We report the results of our continued review of 11 total hip arthroplasties using 22.225 mm alumina ceramic femoral heads on a Charnley flanged stem, articulating with chemically cross-linked polyethylene. There was an initial bedding-in of up to 0.41 mm at the articular surface in the first two years. This had not progressed further, at a minimum follow-up of 15 years. Radiographically no femoral or acetabular component showed loosening or osteolysis

We report the results of our continued review of 14 hip arthroplasties using alumina ceramic femoral heads with cross-linked polyethylene cups. There have been no complications and a very low rate of penetration. This was 0.02 mm per year after an initial ‘bedding-in’ period of two years. There has been no change in the mean rate between our earlier study at six years and the current results at 10 to 11 years. The use of these bearing surfaces appears to reduce the potential amount of polyethylene debris and may provide the next logical stage in the development of the Charnley low-friction arthroplasty

From 1981 to 1983, we implanted Bioceram type-4 and type-5 prostheses in 61 hips in 54 patients with osteoarthritis secondary to acetabular dysplasia, congenital subluxation, or congenital dislocation of the hip. Fifty-seven hips in 50 patients were followed for a mean of 11.1 years (10 to 13). The mean age of the patients at operation was 53 years (31 to 70). Functional evaluation using the Merle d'Aubigne and Postel hip score showed a 77% success rate. Radiological loosening occurred in three femoral (5%) and 16 acetabular components (28%). Autologous femoral head grafts were used in 18 hips and became incorporated, giving mechanical support to the socket except for one which occupied a large weight-bearing area and eventually collapsed. The mean polyethylene wear was 1.1 mm (0 to 3.6) and the mean wear rate was 0.10 mm/year (0 to 0.31). A high rate of wear correlated with calcar resorption (p > 0.002) but not with acetabular loosening. There was no breakage of a ceramic head. Study of the ceramic heads and polyethylene sockets retrieved after ten years showed excellent surface roughness, sphericity, and bending strength for the heads but scratches and voids were seen on the sockets.

We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads.

In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles.

Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs.

Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements.

Aims

The aim of this study was to report the mid-term clinical outcome of cemented unlinked J-alumina ceramic elbow (JACE) arthroplasties when used in patients with rheumatoid arthritis (RA).

The purpose of this study was to evaluate the clinical results of a newly designed prosthesis to replace the body of the talus in patients with aseptic necrosis. Between 1999 and 2006, 22 tali in 22 patients were replaced with a ceramic prosthesis. A total of eight patients were treated with the first-generation prosthesis, incorporating a peg to fix into the retained neck and head of the talus, and the remaining 14 were treated with the second-generation prosthesis, which does not have the peg. The clinical results were assessed by the American Orthopaedic Foot and Ankle Society ankle/hindfoot scale.

The mean follow-up was 98 months (18 to 174). The clinical results of the first-generation prostheses were excellent in three patients, good in one, fair in three and poor in one. There were, however, radiological signs of loosening, prompting a change in design. The clinical results of the second-generation prostheses were excellent in three patients, good in five, fair in four and poor in two, with more favourable radiological appearances. Revision was required using a total talar implant in four patients, two in each group.

Although the second-generation prosthesis produced better results, we cannot recommend the use of a talar body prosthesis. We now recommend the use of a total talar implant in these patients.

Aims. Our aim in this study was to describe a continuing review of 11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral heads on a Charnley flanged femoral component, articulating against a silane crosslinked polyethylene. Patients and Methods. Nine patients (11 THAs) were reviewed at a mean of 27.5 years (26 to 28) post-operatively. Outcome was assessed using the d’Aubigne and Postel, and Charnley scores and penetration was recorded on radiographs. In addition, the oxidation of a 29-year-old shelf-aged acetabular component was analysed. Results. The mean clinical outcome scores remained excellent at final follow-up. The mean total penetration remained 0.41 mm (0.40 to 0.41). There was no radiographic evidence of acetabular or femoral loosening or osteolysis. There was negligible oxidation in the shelf-aged sample despite gamma irradiation and storage in air. Conclusion. These results highlight the long-term stability and durability of this type of crosslinked, antioxidant containing polyethylene when used in combination with a small diameter alumina ceramic femoral head. Cite this article: Bone Joint J 2017;99-B:1286–9

