to validate our findings and confirm the advantages offered by this cup. Cite this article: Bone Jt Open 2024;5(10):825–831

Introduction. Large-scale retrieval studies have shown backside wear in tibial inserts is dependent on the surface roughness of the tibial tray. Manufacturers acknowledge this design factor and have responded with the marketing of mirror-finished trays, which are clinically proven to have lower wear rates in comparison to historically “rough” (e.g. grit blasted) trays. While the relationship between wear and surface roughness has been explored in other polymer applications, the quantitative dependence of backside wear rate on quantitative surface finish has not yet been established for modern devices. The present study evaluates small-excursion polyethylene wear on pucks of a variety of surface roughnesses. The objective of this study is to determine where inflection points exist in the relationship between surface roughness and wear rate. Materials and Methods. An AMTI Orthopod, 6-station pin on disk tribotest was designed to mimic worst-case in vivo backside wear conditions based on published retrieval analyses. Titanium (Ti6Al4V) pucks with six different surface roughness preparations (Sa ranges from 0.06 um to 1.06 um) were characterized with white light profilometry. Never implanted polyethylene tibial inserts (never irradiated, EtO sterilized) were machined into 6 mm diameter cylindrical pins. Fretting-type motion was conducted in a 2mm square pattern at 2Hz under 100 N constant force in 25% bovine serum lubricant for 1.35 million cycles in triplicate. Mass measurements were taken every 225 thousand cycles. Results. Over the range of surface roughness studied (Sa = 0.06 – 1.06 µm), wear rate grew logistically. The wear rate for highly polished titanium (Sa = 0.06 µm) was not statistically different from less-polished titanium with Sa of 0.14 µm (p > 0.1). Titanium pucks having the highest surface roughness (Sa > 0.5µm), removed material significantly faster than those with roughness less than 0.3µm. The results of these tests suggest that Ti trays with Sa less than 0.15µm may yield equivalent clinical backside wear results, while pucks with Sa greater than 0.15µm begin to have increased wear rates that may be clinically significant. The two pucks with Sa greater than 0.5 µm yielded wear rates failing to be statistically differentiable (p = 0.059), corresponding with the flattening of the logistic curve. Discussion. These results suggest that baseplates with Sa less than 0.15 µm may ultimately yield clinically equivalent outcomes. The wear rate curve changes slope between Sa 0.14 and 0.22 µm and continues to increase across the range of surface roughnesses studied. The wear rates on rough pucks (Sa > 0.5 µm) showed high variation, reducing the ability to distinguish the two statistically (p = 0.059). Further study will better distinguish wear properties at higher surface roughnesses. Conclusion. These findings demonstrate that there may be a range of finishes between a mirror polish and grit blast that may produce clinically equivalent wear rates. This work provides justification for further study into the relationship between backside wear, baseplate tray roughness, and material choices. For any figures or tables, please contact authors directly

Aims. Micromotion of the polyethylene (PE) inlay may contribute to backside PE wear in addition to articulate wear of total knee arthroplasty (TKA). Using radiostereometric analysis (RSA) with tantalum beads in the PE inlay, we evaluated PE micromotion and its relationship to PE wear. Methods. A total of 23 patients with a mean age of 83 years (77 to 91), were available from a RSA study on cemented TKA with Maxim tibial components (Zimmer Biomet). PE inlay migration, PE wear, tibial component migration, and the anatomical knee axis were evaluated on weightbearing stereoradiographs. PE inlay wear was measured as the deepest penetration of the femoral component into the PE inlay. Results. At mean six years’ follow-up, the PE wear rate was 0.08 mm/year (95% confidence interval 0.06 to 0.09 mm/year). PE inlay external rotation was below the precision limit and did not influence PE wear. Varus knee alignment did not influence PE wear (p = 0.874), but increased tibial component total translation (p = 0.041). Conclusion. The PE inlay was well fixed and there was no relationship between PE stability and PE wear. The PE wear rate was low and similar in the medial and lateral compartments. Varus knee alignment did not influence PE wear. Cite this article: Bone Joint Res 2024;13(5):226–236

