Introduction. The advantages of metal on metal (MOM) hip replacement are decreased wear rate, preservation of bone stock, anatomical restoration and enhanced stability. Large amounts of metal wear particles and metal ions are released which may induce adverse reactions including local soft tissue toxicity, hypersensitivity reactions, bone loss and risk of carcinogenesis. Aseptic loosening can be the result of a peri prosthetic osteolysis generated as a result of a biological response to particulate wear debris. Our aim in this study was to determine whether a steeply inclined acetabular component would give rise to a higher concentration of metal ions. Patients and methods. Between April 2003 and June 2006, 22 patients had MOM hip replacement for osteoarthritis by a single Surgeon. There were 12 male and 10 female patients. The average age at the time of surgery was 56 years (Range: 44–69 years). We divided the 22 patients into 2 groups, one group (A) of 11 patients with the acetabular inclination angle more than 50 degrees and the other group (B) of 11 patients with the angle less than 50 degrees. The inclination of the acetabular cup was measured using a standard AP radiograph of the pelvis. The patients had metal ion levels (blood chromium and serum cobalt) measured at an average follow up of 3.2 years (Range 2.4 to 5 years). Results. Mean blood chromium level in the group A (146 nM/L) was significantly higher (p=0.005) than in Group B (92 nM/L). Mean serum cobalt level in the group A (245 nM/L) was significantly higher (p=0.002) than in Group B (110 nM/L). Discussion. The early to mid term published results of MOM hip replacements have been encouraging. There are, however, a number of concerns about the MOM bearing. Although its wear rate is low, it still releases metal ions into the body particularly cobalt and chromium since most metal on metal bearings are made of a cobalt chromium alloy. The long-term consequences of increased levels of these ions in the body are not known. High concentrations of Co and Cr are toxic and are known to interfere with a number of biological functions. There also have been recent reports of soft tissue reactions with MOM hip replacement. In the light of these concerns, it is important to examine factors which may influence the release of metal ions after MOM hip replacement. It has been reported in the recent literature that the position of the acetabular component will influence the bearing wear inturn leading to the release of metal ions after MOM hip replacement. Our findings indicate that steeply inclined acetabular components with an inclination angle greater than 50 degrees gives rise to higher concentration of metal ions

INTRODUCTION. Cementless Total Hip Replacement surgery is a well established procedure for relative young patients with severe hip disease. Excellent long term clinical results have been published on the performance of the femoral component. With growing clinical experience, our concern focused on excessive wear of the Ultra High Molecular Weight Polyethylene (UHMWPE) ringloc liner of the Mallory Head cementless Total Hip Prosthesis. After its introduction in our clinic in 1997, this implant is still in use without any modification. We were concerned that due to premature liner wear, the performance of this implant would not be compliant with the international guideline on implant survival (NICE guidelines: at 10 year follow up, 90% of all implants should still be in situ). Our objective was to establish the amount of liner wear in our first 200 MH implants. METHODS. Our first 200 patients consecutively treated with Mallory Head prostheses were followed up to obtain a recent digital image. Follow up was complete for 181 (90.5%) of our 200 patients. Ten had died and nine were not able or willing to come for follow up. The mean duration of follow up was 8.3 years (range: 8–13). The 181 recent digital images were classified as either excessive wear or no excessive wear by two independent orthopedic surgeons. Next, liner wear was measured in the 2D frontal plane using PolyWare Pro/3D Digital Version Rev 5.1 software (Draftware Developers, Conway, USA). A threshold for excessive liner wear was set at 0.2mm/year, according to literature. RESULTS. Using software for measuring PE wear, 46.7% of all patients had excessive UHMWPE wear (> 0.2mm/yr). There was no relation between the amount of wear and BMI, gender, component size or the acetabular inclination angle. Thirteen patients (6.5%) were revised. Nine of these revisions were for excessive liner wear or aseptic loosening (4.5%). For now, our series of cementless Mallory Head prostheses is compliant with the NICE guideline on implant survival. However, with the measured amount of wear we expect to see a significant increase in the number of revisions for liner wear in the near future. DISCUSSION. Our clinical observation of premature UHMWPE wear proved correct. The measured amount of UHMWPE wear is consistent with the few other studies published on this subject. Although we present a retrospective study, limiting the strength of our results, we have included a large group of patients with acceptable loss to follow up. It is unclear if the observed wear will lead to a sharp increase in the number of revisions within the next few years. Possibly, future revisions will be complicated by loss of acetabular bone stock following the pathofysiological reaction to wear particles. Our results can probably be generalised for any district hospital