Aims. Total ankle arthroplasty (TAA) has become the most reliable surgical solution for patients with end-stage arthritis of the ankle. Aseptic loosening of the talar component is the most common complication. A custom-made artificial talus can be used as the talar component in a combined TAA for patients with poor bone stock of the talus. The purpose of this study was to investigate the functional and clinical outcomes of combined TAA. Patients and Methods. Ten patients (two men, eight women; ten ankles) treated using a combined TAA between 2009 and 2013 were matched for age, gender, and length of follow-up with 12 patients (one man, 11 women; 12 ankles) who underwent a standard TAA. All had end-stage arthritis of the ankle. The combined TAA features a tibial component of the TNK ankle (Kyocera, Kyoto, Japan) and an alumina ceramic artificial talus (Kyocera), designed using individualized CT data. The mean age at the time of surgery in the combined TAA and standard TAA groups was 71 years (. 61. to 82) and 75 years (62 to 82), respectively. The mean follow-up was 58 months (43 to 81) and 64 months (48 to 88), respectively. The outcome was assessed using the Japanese Society for Surgery of the Foot (JSSF) ankle-hindfoot scale, the Ankle Osteoarthritis Scale (AOS), and the Self-Administered Foot Evaluation Questionnaire (SAFE-Q). Results. The mean preoperative JSSF score of the combined TAA and standard TAA groups was 44 (. sd. 11) and 49 (. sd. 10), respectively. The mean postoperative JSSF scores were 89 (. sd. 6.1) and 72 (. sd. 15), respectively. The mean postoperative JSSF score of the combined TAA group was significantly higher (p = 0.0034). The mean preoperative AOS scores for pain and function in the combined TAA and standard TAA groups were 5.8 (. sd. 3.3) and 5.5 (. sd. 3.1), and 8.6 (. sd. 1.3), and 7.1 (. sd. 2.9), respectively. The mean postoperative AOS scores of pain and function were 2.5 (. sd. 2.5) and 2.2 (. sd. 1.9), and 2.5 (. sd. 3.3) and 3.4 (. sd. 2.9), respectively. There were no significant differences between the two groups in terms of postoperative AOS scores. The mean postoperative SAFE-Q scores were: for pain, 76 (. sd. 23) and 70 (. sd. 23); for physical function, 66 (. sd. 25) and 55 (. sd. 27); for social function, 73 (. sd. 35) and 62 (. sd. 34); for shoe-related, 73 (. sd. 19) and 65 (. sd. 26); and for general health, 78 (. sd. 28) and 67 (. sd. 29), respectively. There were no significant differences between the two groups in terms of postoperative SAFE-Q scores. Conclusion. Combined TAA resulted in better clinical results than standard TAA. Cite this article: Bone Joint J 2019;101-B:443–446

We present a retrospective series of 170 cemented titanium straight-stem femoral components combined with two types of femoral head: cobalt-chromium (CoCr) alloy (114 heads) and alumina ceramic (50 heads). Of the study group, 55 patients (55 stems) had died and six (six stems) were lost to follow-up. At a mean of 13.1 years (3 to 15.3) 26 stems had been revised for aseptic loosening. The mean follow-up time for stable stems was 15.1 years (12.1 to 16.6). Survival of the stem at 15 years was 75.4% (95% confidence interval (CI) 67.3 to 83.5) with aseptic failure (including radiological failure) as the end-point, irrespective of the nature of the head and the quality of the cement mantle. Survival of the stem at 15 years was 79.1% (95% CI 69.8 to 88.4) and 67.1% (95% CI 51.3 to 82.9) with the CoCr alloy and ceramic heads, respectively. The quality of the cement mantle was graded as a function of stem coverage: stems with complete tip coverage (type 1) had an 84.9% (95% CI 77.6 to 92.2) survival at 15 years, compared with those with a poor tip coverage (type 2) which had a survival of only 22.4% (95% CI 2.4 to 42.4). The poor quality of the cement mantle and the implantation of an alumina head substantially lowered the survival of the stem. In our opinion, further use of the cemented titanium alloy straight-stem femoral components used in our series is undesirable

We examined the behaviour of alumina ceramic heads in 156 cemented total hip arthroplasties, at a minimum follow-up of eight years. They were divided into three groups according to the size of the femoral head; 22, 26, and 28 mm. We measured polyethylene wear radiologically using a computer-aided technique. The linear wear rate of polyethylene sockets for the 28 mm heads was high (0.156 mm/year), whereas those for the 22 and 26 mm heads were relatively low (0.090 and 0.098 mm/year, respectively). Moreover, the surface roughness data of retrieved femoral heads clearly showed maintenance of an excellent surface finish of the current alumina. We conclude that the alumina ceramic femoral heads currently used are associated with a reduced rate of polyethylene wear

Surgeons remain concerned that ceramic hip prostheses may fail catastrophically if either the head or the liner is fractured. We report two patients, each with a ceramic-on-ceramic total hip replacement who sustained high-energy trauma sufficient to cause a displaced periprosthetic acetabular fracture in whom the ceramic bearings survived intact. Simultaneous fixation of the acetabular fracture, revision of the cementless acetabular prosthesis and exchange of the ceramic bearings were performed successfully in both patients. Improved methods of manufacture of new types of alumina ceramic with a smaller grain size, and lower porosity, have produced much stronger bearings. Whether patients should be advised to restrict high-impact activities in order to protect these modern ceramic bearings from fracture remains controversial