Aims. Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA. Methods. We prospectively reviewed 19 patients who underwent primary cementless THA with the XLPE acetabular liner (X3) and a 36 or 40 mm femoral head with a resultant liner thickness of at least 5.8 mm. RSA radiographs at one week, six months, and one, two, five, and ten years postoperatively and femoral head penetration within the acetabular component were measured with UmRSA software. Of the initial 19 patients, 12 were available at the ten-year time point. Results. The median proximal, 2D, and 3D wear rates calculated between one and ten years were all less than 0.005 mm/year, with no patient recording a proximal wear rate of more than 0.021 mm/year. Importantly, there was no increase in the wear rate between five and ten years. Conclusion. The very low wear rate of X3 XLPE liners with larger articulations remains encouraging for the future clinical performance of this material. Cite this article: Bone Jt Open 2023;4(11):839–845

Aims. Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning. Methods. 3D CT imaging was combined with a recently validated method of mapping bearing surface wear in retrieved hip implants. The asymmetrical stabilizing fins of Birmingham hip replacements (BHRs) allowed the co-registration of their acetabular wear maps and their computational models, segmented from CT scans. The in vivo location of edge-wear was measured within a standardized coordinate system, defined using the anterior pelvic plane. Results. Edge-wear was found predominantly along the superior acetabular edge in all cases, while its median location was 8° (interquartile range (IQR) -59° to 25°) within the anterosuperior quadrant. The deepest point of these scars had a median location of 16° (IQR -58° to 26°), which was statistically comparable to their centres (p = 0.496). Edge-wear was in closer proximity to the superior apex of the cups with greater angles of acetabular inclination, while a greater degree of anteversion influenced a more anteriorly centred scar. Conclusion. The anterosuperior location of edge-wear was comparable to the degradation patterns observed in acetabular cartilage, supporting previous findings that hip joint forces are directed anteriorly during a greater portion of walking gait. The further application of this novel method could improve the current definition of optimal and safe acetabular component positioning. Cite this article: Bone Joint Res 2021;10(10):639–649

Introduction: Although acetabular cup wear is usually reported in terms of penetration (measured from radiographs), true wear – wear volume – depends on several variables. This study examined how these variables affect the calculation of the theoretical wear volume at the low wear penetrations found with highly cross-linked polyethylene (XLPE) cups. Method: A computerised numerical analysis technique was used to calculate the “exact” theoretical wear volume of an acetabular cup under a variety of circumstances, including: variations in wear direction, head size, and initial radial discrepancy (i.e. initial difference between socket and head sizes). The validity of published wear volume formulae was assessed. The effects of creep and wear measurement error were also assessed. Results: For a given wear penetration, as the wear direction (relative to the cup base) increased, the wear volume increased – almost doubling as the direction reached 60°. The initial radial discrepancy made a substantial difference to the calculated wear volume at penetrations less than 1 mm. At low penetrations, its neglect caused an overestimation of wear volume of well over 100%. Creep volume was substantially overestimated because of this. An analysis of wear measurement error showed that the calculation of wear direction (an important variable in the calculation of wear volume) was severely affected at low penetrations by the precision of penetration measurements. For a penetration precision of ±0.25 mm (as reported for the Martell Hip Analysis Suite), the maximum wear direction error was ±39° at a penetration of 0.4 mm. When the precision was ±0.1 mm (as with RSA), this reduced to ±14°. Discussion: Many studies have shown the superior wear performance XLPE acetabular cups compared with standard PE cups. In those studies, comparison in terms of wear penetration was possible because of the large difference in penetrations between the two groups. This study has shown that true wear (wear volume) is significantly affected by wear direction (relative to the cup), the initial radial discrepancy, and the femoral head size. The differences in penetrations when comparing two types of XLPE cups would not be so large and it is therefore necessary to compare the two groups in terms of wear volume. Published formulae for estimating the wear volume of acetabular cups do not take the initial radial discrepancy into account, and they can substantially overestimate the wear volume in the penetration range encountered with XLPE cups. Creep volume is also greatly overestimated. Since wear volume varies with wear direction, the wear measurement technique must be capable of accurately determining the wear direction. This analysis has shown that only RSA might have sufficient precision to determine the wear direction at the medium-term penetrations encountered with XLPE cups

