The purpose of this study was to undertake a meta-analysis to determine whether there is lower polyethylene wear and longer survival when using mobile-bearing implants in total knee replacement when compared with fixed-bearing implants. Of 975 papers identified, 34 trials were eligible for data extraction and meta-analysis comprising 4754 patients (6861 knees). We found no statistically significant differences between the two designs in terms of the incidence of radiolucent lines, osteolysis, aseptic loosening or survival. There is thus currently no evidence to suggest that the use of mobile-bearing designs reduce polyethylene wear and prolong survival after total knee replacement. Cite this article: Bone Joint J 2013;95-B:1057–63

Aims. The aim of this study was to determine whether there is a difference in the rate of wear between acetabular components positioned within and outside the ‘safe zones’ of anteversion and inclination angle. Patients and Methods. We reviewed 100 hips in 94 patients who had undergone primary total hip arthroplasty (THA) at least ten years previously. Patients all had the same type of acetabular component with a bearing couple which consisted of a 28 mm cobalt-chromium head on a highly crosslinked polyethylene (HXLPE) liner. A supine radiostereometric analysis (RSA) examination was carried out which acquired anteroposterior (AP) and lateral paired images. Acetabular component anteversion and inclination angles were measured as well as total femoral head penetration, which was divided by the length of implantation to determine the rate of polyethylene wear. Results. The mean anteversion angle was 19.4° (-15.2° to 48°, . sd. 11.4°), the mean inclination angle 43.4° (27.3° to 60.5°, . sd. 6.6°), and the mean wear rate 0.055 mm/year (. sd. 0.060). Exactly half of the hips were positioned inside the ‘safe zone’. There was no difference (median difference, 0.012 mm/year; p = 0.091) in the rate of wear between acetabular components located within or outside the ‘safe zone’. When compared to acetabular components located inside the ‘safe zone’, the wear rate was no different for acetabular components that only achieved the target anteversion angle (median difference, 0.012 mm/year; p = 0.138), target inclination angle (median difference, 0.013 mm/year; p = 0.354), or neither target (median difference, 0.012 mm/year; p = 0.322). Conclusion. Placing the acetabular component within or outside the ‘safe zone’ did not alter the wear rate of HXLPE at long-term follow-up to a level that risked osteolysis. HXLPE appears to be a forgiving bearing material in terms of articular surface wear, but care must still be taken to position the acetabular component correctly so that the implant is stable. Cite this article: Bone Joint J 2018;100-B:891-7

Aims

Wear of the polyethylene (PE) tibial insert of total knee arthroplasty (TKA) increases the risk of revision surgery with a significant cost burden on the healthcare system. This study quantifies wear performance of tibial inserts in a large and diverse series of retrieved TKAs to evaluate the effect of factors related to the patient, knee design, and bearing material on tibial insert wear performance.

Aims

Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE.

Objectives

The accuracy and precision of two new methods of model-based radiostereometric analysis (RSA) were hypothesised to be superior to a plain radiograph method in the assessment of polyethylene (PE) wear.

The Oxford Unicompartmental Knee replacement (UKR) was introduced as a design to reduce polyethylene wear. There has been one previous retrieval study involving this implant, which reported very low rates of wear in some specimens but abnormal patterns of wear in others. There has been no further investigation of these abnormal patterns. The bearings were retrieved from 47 patients who had received a medial Oxford UKR for anteromedial osteoarthritis of the knee. None had been studied previously. The mean time to revision was 8.4 years (. sd. 4.1), with 20 having been implanted for over ten years. The macroscopic pattern of polyethylene wear and the linear penetration were recorded for each bearing. The mean rate of linear penetration was 0.07 mm/year. The patterns of wear fell into three categories, each with a different rate of linear penetration; 1) no abnormal macroscopic wear and a normal articular surface, n = 16 (linear penetration rate = 0.01 mm/year); 2) abnormal macroscopic wear and normal articular surfaces with extra-articular impingement, n = 16 (linear penetration rate = 0.05 mm/year); 3) abnormal macroscopic wear and abnormal articular surfaces with intra-articular impingement +/− signs of non-congruous articulation, n = 15 (linear penetration rate = 0.12 mm/year). The differences in linear penetration rate were statistically significant (p < 0.001). These results show that very low rates of polyethylene wear are possible if the device functions normally. However, if the bearing displays suboptimal function (extra-articular, intra-articular impingement or incongruous articulation) the rates of wear increase significantly

