Background
Currently, stailess steel, titanium and carbon-fiber reinforced polyetheretherketone (CF-PEEK) plates are available for the treatment of distal radius fractures. Since the possibility to create a less rigid fixation may represent an advantage in case of ostheoporotic or poor quality bone, the aim of this study is to compare the biomechanical properties of these three materials in terms of bending stiffness with a single static load and after cyclical loading, simulating physiologic wrist motion.
Materials and Methods
Three volar plating systems with fixed angle were tested: Zimmer stainless steel volar lateral column (Warsaw, IN); Hand Innovations titanium DVR (Miami, FL); Lima Corporate CF-PEEK DiPHOS-RM (San Daniele Del Friuli, Udine, Italy). For each type of plate tested four right synthetic composite bone radii were used. An unstable, extraarticular fracture was simulated by making an 8 mm gap with a saw starting 12 mm proximal to the articular surface of the radius on the distal radio-ulnar joint side. The osteotomies were made perpendicular to the long axis of the bone to allow for a consistent fracture gap on the dorsal and volar sides of the radius. Plates were implanted using all the distal and proximal fixation holes [Fig. 1]. Each synthetic radius model was potted in methylmethacrylate and tested in a bi-axial servo-hydraulic test frame (MTS Minibionix 858, universal testing machine) for load to failure by advancing a cobalt chrome sphere centered over the articular surface at a constant rate of displacement of 5 mm/min. The sphere was advanced until the construct failed or the dorsal edges of the fracture met. The resultant force was defined as bending stiffness pre fatigue. Three constructs for each plate were then dynamically loaded for 6000 cycles of fatigue at a frequency of 10Hz, with a load value corresponding to the 50% of the previously calculated bending strength. Finally, the constructs were loaded to failure, measuring the bending stiffness post fatigue.
Introduction. Total hip replacement with metal-on-polymer (MoP) hip prostheses is a successful treatment for late-stage osteoarthritis. However, the wear debris generated from the polymer acetabular liners remains a problem as it can be associated with osteolysis and aseptic loosening of the implant. This has led to the investigation of more wear resistant polymers in orthopaedics. Cross-linked polyethylene (XLPE) is now the gold-standard acetabular liner material. However, we asked if carbon fibre reinforced