Purpose:. Although short term outcomes of reverse total shoulder arthroplasty (rTSA) have been promising, long-term success may be limited due to complications, including scapular notching. Scapular notching has been explained primarily as a mechanical erosion, however, generation of wear debris may lead to further biologic changes contributing to the severity of scapular notching. Highly cross-linked ultra-high molecular weight polyethylene (UHMWPE) has been used routinely in constrained joint applications such as total hip arthroplasty for reduction of wear debris particles. Although rTSA shares similarity in design conformity, conventional UHMWPE remains the gold standard. Methods:. A commercially available hip simulator was converted to a 12-station rTSA wear simulator. Conventional and highly cross-linked UHMWPE humeral liners were subjected to 5,000,000 cycles of alternating abduction-adduction and flexion-extension loading profiles. Every 250,000 cycles, liners were evaluated with gravimetric wear measurements and test serum was collected for morphological characterization of wear particles. Results:. Highly cross-linked UHMWPE liners (36.5 ± 10.0 mm. 3. /million cycle) exhibited significantly lower volumetric wear rates compared to conventional UHMWPE liners (83.6 ± 20.6 mm3/million cycle) (p < 0.001) (Figure 1). The flexion-extension loading profile exhibited significantly higher wear rates for both conventional (p < 0.001) and highly cross-linked UHMWPE (p < 0.001) compared to the abduction-adduction loading profile. Highly cross-linked wear particles had an equivalent circle diameter significantly smaller than wear particles from conventional UHMWPE (p < 0.001) (Figure 2). Highly cross-linked wear particles were also significantly less fibrillar than conventional UHMWPE particles with respect to particle aspect ratio (p < 0.001) and particle roundness (p < 0.001). Conclusion:. This is the first study to examine the effect of cross-linked PE in a rTSA wear simulation. Highly cross-linked UHMWPE liners significantly reduced UHWMPE wear and subsequent particle generation. More favorable wear properties with the use of highly cross-linked UHMWPE may lead to increased rTSA device longevity and fewer complications but must be weighed against the impact of reduced mechanical properties

Abstract. Introduction. The Oxford Unicompartmental Knee Replacement's (OUKR's) fully-congruent design minimises polyethylene wear. Consequently, wear is a rare failure mechanism. Phase-3 OUKR linear wear at 5 years was higher than previous OUKR phases, but very low compared to fixed-bearing UKRs. This study aimed to measure OUKR bearing wear at 10 years and investigate factors that may affect wear. Methodology. Bearing thickness for 39 OUKRs from a randomised study was calculated using radiostereometric analysis at regular intervals up to 10 years. Data for 39 and 29 OUKRs was available at 5 and 10 years, respectively. As creep occurs early, wear rate was calculated using linear regression between 6 months and 10 years. Relationships between wear and patient factors, fixation method, Oxford Knee Score (OKS), bearing position, and component position were analysed. Results. The mean wear rate was 0.06mm/year. Fixation method, age, OKS, component size, and bearing size had no correlation with wear. A higher BMI was associated with lower wear (p=0.01). Bearings more than 4mm from the wall had significantly more wear (p=0.04) than those less than 4mm from the wall. There was a linear correlation between the femoral component contact area on the bearing and wear (p=0.04). Conclusions. Phase-3 bearing wear rate is constant, significantly higher than previous OUKR phases at 10 years, and may increase the risk of long-term bearing failure. To minimise complications associated with wear, size 4 bearings should be used in young patients and manufacturing bearings from more durable, highly crosslinked polyethylene should be studied