We examined radiographic polyethylene wear in 233 cemented total hip arthroplasties (201 patients) with either a metal-backed or a non-metal-backed acetabular cup. All patients had identical cemented one-piece titanium femoral stems with a femoral head diameter of 28 mm. The mean linear wear rate was 0.11 mm/yr in metal-backed sockets and 0.08 mm/yr in non-metal-backed sockets (p = 0.0002). The mean volumetric wear rate was 66.2 mm3/yr in the metal-backed sockets and 48.2 mm3/yr in the polyethylene sockets (p = 0.0002). The addition of metal backing to a cemented acetabular cup therefore resulted in a 37% increase in mean polyethylene wear rates which may partially explain the higher failure rate of cemented metal-backed cups. Linear regression analysis also implicated increased follow-up time (log), gross acetabular migration, metal backing and male gender in increasing polyethylene wear. We advocate the use of an all-polyethylene cup in cemented total hip arthroplasty. The increased polyethylene wear must also cause concern about the wear rate of uncemented metal-backed acetabular sockets

Wear of polyethylene is associated with aseptic loosening of orthopaedic implants and has been observed in hip and knee prostheses and anatomical implants for the shoulder. The reversed shoulder prostheses have not been assessed as yet. We investigated the volumetric polyethylene wear of the reversed and anatomical Aequalis shoulder prostheses using a mathematical musculoskeletal model. Movement and joint stability were achieved by EMG-controlled activation of the muscles. A non-constant wear factor was considered. Simulated activities of daily living were estimated from in vivo recorded data. After one year of use, the volumetric wear was 8.4 mm. 3. for the anatomical prosthesis, but 44.6 mm. 3. for the reversed version. For the anatomical prosthesis the predictions for contact pressure and wear were consistent with biomechanical and clinical data. The abrasive wear of the polyethylene in reversed prostheses should not be underestimated, and further analysis, both experimental and clinical, is required

We examined the behaviour of alumina ceramic heads in 156 cemented total hip arthroplasties, at a minimum follow-up of eight years. They were divided into three groups according to the size of the femoral head; 22, 26, and 28 mm. We measured polyethylene wear radiologically using a computer-aided technique. The linear wear rate of polyethylene sockets for the 28 mm heads was high (0.156 mm/year), whereas those for the 22 and 26 mm heads were relatively low (0.090 and 0.098 mm/year, respectively). Moreover, the surface roughness data of retrieved femoral heads clearly showed maintenance of an excellent surface finish of the current alumina. We conclude that the alumina ceramic femoral heads currently used are associated with a reduced rate of polyethylene wear

Objectives. Bone void fillers are increasingly being used for dead space management in arthroplasty revision surgery. The aim of this study was to investigate the influence of calcium sulphate bone void filler (CS-BVF) on the damage and wear of total knee arthroplasty using experimental wear simulation. Methods. A total of 18 fixed-bearing U2 total knee arthroplasty system implants (United Orthopedic Corp., Hsinchu, Taiwan) were used. Implants challenged with CS-BVF were compared with new implants (negative controls) and those intentionally scratched with a diamond stylus (positive controls) representative of severe surface damage (n = 6 for each experimental group). Three million cycles (MC) of experimental simulation were carried out to simulate a walking gait cycle. Wear of the ultra-high-molecular-weight polyethylene (UHMWPE) tibial inserts was measured gravimetrically, and damage to articulating surfaces was assessed using profilometry. Results. There was no significant difference (p  >  0.05) between the wear rate of implants challenged with CS-BVF (3.3 mm. 3. /MC (95% confidence interval (CI) 1.8 to 4.8)) and the wear rate of those not challenged (2.8 mm. 3. /MC (95% CI 1.3 to 4.3)). However, scratching the cobalt-chrome (CoCr) significantly (p < 0.001) increased the wear rate (20.6 mm. 3. /MC (95% CI 15.5 to 25.7)). The mean surface roughness of implants challenged with CS-BVF was equivalent to negative controls both after damage simulation (p = 0.98) and at the conclusion of the study (p = 0.28). Conclusion. When used close to articulating surfaces, a low-hardness, high-purity CS-BVF had no influence on wear. When trapped between the articulating surfaces of a total knee arthroplasty, CS-BVF did not scratch the surface of CoCr femoral components, nor did it increase the wear of UHMWPE tibial inserts compared with undamaged negative controls. Cite this article: R. M. Cowie, S. S. Aiken, J. J. Cooper, L. M. Jennings. The influence of a calcium sulphate bone void filler on the third-body damage and polyethylene wear of total knee arthroplasty. Bone Joint Res 2019;8:65–72. DOI: 10.1302/2046-3758.82.BJR-2018-0146.R1