Despite extensive experience with prosthetic replacement for the reconstruction of limbs following juxta-articular resection of tumours, there are few reports of prosthetic replacement of the distal radius. We present two cases of massive bone defects of the distal radius in which alumina ceramic prosthetic replacements were used. We evaluated the patients more than ten years after the procedure. Both patients had degenerative changes to the wrist. This, however, was not associated with pain or decreased function, and both had returned to their previous occupation after surgery. When a patient has a massive defect of the distal radius, reconstruction using a ceramic prosthesis is a reasonable alternative to using autograft. This method of treatment results in little pain, a moderate range of movement and satisfactory function

The Norwegian Arthroplasty Register has shown that several designs of uncemented femoral stems give good or excellent survivorship. The overall findings for uncemented total hip replacement however, have been disappointing because of poor results with the use of metal-backed acetabular components. In this study, we exclusively investigated the medium-to long-term performance of primary uncemented metal-backed acetabular components. A total of 9113 primary uncemented acetabular components were implanted in 7937 patients between 1987 and 2007. These were included in a prospective, population-based observational study. All the implants were modular and metal-backed with ultra-high-molecular-weight polyethylene liners. The femoral heads were made of stainless steel, cobalt-chrome (CoCr) alloy or alumina ceramic. In all, seven different designs of acetabular component were evaluated by the Kaplan-Meier survivorship method and Cox regression analysis. Most acetabular components performed well up to seven years. When the endpoint was revision of the acetabular component because of aseptic loosening, the survival ranged between 87% and 100% at ten years. However, when the endpoint was revision for any reason, the survival estimates were 81% to 92% for the same implants at ten years. Aseptic loosening, wear, osteolysis and dislocation were the main reasons for the relatively poor overall performance of the acetabular components. Prostheses with alumina heads performed slightly better than those with stainless steel or CoCr alloy in subgroups. Whereas most acetabular components performed well at seven years, the survivorship declined with longer follow-up. Fixation was generally good. None of the metal-backed uncemented acetabular components with ultra-high-molecular-weight polyethylene liners in our study had satisfactory long-term results because of high rates of wear, osteolysis, aseptic loosening and dislocation

Aims

There are concerns regarding complications and longevity of total elbow arthroplasty (TEA) in young patients, and the few previous publications are mainly limited to reports on linked elbow devices. We investigated the clinical outcome of unlinked TEA for patients aged less than 50 years with rheumatoid arthritis (RA).

We prospectively assessed the efficacy of a ceramic-on-metal (CoM) hip bearing with uncemented acetabular and femoral components in which cobalt­–chrome acetabular liners and alumina ceramic heads were used. The cohort comprised 94 total hip replacements (THRs) in 83 patients (38 women and 45 men) with a mean age of 58 years (42 to 70). Minimum follow-up was two years. All patients had pre- and post-operative assessment using the Western Ontario and McMaster Universities osteoarthritis index (WOMAC), Oxford hip score and Short-Form 12 scores. All showed a statistically significant improvement from three months post-operatively onwards (all p < 0.001). After two years whole blood metal ion levels were measured and chromosomal analysis was performed. The levels of all metal ions were elevated except vanadium. Levels of chromium, cobalt, molybdenum and titanium were significantly higher in patients who underwent bilateral THR compared with those undergoing unilateral THR (p < 0.001). Chromosomal analysis demonstrated both structural and aneuploidy mutations. There were significantly more breaks and losses than in the normal population (p < 0.001). There was no significant difference in chromosomal aberration between those undergoing unilateral and bilateral procedures (all analyses p ≥ 0.62). The use of a CoM THR is effective clinically in the short-term, with no concerns, but the significance of high metal ion levels and chromosomal aberrations in the long-term remains unclear. Cite this article: Bone Joint J 2013;95-B:1040–44

At yearly intervals we compared the radiological wear characteristics of 81 alumina ceramic femoral heads with a well-matched group of 43 cobalt-chrome femoral heads. Using a computer-assisted measurement system we assessed two-dimensional penetration of the head into the polyethylene liner. We used linear regression analysis of temporal data of the penetration of the head to calculate the true rates of polyethylene wear for both groups. At a mean of seven years the true rate of wear of the ceramic group was slightly greater (0.09 mm/year, SD 0.07) than that of the cobalt-chrome group (0.07 mm/year, SD 0.04). Despite the numerous theoretical advantages of ceramic over cobalt-chrome femoral heads, the wear performance in vivo of these components was similar