The purpose of the study was to compare the mechanical properties, oxidation and wear resistance of a vitamin E blended and moderately crosslinked polyethylene for total knee arthroplasty (MXE) in comparison with clinically established polyethylene materials. The following polyethylene materials were tested: CPE (30 kGy e-beam sterilized), XLPE (75 kGy gamma crosslinked @ 100°C), ViXLPE (0.1 % vitamin E blended, 80 kGy e-beam crosslinked @ 100°C), and MXE (0.1 % vitamin E blended polyethylene, 30 kGy gamma sterilized). For the different tests, the polyethylene materials were either unaged or artificially aged for two or six weeks according to ASTM F2003-02. The oxidation index was measured based on ASTM F2102 at a 1 mm depth. Small punch testing was performed based on ASTM F2977. Mechanical properties were measured on unaged materials according to ASTM D638. Wear simulation was performed on a load controlled 3 + 1 station knee wear simulator (EndoLab GmbH, Thansau, Germany) capable of reproducing loads and movement of highly demanding activities (HDA) as well as ISO 14243-1 load profiles. The load profiles were applied for 5 million cycles (mc) or delamination of the polyethylene components. Medium size AS e.motion. ®. PS Pro (Aesculap AG, Tuttlingen, Germany) femoral and tibial components with a ZrN-multilayer surface, as well as Columbus. ®. CR cobalt-chrome alloy femoral and tibial components were tested. Particle analysis was performed on the serum samples of the ISO 14243-1 wear simulations based on ISO 17853:2011 and ASTM F1877. The analysis of the mechanical properties show that moderately crosslinked polyethylene (MXE) might be a superior material for total knee arthroplasty applications [Schwiesau et al. 2021]. The addition of vitamin E in a moderately crosslinked polyethylene prevented its oxidation, kept its mechanical characteristics, and maintained a low wear, even under a HDA knee wear simulation

Abstract. Unicompartment knee replacement (UKR) has been an effective treatment of isolated medial compartment osteoarthritis (OA). There has been several studies which suggest that patellofemoral (PFJ) wear may not be a relative contraindication for UKR with no statistical difference in failure rates. There is currently conflicting evidence on the role of BMI. We will review if BMI and PFJ wear impacts on the post operative functional scores following UKR. A retrospective review of a prospectively collected database was performed. Data was collected between 26/6/2014 and 25/8/2022. 159 UKR procedures were identified. BMI and PFJ cartilage wear were collected. Oxford knee scores (OKS) were collected at > 2 years. PFJ wear was split into International Cartilage Research Society (ICRS) grades I&II and III&IV. 159 UKR procedures were identified, of these 115 had 2 year follow up. There were 77 who had OKS recorded at 2 years. For PFJ wear there was no statistical difference in the median OKS at 2 years 45 vs 43.5 (p=0.408). Assessing the BMI the median was 29kg/m. 2. , range 20–43kg/m. 2. Spearman's rank was performed to assess the correlation between BMI and >2 year OKS, this demonstrated a moderately negative correlation p(df)=−0.339 (CI 95% −0.538, −0.104) p=0.004. There is no statistically significant difference in >2 year OKS following UKR regardless of PFJ wear. There is a moderately negative correlation between BMI and >2 year OKS which was significant p=0.004. Therefore BMI is a more important consideration when counselling patients for UKR