We made a clinical study of polyethylene wear in 240 hips of 187 patients having primary total hip arthroplasties from 1989 to 1990, using uncemented Osteonics components, with a head size of 26 mm. We excluded cups with anteversion of over 20° and measured linear wear by a new method using a digitiser and special software of our design. Follow-up was from two to five years (mean 4.3). The mean age at operation was 50.3 years, with more men than women (1.4:1). The mean linear wear per year was 0.15 mm; this did not increase with the longevity of the prosthesis (p = 0.54). In 59 hips showing evidence of osteolysis, the mean linear wear rate was significantly higher at 0.23 mm/year (p < 0.001). The mean linear wear rate also correlated significantly with age at the time of operation (p = 0.008), but we found no significant correlations with body-weight, gender, aetiology of the disease, thickness of polyethylene, or cup position. Our new method of measurement is time-saving and reproducible. The results confirm the greater rate of linear wear of polyethylene in patients showing osteolysis and in those who are younger

We measured polyethylene wear in 231 porous-coated uncemented acetabular cups. We divided the hips into two groups according to the fixation of the femoral component, by cementing (n = 97) or press-fit (n = 134). Follow-up was from three to five years. The patients in two sub-groups were matched for weight, diagnosis, sex, age and length of follow-up. The linear wear rate of cups articulated with uncemented femoral components (0.22 mm/year) was significantly higher than the wear rate (0.15 mm/year) of cups articulated within cemented femoral components (p < 0.05). These results can be compared with previously reported wear rates of 0.08 mm/year for cemented all-polyethylene cups and 0.11 mm/year for cemented metal-backed cups. The higher wear rates of uncemented arthroplasties could jeopardize the long-term results of this type of hip replacement

We have studied the influence of weight-bearing on the measurement of wear of the polyethylene acetabular component in total hip arthroplasty using two techniques. The measured vertical wear was significantly greater when radiographs were taken weight-bearing rather than with the patient supine (p = 0.001, method 1; p = 0.007, method 2). Calculations of rates of linear wear of the acetabular component were significantly underestimated (p < 0.05) when radiographs were taken supine. There are two reasons for this. First, a change in pelvic orientation when bearing weight ensures that the thinnest polyethylene is brought into relief, and secondly, the head of the femoral component assumes the position of maximal displacement along its wear path. Interpretation of previous studies on both linear and volumetric polyethylene wear in total hip arthroplasty should be reassessed in the light of these findings

The Oxford unicompartmental knee replacement (UKR) was designed to minimise wear utilising a fully-congruent, mobile, polyethylene bearing. Wear of polyethylene is a significant cause of revision surgery in UKR in the first decade, and the incidence increases in the second decade. Our study used model-based radiostereometric analysis to measure the combined wear of the upper and lower bearing surfaces in 13 medial-compartment Oxford UKRs at a mean of 20.9 years (17.2 to 25.9) post-operatively. The mean linear penetration of the polyethylene bearing was 1.04 mm (0.307 to 2.15), with a mean annual wear rate of 0.045 mm/year (0.016 to 0.099). The annual wear rate of the phase-2 bearings (mean 0.022 mm/year) was significantly less (p = 0.01) than that of phase-1 bearings (mean 0.07 mm/year). The linear wear rate of the Oxford UKR remains very low into the third decade. We believe that phase-2 bearings had lower wear rates than phase-1 implants because of the improved bearing design and surgical technique which decreased the incidence of impingement. We conclude that the design of the Oxford UKR gives low rates of wear in the long term