We have compared the survival of two hydroxyapatite (HA)-coated cups, 1208 Atoll hemispheric and 2641 Tropic threaded, with cemented Charnley all-polyethylene cups (16 021) using the Cox regression model. The Tropic cup used in combination with an alumina ceramic femoral head, had good results, similar to those of the Charnley cup. When used in combination with a stainless-steel head, however, the risk of revision beyond four years was increased 3.4 times for the Tropic cup compared with the Charnley cup (p < 0.001). Over the same period, the Atoll cup had an increased risk of revision of 3.8 times when used with the alumina heads (p < 0.001) and an increased risk of 6.1 times when used with stainless-steel heads (p < 0.001). Revision because of wear and osteolysis was more common with both types of HA-coated cup than with the Charnley cup. The rate of revision of the Atoll cup because of aseptic loosening was also increased. We found that HA-coated cups did not perform better than the Charnley cup

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

The Morscher-Spotorno (MS-30) femoral stem is a stainless-steel, straight, three-dimensionally tapered, collarless implant for cemented fixation in total hip replacement. We report the results at ten years of a consecutive series of 124 total hip replacements in 121 patients with the matt-surfaced MS-30 stem and an alumina ceramic head of 28-mm diameter. All the stems were fixed with Palacos bone cement with gentamicin using a modern cementing technique. They were combined with an uncemented, press-fit cup. The mean period of observation was 10.2 years (8.3 to 12.1) and no patient was lost to follow-up. Twenty-seven patients (22%) died with the implant in situ. Nine could only be interviewed by telephone. We included 85 patients with 88 hips in the clinical and radiological follow-up examinations. None of the stems or cups had been revised. The Harris hip score was excellent or good in 97% (85 hips) and moderate in 3% (three hips). Radiologically, six hips (6.8%) had osteolysis adjacent to the stem, mostly in Gruen zone 7. Twenty (22.7%) showed one or more radiolucent lines. Twenty-two stems (25%) had subsided by 2 mm to 5 mm. In these cases two showed osteolysis (9.1%) with subsidence and four without (6.1%). Radiolucent lines were seen in seven with migration (31.8%) and in 13 without (19.7%). No infections and no acetabular osteolysis were observed. The clinical results were excellent with survivorship after ten years of 100% and only a slightly statistically non-significant higher rate of osteolysis and radiolucency in cases of subsidence

Aims

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged less than 50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component.

Aims

The aim of this study was to evaluate the suitability of the tapered cone stem in total hip arthroplasty (THA) in patients with excessive femoral anteversion and after femoral osteotomy.

Aims

The Exeter V40 cemented femoral stem was first introduced in 2000. The largest single-centre analysis of this implant to date was published in 2018 by Westerman et al. Excellent results were reported at a minimum of ten years for the first 540 cases performed at the designer centre in the Exeter NHS Trust, with stem survivorship of 96.8%. The aim of this current study is to report long-term outcomes and survivorship for the Exeter V40 stem in a non-designer centre.

Aims

To compare long-term survival of all-cemented and hybrid total hip arthroplasty (THA) using the Exeter Universal stem.

Ceramic bearings have several desirable properties, such as resistance to wear, hardness, and biocompatibility, that favour it as an articulating surface in hip arthroplasty. However, ceramic fracture remains a concern. We have reviewed the contemporary literature, addressing the factors that can influence the incidence of ceramic bearing surface fracture.

Cite this article: Bone Joint J 2019;101-B:897–901.

Aims

We conducted a prospective study of a delta ceramic total hip arthroplasty (THA) to determine the rate of ceramic fracture, to characterise post-operative noise, and to evaluate the mid-term results and survivorship.

The practice of removing a well-fixed cementless femoral component is associated with high morbidity. Ceramic bearing couples are low wearing and their use minimises the risk of subsequent further revision due to the production of wear debris. A total of 165 revision hip replacements were performed, in which a polyethylene-lined acetabular component was revised to a new acetabular component with a ceramic liner, while retaining the well-fixed femoral component. A titanium sleeve was placed over the used femoral trunnion, to which a ceramic head was added. There were 100 alumina and 65 Delta bearing couples inserted.

The mean Harris hip score improved significantly from 71.3 (9.0 to 100.0) pre-operatively to 91.0 (41.0 to 100.0) at a mean follow up of 4.8 years (2.1 to 12.5) (p < 0.001). No patients reported squeaking of the hip.

There were two fractures of the ceramic head, both in alumina bearings. No liners were seen to fracture. No fractures were observed in components made of Delta ceramic. At 8.3 years post-operatively the survival with any cause of failure as the endpoint was 96.6% (95% confidence interval (CI) 85.7 to 99.3) for the acetabular component and 94.0% (95% CI 82.1 to 98.4) for the femoral component.

The technique of revising the acetabular component in the presence of a well-fixed femoral component with a ceramic head placed on a titanium sleeve over the used trunnion is a useful adjunct in revision hip practice. The use of Delta ceramic is recommended.