Introduction. Previous studies have shown that third body damage to the femoral head in metal-on-polyethylene hip replacement bearings can lead to accelerated wear of the polyethylene liners. The resulting damage patterns observed on retrieved metal heads are typically scratches and scrapes. The damage created in vitro must represent the third body damage that occurs clinically. A computational model was developed to predict the acceleration of wear of polyethylene articulating against in vitro damaged femoral heads. This involved using a damage registry from retrieval femoral heads to develop standardized templates of femoral head scratches statistically representative of retrieval damage. The aim of this study was to determine the wear rates of polyethylene liners articulating against retrievals and artificially damaged metal heads for the purpose of validating a computational wear prediction model; and to develop and validate an in vitro standardised femoral head damage protocol for pre-clinical testing of hip replacements. Materials and Methods. Twenty nine, 32mm diameter, metal-on-moderately cross-linked polyethylene bearings (Marathon. TM. ) inserted into Ti-6Al-4V shells (Pinnacle. ®). were tested in this study. All products were manufactured by DePuy Synthes, Warsaw, Indiana, USA. Following a retrieval study seven different damage patterns were defined, and these were applied to the femoral heads using a four-degree-of-freedom CNC milling machine (Figure 1). The ProSim 10-station pneumatic hip joint simulator (Simulation Solutions, UK) was used for experimental wear simulation using standard gait cycles and testing each experimental group for 3 million cycles. The acetabular cups were inclined at 35° on the simulator (equivalent to 45° in vivo). The wear volumes were determined using a microbalance (Mettler-Toledo XP205, Switzerland) at one million cycle intervals. Statistical analysis used was one way ANOVA followed by a post hoc analysis with significance taken at p<0.05. Results. Different damage patterns accelerated the wear of polyethylene at different rates (Figure 2). The moderately scratched and severely scratched heads caused a 2 fold (p<0.01) and 5.5 fold (p<0.01) increase when compared to the wear rate of the undamaged head group. However, the scraped damage caused a lower increase than the scratched heads, with a 1.4 fold (p=0.2) increase for the moderately scraped heads and 2.6 fold (p<0.01) increase for the severely scraped heads. The moderate hybrid and severe hybrid groups resulted in a similar increase to the scraped heads with 1.8 fold (p<0.01) increase with the moderate hybrid and 3 fold (p<0.01) increase with the severe hybrid. The wear of polyethylene against the mild hybrid and retrieved heads was not significantly different (p= 0.9) to the wear against undamaged heads. Discussion. A standardised protocol for generating in vitro damage representative of clinically occurring damage on femoral heads for preclinical testing purposes is needed. The wear rates of polyethylene liners articulating against the retrieval heads were similar to those articulating against the undamaged femoral heads. This study has shown the variations in wear rate of polyethylene bearing under different damage patterns generated in vitro. The wear prediction computational model predict similar trends of the wear acceleration reported in the experimental study

Introduction:. Backside wear has been previously reported through in-vitro and in-vivo to have a significant contribution to the total wear in rotating bearing TKRs. The present study investigated the contribution of backside wear to the total wear in the PFC Sigma rotating platform mobile bearing TKR. In addition, the wear results were compared to the computed wear rates of the PFC Sigma fixed bearing TKR, with two different bearing materials. Materials and Methods:. The commercially available PFC Sigma rotating platform mobile bearing and PFC Sigma fixed bearing total knee replacements, size 3 (DePuy, UK) were tested, with either conventional or moderately cross-linked (5 MRad) GUR1020 UHMWPE bearing materials. The computational wear model for the knee implants was based on the contact area and an independent experimentally determined non-dimensional wear coefficient [1,2,3]. The experimental wear test for the mobile bearing was force controlled using the ISO anterior-posterior force (ISO14243-1-2009). However, due to time limitation of the explicit simulation required to run the force controlled model, the simulation was run using the AP displacements taken from the experimental knee simulator which was run under the ISO AP force. The Sigma fixed bearing TKR was run under high level of anterior-posterior displacements (maximum of 10 mm). Results and Discussion:. The rotating platform bearing showed lower wear rates, compared to that of the PFC Sigma fixed bearing, for both conventional and moderately cross-linked UHMWPE bearing materials (Fig. 1). Moreover, the results showed a high contribution of backside wear to the total wear, approximately 1 mm. 3. /million cycles (∼30% of the total wear). The computational wear predictions were in good agreements with the clinical and experimental measurements [4,5]. Contrasting the effect of bearing material on wear prediction, introducing the moderately cross-linked UHMWPE as a bearing material reduced the predicted wear rates by approximately 1 mm. 3. /million cycles in rotating platform bearing, compared to more than 5 mm. 3. /million cycles in PFC fixed bearing TKR. This reduced effect of cross-linking on wear in mobile bearing was mainly attributed to the lower cross-shear ratios in these bearings, compared to fixed bearings, and the less dependency of wear in moderately cross-linked UHMWPE on the degree of cross-shear, compared to conventional UHMWPE. Decreasing the degree of cross-shear from higher values (Sigma curved insert, high kinematic) to lower ones (rotating platform bearing) changed the predicted wear rates from 8.7 to 3.3 and from 3.4 to 2.4 (mm. 3. /million cycles), for conventional and moderately cross-linked UHMWPE materials respectively (Fig. 2). Conclusion:. The modelling confirmed the previous experimental observations of very low wear with the rotating platform knee. The models also determined the level of wear from the backside of the rotating platform knee which was approximately 1 mm. 3. /million cycles. The fixed bearing knee with moderately cross linked polyethylene also showed low wear at approximately 3 mm. 3. /million cycles. These low wear rates were determined under high kinematic walking cycles conditions. Future work will consider additional conditions