Aims. Vitamin E-diffused, highly crosslinked polyethylene (VEPE) and porous titanium-coated (PTC) shells were introduced in total hip arthroplasty (THA) to reduce the risk of aseptic loosening. The purpose of this study was: 1) to compare the wear properties of VEPE to moderately crosslinked polyethylene; 2) to assess the stability of PTC shells; and 3) to report their clinical outcomes at seven years. Patients and Methods. A total of 89 patients were enrolled into a prospective study. All patients received a PTC shell and were randomized to receive a VEPE liner (n = 44) or a moderately crosslinked polyethylene (ModXLPE) liner (n = 45). Radiostereometric analysis (RSA) was used to measure polyethylene wear and component migration. Differences in wear were assessed while adjusting for body mass index, activity level, acetabular inclination, anteversion, and head size. Plain radiographs were assessed for radiolucency and patient-reported outcome measures (PROMs) were administered at each follow-up. Results. In total, 73 patients (82%) completed the seven-year visit. Mean seven-year linear proximal penetration was -0.07 mm (. sd. 0.16) and 0.00 mm (. sd. 0.22) for the VEPE and ModXLPE cohorts, respectively (p = 0.116). PROMs (p = 0.310 to 0.807) and radiolucency incidence (p = 0.330) were not different between the polyethylene cohorts. The mean proximal shell migration rate was 0.04 mm per year (. sd. 0.09). At seven years, patients with radiolucency (34%) demonstrated greater migration (mean difference: 0.6 mm (. sd. 0.2); p < 0.001). PROMs were lower for patients with radiolucency and greater proximal migration (p = 0.009 to p = 0.045). No implants were revised for aseptic loosening. Conclusion. This is the first randomized controlled trial to report seven-year RSA results for VEPE. All wear rates were below the previously reported osteolysis threshold (0.1 mm per year). PTC shells demonstrated acceptable primary stability through seven years, as indicated by low migration and lack of aseptic loosening. However, patients with acetabular radiolucency were associated with higher shell migration and lower PROM scores. Cite this article: Bone Joint J 2019;101-B:760–767

Aims

Micromotion of the polyethylene (PE) inlay may contribute to backside PE wear in addition to articulate wear of total knee arthroplasty (TKA). Using radiostereometric analysis (RSA) with tantalum beads in the PE inlay, we evaluated PE micromotion and its relationship to PE wear.

We have followed up for a period of seven to nine years 100 consecutive arthroplasties of the hip in which an entirely HA-coated implant had been used. The clinical results were excellent and bony incorporation was extensive in all components. No stem became loose or subsided but five cups were revised because of loosening after 3.8 to 5.5 years, having functioned painlessly and shown radiological ingrowth. Revision procedures because of excessive polyethylene wear have been performed on 18 hips and are planned for six more. Two eroded metal backings with worn-through polyethylene were exchanged; six hips showed metallosis without polyethylene wear-through. There were two cases of granulomatous cysts in the groin and 66 hips had osteolysis located periarticularly, in the greater trochanter or in the acetabulum

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

Aims. Isolated acetabular liner exchange with a highly crosslinked polyethylene (HXLPE) component is an option to address polyethylene wear and osteolysis following total hip arthroplasty (THA) in the presence of a well-fixed acetabular shell. The liner can be fixed either with the original locking mechanism or by being cemented within the acetabular component. Whether the method used for fixation of the HXLPE liner has any bearing on the long-term outcomes is still unclear. Methods. Data were retrieved for all patients who underwent isolated acetabular component liner exchange surgery with a HXLPE component in our institute between August 2000 and January 2015. Patients were classified according to the fixation method used (original locking mechanism (n = 36) or cemented (n = 50)). Survival and revision rates were compared. A total of 86 revisions were performed and the mean duration of follow-up was 13 years. Results. A total of 20 patients (23.3%) had complications, with dislocation alone being the most common (8.1%; 7/86). Ten patients (11.6%) required re-revision surgery. Cementing the HXLPE liner (8.0%; 4/50) had a higher incidence of re-revision due to acetabular component liner-related complications than using the original locking mechanism (0%; 0/36; p = 0.082). Fixation using the original locking mechanism was associated with re-revision due to acetabular component loosening (8.3%; 3/36), compared to cementing (0%; 0/50; p = 0.038). Overall estimated mean survival was 19.2 years. There was no significant difference in the re-revision rate between the original locking mechanism (11.1%; 4/36) and cementing (12.0%; 6/50; p = 0.899). Using Kaplan-Meier survival analysis, the revision-free survival of HXLPE fixed with the original locking mechanism and cementing was 94.1% and 93.2%, respectively, at ten years, and 84.7% and 81.3%, respectively, at 20 years (p = 0.840). Conclusion. The re-revision rate and the revision-free survival following acetabular component liner exchange revision surgery using the HXLPE liner were not influenced by the fixation technique used. Both techniques were associated with good survival at a mean follow-up of 13 years. Careful patient selection is necessary for isolated acetabular component liner exchange revision surgery in order to achieve the best outcomes. Cite this article: Bone Joint J 2024;106-B(5 Supple B):59–65