Cite this article: Bone Joint J 2013;95-B:333–8.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

A moderator and panel of five experts led an interactive session in discussing five challenging and interesting patient case presentations involving surgery of the hip. The hip pathologies reviewed included failed open reduction internal fixation of subcapital femoral neck fracture, bilateral hip disease, evaluation of pain after metal-on-metal hip arthroplasty, avascular necrosis, aseptic loosening secondary to osteolysis and polyethylene wear, and management of ceramic femoral head fracture.

Despite its intrinsic ability to regenerate form and function after injury, bone tissue can be challenged by a multitude of pathological conditions. While innovative approaches have helped to unravel the cascades of bone healing, this knowledge has so far not improved the clinical outcomes of bone defect treatment. Recent findings have allowed us to gain in-depth knowledge about the physiological conditions and biological principles of bone regeneration. Now it is time to transfer the lessons learned from bone healing to the challenging scenarios in defects and employ innovative technologies to enable biomaterial-based strategies for bone defect healing. This review aims to provide an overview on endogenous cascades of bone material formation and how these are transferred to new perspectives in biomaterial-driven approaches in bone regeneration.

Cite this article: T. Winkler, F. A. Sass, G. N. Duda, K. Schmidt-Bleek. A review of biomaterials in bone defect healing, remaining shortcomings and future opportunities for bone tissue engineering: The unsolved challenge. Bone Joint Res 2018;7:232–243. DOI: 10.1302/2046-3758.73.BJR-2017-0270.R1.

A modular layered acetabular component (metal-polyethylene-ceramic) was developed in Japan for use in alumina ceramic-on-ceramic total hip replacement. Between May 1999 and July 2000, we performed 35 alumina ceramic-on-ceramic total hip replacements in 30 consecutive patients, using this layered component and evaluated the clinical and radiological results over a mean follow-up of 5.8 years (5 to 6.5). A total of six hips underwent revision, one for infection, two for dislocation with loosening of the acetabular component, two for alumina liner fractures and one for component dissociation with pelvic osteolysis. There were no fractures of the ceramic heads, and no loosening of the femoral or acetabular component in the unrevised hips was seen at final follow-up. Osteolysis was not observed in any of the unrevised hips. The survivorship analysis at six years after surgery was 83%. The layered acetabular component in our experience, has poor durability because of unexpected mechanical failures including alumina liner fracture and component dissociation.

Our aim in this prospective study was to compare the bone mineral density (BMD) around cementless acetabular and femoral components which were identical in geometry and had the same alumina modular femoral head, but differed in regard to the material of the acetabular liners (alumina ceramic or polyethylene) in 50 patients (100 hips) who had undergone bilateral simultaneous primary total hip replacement. Dual energy X-ray absorptiometry scans of the pelvis and proximal femur were obtained at one week, at one year, and annually thereafter during the five-year period of the study.

At the final follow-up, the mean BMD had increased significantly in each group in acetabular zone I of DeLee and Charnley (20% (15% to 26%), p = 0.003), but had decreased in acetabular zone II (24% (18% to 36%) in the alumina group and 25% (17% to 31%) in the polyethylene group, p = 0.001). There was an increase in the mean BMD in zone III of 2% (0.8% to 3.2%) in the alumina group and 1% (0.6% to 2.2%) in the polyethylene group (p = 0.315). There was a decrease in the mean BMD in the calcar region (femoral zone 7) of 15% (8% to 24%) in the alumina group and 14% (6% to 23%) in the polyethylene group (p < 0.001). The mean bone loss in femoral zone 1 of Gruen et al was 2% (1.1% to 3.1%) in the alumina group and 3% (1.3% to 4.3%) in the polyethylene group (p = 0.03), and in femoral zone 6, the mean bone loss was 15% (9% to 27%) in the alumina group and 14% (11% to 29%) in the polyethylene group compared with baseline values. There was an increase in the mean BMD on the final scans in femoral zones 2 (p = 0.04), 3 (p = 0.04), 4 (p = 0.12) and 5 (p = 0.049) in both groups.

There was thus no significant difference in the bone remodelling of the acetabulum and femur five years after total hip replacement in those two groups where the only difference was in the acetabular liner.

We compared a modular neck system with a non-modular system in a cementless anatomical total hip replacement (THR). Each group consisted of 74 hips with developmental hip dysplasia. Both groups had the same cementless acetabular component and the same articulation, which consisted of a conventional polyethylene liner and a 28 mm alumina head. The mean follow-up was 14.5 years (13 to 15), at which point there were significant differences in the mean total Harris hip score (modular/non-modular: 98.6 (64 to 100)/93.8 (68 to 100)), the mean range of abduction (32° (15° to 40°)/28 (0° to 40°)), use of a 10° elevated liner (31%/100%), the incidence of osteolysis (27%/79.7%) and the incidence of equal leg lengths (≥ 6 mm, 92%/61%). There was no disassociation or fracture of the modular neck.