In the retrieval analysis of explanted hip joints, the estimation of wear volume and visualization of wear pattern are commonly used to evaluate in-vivo performance. While many studies report wear volumes from explanted hips, it is important to understand the limitations of these estimates including the sources and magnitude of uncertainty of the reported results. This study builds on a previous uncertainty analysis by Carmignato et al. to quantify the magnitude of uncertainty caused by the assumption that the as-manufactured shape of an explanted hip component is a perfect sphere. Synthetic data sets representing idealized measurements of spheroidal explants (prolate, oblate and pinched) with a nominal diameter of 50 mm were generated. These data sets represent the shape and magnitude of form deviations observed for explanted hip components (Figure 1). Data were simulated for either unworn components or those with a known volume and magnitude of wear simulated to represent 5 µm penetration of a 49.90 mm femoral head into an acetabular cup (Table 1). The volume of wear and wear pattern were estimated using a custom Matlab script developed for analysis of metrology data from explanted hip joints. This script fits a least squares sphere to data points in unworn, as manufactured regions of the surface to estimate the as-manufactured shape of the component. The diameter of the best fit sphere, and wear volume were compared to the known wear depths and volumes from the synthetic datasets. The results showed that the Matlab script estimated a wear volume of up to 1.4 mm. 3. for an unworn cup with a radial deviation of 10 µm. The maximum error of 13.3 mm. 3. was for a pinched cup with wear at the pole. The complete results are shown in Table 2. In some cases with aspherical form deviations, the least squares sphere fitted to the synthetic data was displaced in the Z direction with respect to the origin of the spheroid and the radius of the least squares sphere was outside the range of the principal radii of the spheroid. For instance, in case 5, the center was shifted 22 µm vertically from the mathematical center. The results from this study show that the magnitude of uncertainty due to form deviations on wear volume varies depending on the shape and magnitude of the form deviations and in some cases was greater than 10 mm. 3. A further important finding is that in some instances, the diameter and center of the least squares sphere fitted to the unworn regions may not be consistent with the mathematical radius and center of the synthetic data. This may have important implications for the “reverse engineering” of the as-manufactured dimensions from worn explanted hip joints. Please contact authors directly for the figure:. Figure 1 Graphical depiction of a) synthetic data set, b) deviation map of a hemispherical acetabular cup with simulated wear, c) deviation map of a prolate spheroid with simulated wear at rim with color bar set to ±5 microns, d) deviation map of pinched ellipsoid with simulated wear at 45 degrees from pole