We examined 86 polyethylene inserts, retrieved from total and unicompartmental knee prostheses after an average of 39.5 months in situ, grading them from 0 to 3 for seven modes of polyethylene degradation. Severe wear, with delamination or deformation, was observed in 51% of the implants, and was associated with time in situ, lack of congruency, thin polyethylene, third-body wear debris, and heat-pressed polyethylene. Significant under-surface cold flow was identified in some areas of unsupported polyethylene, and was associated with delamination in the load-bearing areas of thin inserts above screw holes in the underlying metal tray. We recommend the use of thicker polyethylene inserts, particularly in young, active patients and in designs with screw holes in the tibial baseplate. Thin polyethylene inserts which are at risk for accelerated wear and premature failure should be monitored radiographically at annual intervals

Isolated wear of the polyethylene tibial component led to failure in five of a series of 108 uncemented porous-coated knee replacements. The clinical features included pain, effusion and instability with progressive varus deformity. In all cases there was extensive wear on the medial side of the polyethylene surface of the prosthesis. The mechanism of such wear is complex, being due in part to the unconstrained nature of the joint and the incongruity of its surfaces. Other design characteristics may have contributed.

Aims. The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). Methods. We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up. Results. The mean follow-up period was 19.1 years (SD 0.6; 17.3 to 20.1). The 19-year overall survival rate with the end point of all-cause revision was 97.0% (95% confidence interval (CI) 91 to 100). The mean JOA score improved from 43.2 (SD 10.6; 30 to 76) before surgery to 90.2 (SD 6.4; 76 to 98) at the final follow-up (p < 0.001). There was no osteolysis or loosening of the acetabular or femoral components. The overall steady-state wear rate was 0.013 mm/year (SD 0.012). There was no hip with a steady-state wear rate of > 0.1 mm/year. There was no significant difference in wear rates for each period. We found no significant correlation between the wear rate and age, body weight, BMI, or cup inclination. Conclusion. First-generation annealed HXLPE shows excellent wear resistance and no acceleration of wear for approximately 20 years, with low all-cause revision rates. Cite this article: Bone Joint J 2022;104-B(2):200–205

Nanometre-sized particles of ultra-high molecular weight polyethylene have been identified in the lubricants retrieved from hip simulators. Tissue samples were taken from seven failed Charnley total hip replacements, digested using strong alkali and analysed using high-resolution field emission gun-scanning electron microscopy to determine whether nanometre-sized particles of polyethylene debris were generated in vivo. A randomised method of analysis was used to quantify and characterise all the polyethylene particles isolated.

We isolated nanometre-sized particles from the retrieved tissue samples. The smallest identified was 30 nm and the majority were in the 0.1 μm to 0.99 μm size range. Particles in the 1.0 μm to 9.99 μm size range represented the highest proportion of the wear volume of the tissue samples, with 35% to 98% of the total wear volume comprised of particles of this size. The number of nanometre-sized particles isolated from the tissues accounted for only a small proportion of the total wear volume. Further work is required to assess the biological response to nanometre-sized polyethylene particles.

Laboratory wear testing of ultra high molecular weight polyethylene from 12 Charnley acetabular cups, removed after periods of up to 17.5 years showed that the large patient-to-patient variations in clinical penetration rate cannot be explained by batch-to-batch variation in the wear resistance of the material. Nor was there any evidence of a time-dependent degradation in wear resistance of the material.

We studied wear in the ultra-high-molecular-weight polyethylene offset bore socket in 54 hips which had had Charnley low-friction arthroplasty. At an average follow-up of 8.1 years, the mean penetration rate was 0.04 mm per year. Correlation between the depth of socket penetration and the incidence of socket migration was confirmed, but socket migration occurred with lower penetration than had been previously reported.