The modular system reduces the need for an elevated liner, thereby reducing the incidence of osteolysis. It gives a better range of movement and allows the surgeon to make an accurate adjustment of leg length.

Fracture of a ceramic component in total hip replacement is a rare but potentially catastrophic complication. The incidence is likely to increase as the use of ceramics becomes more widespread. We describe such a case, which illustrates how inadequate initial management will lead to further morbidity and require additional surgery. We present the case as a warning that fracture of a ceramic component should be revised to another ceramic-on-ceramic articulation in order to minimise the risk of further catastrophic wear.

We report the clinical and radiological outcomes of a series of contemporary cementless ceramic-on-ceramic total hip replacements (THRs) at ten years in patients aged ≤ 55 years of age. Pre- and post-operative activity levels are described. A total of 120 consecutive ceramic cementless THRs were performed at a single centre in 110 patients from 1997 to 1999. The mean age of the patients at operation was 45 years (20 to 55). At ten years, four patients had died and six were lost to follow-up, comprising ten hips. The mean post-operative Harris hip score was 94.7 (55 to 100). Radiological analysis was undertaken in 90 available THRs of the surviving 106 hips at final review: all had evidence of stable bony ingrowth, with no cases of osteolysis. Wear was undetectable. There were four revisions. The survival for both components with revision for any cause as an endpoint was 96.5% (95% confidence interval 94.5 to 98.7). The mean modified University of California, Los Angeles activity level rose from a mean of 6.4 (4 to 10) pre-operatively to 9.0 (6 to 10) at the ten-year post-operative period.

Alumina ceramic-on-ceramic bearings in cementless primary THR in this series have resulted in good clinical and radiological outcomes with undetectable rates of wear and excellent function in the demanding younger patient group at ten years.

Cite this article: Bone Joint J 2013;95-B:1603–9.

This study reviewed the results of a cementless anatomical femoral component to give immediate post-operative stability, and with a narrow distal section in order not to contact the femoral cortex in the diaphysis, ensuring exclusively metaphyseal loading.

A total of 471 patients (601 hips) who had a total hip replacement between March 1995 and February 2002 were included in the study. There were 297 men and 174 women. The mean age at the time of operation was 52.7 years (28 to 63). Clinical and radiological evaluation were performed at each follow-up. Bone densitometry was carried out on all patients two weeks after operation and at the final follow-up examination. The mean follow-up was 8.8 years (5 to 12).

The mean pre-operative Harris hip score was 41 points (16 to 54), which improved to a mean of 96 (68 to 100) at the final follow-up. No patient complained of thigh pain at any stage. No acetabular or femoral osteolysis was observed and no hip required revision for aseptic loosening of either component. Deep infection occurred in two hips (0.3%) which required revision. One hip (0.2%) required revision of the acetabular component for recurrent dislocation. Bone mineral densitometry revealed a minimal bone loss in the proximal femur.

This cementless anatomical femoral component with metaphyseal loading but without distal fixation produced satisfactory fixation and encourages proximal femoral loading.

Objectives

Studies reporting specifically on squeaking in total hip arthroplasty have focused on cementless, and not on hybrid, fixation. We hypothesised that the cement mantle of the femur might have a damping effect on the sound transmitted through the metal stem. The objective of this study was to test the effect of cement on sound propagation along different stem designs and under different fixation conditions.

Aims

To determine the effect of a change in design of a cementless ceramic acetabular component in fixation and clinical outcome after total hip arthroplasty

This multicentre study analysed 12 alumina ceramic-on-ceramic components retrieved from squeaking total hip replacements after a mean of 23 months in situ (11 to 61). The rates and patterns of wear seen in these squeaking hips were compared with those seen in matched controls using retrieval data from 33 ‘silent’ hip replacements with similar ceramic bearings. All 12 bearings showed evidence characteristic of edge-loading wear. The median rate of volumetric wear was 3.4 mm³/year for the acetabular component, 2.9 mm³/year on the femoral heads and 6.3 mm³/year for head and insert combined. This was up to 45 times greater than that of previously reported silent ceramic-on-ceramic retrievals. The rate of wear seen in ceramic components revised for squeaking hips appears to be much greater than in that seen in retrievals from ‘silent’ hips.

We investigated factors that were thought to be associated with an increased incidence of squeaking of ceramic-on-ceramic total hip replacements. Between June 1997 and December 2008 the three senior authors implanted 2406 primary total hip replacements with a ceramic-on-ceramic bearing surface. The mean follow-up was 10.6 years. The diagnosis was primary osteoarthritis in each case, and no patient had undergone previous surgery to the hip. We identified 74 squeaking hips (73 patients) giving an incidence of 3.1% at a mean follow-up of 9.5 years (4.1 to 13.3).