We have studied 27 tibial prostheses retrieved from knee replacements after 1 to 9 years. In 22 the femoral components were of cobalt-chrome, in five polyacetal. The design of the components gave a nominal contact area of 320 mm2 on each condyle. The tibial component was of high-density polyethylene (HDP) at least 6 mm thick, and not heat-treated. In the metal/HDP prostheses the average wear rate was 0.025 mm/year. The relative wear on the medial and lateral sides was related to the leg axis. None of the retrieved prostheses showed any severe disruption of their surface. The polyacetal/HDP prostheses showed similar wear with a statistically insignificant trend towards slower penetration. We conclude that the rate of wear of HDP in a conforming tibiofemoral bearing with a fixed tibial component at least 6 mm thick and not heat-treated is slow enough to be safe in clinical practice.

We selected randomly a consecutive series of 162 patients requiring hip replacement to receive either a cementless, hemispherical, modular, titanium acetabular cup or a cemented, all-polyethylene cup. These replacements were performed by two surgeons in four general hospitals. The same surgical technique was used and a 26 mm metal-head femoral component was used in every case.

After exclusions, 115 hips were studied for differences in rates of wear and osteolysis. The mean clinical follow-up was eight years and the mean radiological follow-up, 6.5 years. The cementless cups wore at a mean rate of 0.15 mm per year and the cemented cups at 0.07 mm per year. This difference was significant (p < 0.0001).

Our findings in this mid-term study suggest that cementless cups wear more than cemented cups.

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured.

The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm³/year for the 32 mm head, which was significantly higher than the 41.5 mm³/year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

We recovered 23 meniscal bearings from 18 failed bicompartmental Oxford knee prostheses. They had been implanted for one to nine years. The minimum thickness of the retrieved bearings was measured and compared with the thickness of 25 unused bearings. The mean penetration rate, calculated by two methods, was either 0.043 or 0.026 mm per annum. This compares with 0.19 mm per annum reported for the Charnley hip. The use of a fully congruous meniscal bearing prosthesis can reduce wear in knee arthroplasty to a very low rate.

Aims. This paper describes the methodology, validation and reliability of a new computer-assisted method which uses models of the patient’s bones and the components to measure their migration and polyethylene wear from radiographs after total hip arthroplasty (THA). Materials and Methods. Models of the patient’s acetabular and femoral component obtained from the manufacturer and models of the patient’s pelvis and femur built from a single computed tomography (CT) scan, are used by a computer program to measure the migration of the components and the penetration of the femoral head from anteroposterior and lateral radiographs taken at follow-up visits. The program simulates the radiographic setup and matches the position and orientation of the models to outlines of the pelvis, the acetabular and femoral component, and femur on radiographs. Changes in position and orientation reflect the migration of the components and the penetration of the femoral head. Validation was performed using radiographs of phantoms simulating known migration and penetration, and the clinical feasibility of measuring migration was assessed in two patients. Results. Migration of the acetabular and femoral components can be measured with limits of agreement (LOA) of 0.37 mm and 0.33 mm, respectively. Penetration of the femoral head can be measured with LOA of 0.161 mm. Conclusion. The migration of components and polyethylene wear can be measured without needing specialised radiographs. Accurate measurement may allow earlier prediction of failure after THA. Cite this article: Bone Joint J 2017;99-B:1290–7

Despite many claims of good wear properties following total knee replacement (TKR) with an oxidised zirconium (OxZr) femoral component, there are conflicting clinical results. We hypothesised that there would be no difference in either the mid-term clinical and radiological outcomes or the characteristics of the polyethylene wear particles (weight, size and shape) in patients using an OxZr or cobalt-chrome (CoCr) femoral component. In all 331 patients underwent bilateral TKR, receiving an OxZr femoral component in one knee and a CoCr femoral component in the other. The mean follow-up was 7.5 years (6 to 8). Following aspiration, polyethylene wear particles were analysed using thermogravimetric methods and scanning electron microscopy. At the most recent follow-up, the mean Knee Society score, Western Ontario and McMaster Universities Osteoarthritis Index score, range of movement and satisfaction score were not significantly different in the two groups. The mean weight, size, aspect ratio and roundness of the aspirated wear particles were similar for each femoral component. Survivorship of the femoral, tibial and patellar components was 100% in both groups. In the absence of evidence of an advantage in the medium term we cannot justify the additional expense of an OxZr femoral component.

Aims

The aim of this study was to establish the results of isolated exchange of the tibial polyethylene insert in revision total knee arthroplasty (RTKA) in patients with well-fixed femoral or tibial components. We report on a series of RTKAs where only the polyethylene was replaced, and the patients were followed for a mean of 13.2 years (10.0 to 19.1).

Aims

There is insufficient evidence to recommend the use of alternative polyethylene bearings in modular, fixed-bearing total knee arthroplasty (TKA). The purpose of this study was to compare standard polyethylene (SP) and highly crosslinked polyethylene (XLP) tibial liners in posterior-stabilized TKA, with osteolysis as the primary outcome and clinical results and the rate of re-operation as the secondary outcomes.

Aims

We previously reported the long-term results of the cementless Duraloc-Profile total hip arthroplasty (THA) system in a 12- to 15-year follow-up study. In this paper, we provide an update on the clinical and radiological results of a previously reported cohort of patients at 23 to 26 years´ follow-up.

Aims

The primary aim of this study was to compare the wear properties of vitamin E-diffused, highly crosslinked polyethylene (VEPE) and one formulation of moderately crosslinked and mechanically annealed ultra-high molecular weight polyethylene (ModXLPE) in patients five years after primary total hip arthroplasty (THA). The secondary aim was to assess the clinical results of patients treated with VEPE by evaluating patient-reported outcome measures (PROMs), radiological evidence of fixation, and the incidence of mechanical failure.

We evaluated the outcome of 41 consecutive Charnley low-friction arthroplasties (LFAs) performed by a single surgeon in 28 patients aged ≤ 35 years at operation between 23 and 36 years previously. There were 20 women and eight men with a mean age of 32 years (23 to 35) at surgery. Two patients (three hips) were lost to follow-up at 12 and 17 years post-operatively, respectively, and one patient (one hip) died at 13 years post-operatively. These patients were excluded from the final evaluation. The survival rate of the acetabular components was 92.7% (95% confidence interval (CI) 88.7 to 96.7) at ten years, 67.1% (95% CI 59.75 to 74.45) at 20 years and 53.2% (95% CI 45.3 to 61.1) at 25 years. For the femoral component the survival was 95.1% (95% CI 91.8 to 98.5) at ten years, 77.1% (95% CI 73.9 to 80.3) at 20 years and 68.2% (95% CI 60.7 to 75.8) at 25 years. The results indicate that the Charnley LFA remains a reasonable choice in the treatment of young patients and can serve for comparison with newer techniques and implants.

Cite this article: Bone Joint J 2013;95-B:1052–6.

Introduction. Wear of polyethylene inserts plays an important role in failure of total knee replacement and can be monitored in vivo by measuring the minimum joint space width in anteroposterior radiographs. The objective of this retrospective cross-sectional study was to compare the accuracy and precision of a new model-based method with the conventional method by analysing the difference between the minimum joint space width measurements and the actual thickness of retrieved polyethylene tibial inserts. . Method. Before revision, the minimum joint space width values and their locations on the insert were measured in 15 fully weight-bearing radiographs. These measurements were compared with the actual minimum thickness values and locations of the retrieved tibial inserts after revision. . Results. The mean error in the model-based minimum joint space width measurement was significantly smaller than the conventional method for medial condyles (0.50 vs 0.94 mm, p < 0.01) and for lateral condyles (0.06 vs 0.34 mm, p = 0.02). The precision (standard deviation of the error) of the methods was similar (0.84 vs 0.79 mm medially and both 0.46 mm laterally). The distance between the true minimum joint space width locations and the locations from the model-based measurements was less than 10 mm in the medial direction in 12 cases and less in the lateral direction in 13 cases. Conclusion. The model-based minimum joint space width measurement method is more accurate than the conventional measurement with the same precision. Cite this article: Bone Joint Res 2014;3:289–96