Taller, heavier and younger patients were significantly more likely to have hips that squeaked. Squeaking hips had a significantly higher range of post-operative internal (p = 0.001) and external rotation (p = 0.003) compared with silent hips. Patients with squeaking hips had significantly higher activity levels (p = 0.009). A squeaking hip was not associated with a significant difference in patient satisfaction (p = 0.24) or Harris hip score (p = 0.34). Four implant position factors enabled good prediction of squeaking. These were high acetabular component inclination, high femoral offset, lateralisation of the hip centre and either high or low acetabular component anteversion.

This is the largest study to date to examine patient factors and implant position factors that predispose to squeaking of a ceramic-on-ceramic hip. The results suggest that factors which increase the mechanical forces across the hip joint and factors which increase the risk of neck-to-rim impingement, and therefore edge-loading, are those that predispose to squeaking.

Most published randomised controlled trials which compare the rates of wear of conventional and cross-linked (XL) polyethylene (PE) in total hip arthroplasty (THA) have described their use with a cementless acetabular component.

We conducted a prospective randomised study to assess the rates of penetration of two distinct types of PE in otherwise identical cemented all-PE acetabular components.

A total of 100 consecutive patients for THA were randomised to receive an acetabular component which had been either highly XL then remelted or moderately XL then annealed.

After a minimum of eight years follow-up, 38 hips in the XL group and 30 hips in the annealed group had complete data (mean follow-up of 9.1 years (7.6 to 10.7) and 8.7 years (7.2 to 10.2), respectively). In the XL group, the steady state rate of penetration from one year onwards was -0.0002 mm/year (sd 0.108): in the annealed group it was 0.1382 mm/year (sd 0.129) (Mann–Whitney U test, p < 0.001). No complication specific to either material was recorded.

These results show that the yearly linear rate of femoral head penetration can be significantly reduced by using a highly XLPE cemented acetabular component.

Cite this article: Bone Joint J 2015;97-B:1458–62.

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged <  50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component. This represents an update of previous reports of the same cohort at ten and 16 years, which were reported in 2004 and 2009, respectively. We describe the survival, radiological and functional outcomes at a mean follow-up of 21 years (17 to 25). Of the surviving 34 THAs, one underwent femoral revision for peri-prosthetic fracture after 21 years, and one patient (one hip) was lost to follow-up. Using aseptic loosening as the end-point, 12 hips (31.5%) needed acetabular revision but none needed femoral revision, demonstrating 100% survival (95% confidence interval 89 to 100).

In young patients with high demands, the Furlong HAC–coated femoral component gives excellent long-term results.

Cite this article: Bone Joint J 2015;97-B:749–54.

We have developed a CT-based navigation system using infrared light-emitting diode markers and an optical camera. We used this system to perform cementless total hip replacement using a ceramic-on-ceramic bearing couple in 53 patients (60 hips) between 1998 and 2001. We reviewed 52 patients (59 hips) at a mean of six years (5 to 8) postoperatively. The mid-term results of total hip replacement using navigation were compared with those of 91 patients (111 hips) who underwent this procedure using the same implants, during the same period, without navigation. There were no significant differences in age, gender, diagnosis, height, weight, body mass index, or pre-operative clinical score between the two groups. The operation time was significantly longer where navigation was used, but there was no significant difference in blood loss or navigation-related complications. With navigation, the acetabular components were placed within the safe zone defined by Lewinnek, while without, 31 of the 111 components were placed outside this zone. There was no significant difference in the Merle d’Aubigne and Postel hip score at the final follow-up. However, hips treated without navigation had a higher rate of dislocation. Revision was performed in two cases undertaken without navigation, one for aseptic acetabular loosening and one for fracture of a ceramic liner, both of which showed evidence of neck impingement on the liner. A further five cases undertaken without navigation showed erosion of the posterior aspect of the neck of the femoral component on the lateral radiographs. These seven impingement-related mechanical problems correlated with malorientation of the acetabular component. There were no such mechanical problems in the navigated group.

We conclude that CT-based navigation increased the precision of orientation of the acetabular component and control of limb length in total hip replacement, without navigation-related complications. It also reduced the rate of dislocation and mechanical problems related to impingement.

Large femoral heads have become popular in total hip replacement (THR) as a method of reducing the risk of dislocation. However, if large heads are used in ceramic-on-ceramic THR, the liner must be thinner, which may increase the risk of fracture. To compare the rates of ceramic fracture and dislocation between 28 mm and 32 mm ceramic heads, 120 hips in 109 patients (51 men and 58 women, mean age 49.2 years) were randomised to THR with either a 28 mm or a 32 mm ceramic articulation. A total of 57/60 hips assigned to the 28 mm group and 55/60 hips assigned to the 32 mm group were followed for at least five years. No ceramic component fractures occured in any patient in either group. There was one dislocation in the 32 mm group and none in the 28 mm group (p = 0.464). No hip had detectable wear, focal osteolysis or prosthetic loosening. In our small study the 32 mm ceramic articulation appeared to be safe in terms of ceramic liner fracture.

Cite this article: Bone Joint J 2014;96-B:1459–63.

Symptomatic hip osteonecrosis is a disabling condition with a poorly understood aetiology and pathogenesis. Numerous treatment options for hip osteonecrosis are described, which include non-operative management and joint preserving procedures, as well as total hip replacement (THR). Non-operative or joint preserving treatment may improve outcomes when an early diagnosis is made before the lesion has become too large or there is radiographic evidence of femoral head collapse. The presence of a crescent sign, femoral head flattening, and acetabular involvement indicate a more advanced-stage disease in which joint preserving options are less effective than THR. Since many patients present after disease progression, primary THR is often the only reliable treatment option available. Prior to the 1990s, outcomes of THR for osteonecrosis were poor. However, according to recent reports and systemic reviews, it is encouraging that with the introduction of newer ceramic and/or highly cross-linked polyethylene bearings as well as highly-porous fixation interfaces, THR appears to be a reliable option in the management of end-stage arthritis following hip osteonecrosis in this historically difficult to treat patient population.

Cite this article: Bone Joint J 2013;95-B, Supple A:46–50.

Aims

Ceramic-on-ceramic (CoC) bearings in total hip arthroplasty (THA) are commonly used, but concerns exist regarding ceramic fracture. This study aims to report the risk of revision for fracture of modern CoC bearings and identify factors that might influence this risk, using data from the National Joint Registry (NJR) for England, Wales, Northern Ireland and the Isle of Man.

We report on 397 consecutive revision total hip replacements in 371 patients with a mean clinical and radiological follow-up of 12.9 years (10 to 17.7). The mean age at surgery was 69 years (37 to 93). A total of 28 patients (8%) underwent further revision, including 16 (4%) femoral components. In all 223 patients (56%, 233 hips) died without further revision and 20 patients (5%, 20 hips) were lost to follow-up. Of the remaining patients, 209 (221 hips) were available for clinical assessment and 194 (205 hips) for radiological review at mean follow-up of 12.9 years (10 to 17.7).

The mean Harris Hip Score improved from 58.7 (11 to 92) points to 80.7 (21 to 100) (p <  0.001) and the mean Merle d’Aubigné and Postel hip scores at final follow-up were 4.9 (2 to 6), 4.5 (2 to 6) and 4.3 (2 to 6), respectively for pain, mobility and function. Radiographs showed no lucencies around 186 (90.7%) femoral stems with stable bony ingrowth seen in 199 stems (97%). The survival of the S-ROM femoral stem at 15 years with revision for any reason as the endpoint was 90.5% (95% confidence interval (CI) 85.7 to 93.8) and with revision for aseptic loosening as the endpoint 99.3% (95% CI 97.2 to 99.8).

We have shown excellent long-term survivorship and good clinical outcome of a cementless hydroxyapatite proximally-coated modular femoral stem in revision hip surgery.

Cite this article: Bone Joint J 2014;96-B:730–6.

In 2004 we described the ten-year prospective results of 38 total hip replacements using the Furlong hydroxyapatite-ceramic-coated femoral component in 35 patients < 50 years old. We have now reviewed the surviving 35 arthroplasties in 33 patients at a mean of 16 years (10.3 to 19.9). The mean age of the surviving patients at the time of operation was 41.3 years (26.0 to 49.0). Of these, eight have undergone revision of their acetabular component for aseptic loosening. None of the femoral components has had revision for aseptic loosening giving a survival rate of 100% at 16 years (95% confidence interval 89% to 100%).

The Furlong hydroxyapatite-ceramic-coated femoral component gives excellent long-term survival in young and active patients.

Hip implant retrieval analysis is the most important source of insight into the performance of new materials and designs of hip arthroplasties. Even the most rigorous in vitro testing will not accurately simulate the behavior of implant materials and new designs of prosthetic arthroplasties. Retrieval analysis has revealed such factors as the effects of gamma-in-air sterilisation of polyethylene, fatigue failure mechanisms of polymethylmethacrylate bone cement, fretting corrosion of Morse taper junctions, third body wear effects of both hard-on-hard and hard-on-soft bearing couples, and the effects of impingement of components on the full spectrum of bearing surfaces, none of which was predicted by pre-implantation in vitro testing of these materials and combinations. The temporal sequence of the retrieval process is approximately six years from first implantation through retrieval analysis, laboratory investigation, and publication of results, and thus, in addition to rigorous clinical evaluation, represents the true development and insight cycle for new designs and materials.