Aims. Vitamin E-infused highly cross-linked polyethylene (E1) has recently been introduced in total knee arthroplasty (TKA). An in vitro wear simulator study showed that E1 reduced polyethylene wear. However there is no published information regarding in vivo wear. Previous reports suggest that newly introduced materials which reduce in vitro polyethylene wear do not necessarily reduce in vivo polyethylene wear. To assist in the evaluation of the newly introduced material before widespread use, we established an in vivo polyethylene wear particle analysis for TKA. The aim of this study was to compare in vivo polyethylene wear particle generation between E1 and conventional polyethylene (ArCom) in TKA. Methods. A total of 34 knees undergoing TKA (17 each with ArCom or E1) were investigated. Except for the polyethylene insert material, the prostheses used for both groups were identical. Synovial fluid was obtained at a mean of 3.4 years (SD 1.3) postoperatively. The in vivo polyethylene wear particles were isolated from the synovial fluid using a previously validated method and examined by scanning electron microscopy. Results. The total number of polyethylene wear particles obtained from the knees with E1 (mean 6.9, SD 4.0 × 10. 7. counts/knee) was greater than that obtained from those with ArCom (mean 2.2, SD 2.6 × 10. 7. counts/knee) (p = 0.001). The particle size (equivalent circle of diameter) from the knees with E1 was smaller (mean 0.5 μm, SD 0.1) than that of knees with ArCom (mean 1.5, SD 0.3 μm) (p = 0.001). The aspect ratio of particles from the knees with E1 (mean 1.3, SD 0.1) was smaller than that with ArCom (mean 1.4, SD 0.1) (p < 0.001 ). Conclusion. This is the first report of in vivo wear particle analysis of E1. E1 polyethylene did not reduce the number of in vivo polyethylene wear particles compared with ArCom in early clinical stage. Further careful follow-up of newly introduced E1 for TKA should be carried out. Cite this article: Bone Joint J 2020;102-B(11):1527–1534

Aims

We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty.

Aims. Vitamin E-infused highly crosslinked polyethylene (VEPE) has been introduced into total hip arthroplasty (THA) with the aim of further improving the wear characteristics of moderately and highly crosslinked polyethylenes (ModXLPE and HXLPE). There are few studies analyzing the outcomes of vitamin E-infused components in cemented arthroplasty, though early acetabular component migration has been reported. The aim of this study was to measure five-year polyethylene wear and acetabular component stability of a cemented VEPE acetabular component compared with a ModXLPE cemented acetabular component. Methods. In a prospective randomized controlled trial (RCT), we assessed polyethylene wear and acetabular component stability (primary outcome) with radiostereometric analysis (RSA) in 68 patients with reverse hybrid THA at five years follow-up. Patients were randomized to either a VEPE or a ModXLPE cemented acetabular component. Results. Mean polyethylene wear in the proximal direction was 0.17 mm (SD 0.15) for the VEPE group and 0.20 mm (SD 0.09) for the ModXLPE group (p = 0.005) at five years. Annual proximal wear rates were 0.03 mm/year (VEPE) and 0.04 mm/year (ModXLPE). Total 3D wear was 0.21 mm (SD 0.26) and 0.23 mm (SD 0.10) for the VEPE and ModXLPE groups, respectively (p = 0.009). Total 3D cup translation was 0.72 mm (SD 0.70) (VEPE) and 0.50 mm (SD 0.44) (ModXLPE) (p = 0.409). Conclusion. At five years, there was less polyethylene wear in the VEPE group than in the ModXLPE group. Both VEPE and ModXLPE cemented components showed low annual wear rates. Component stability was similar in the two groups and remained constant up to five years. Whether these results will equate to a lower long-term revision rate is still unknown. Cite this article: Bone Joint J 2020;102-B(12):1646–1653

Aims. Highly cross-linked polyethylene (HXLPE) has greatly improved the durability of total hip arthroplasty (THA) in young patients because of its improved wear characteristics. Few studies have followed this population into the second decade, and therefore the purpose of this investigation was to evaluate the clinical outcome for THA patients 50 years of age and younger at a minimum of 15 years postoperatively. The second purpose was to evaluate the radiological findings secondary to wear or mechanical failure of the implant. Methods. Between October 1999 and December 2005, 105 THAs were performed in 95 patients (53 female, 42 male) aged 50 years and younger (mean 42 years (20 to 50)). There were 87 patients (96 hips) that were followed for a minimum of 15 years (mean 17.3 years (15 to 21)) for analysis. Posterior approach was used with cementless fixation with a median head size of 28 mm. HXLPE was the acetabular bearing for all hips. Radiographs were evaluated for polyethylene wear, radiolucent lines, and osteolysis. Results. Clinical outcomes showed significant improvement of mean Harris Hip Scores from 52.8 (SD 13.5) preoperatively to 94.8 (SD 7.6) postoperatively. One hip was revised for recurrent instability, and there were no infections. No hips were revised for mechanical loosening or osteolysis. Mean polyethylene linear wear was 0.04 mm/year and volumetric wear was 6.22 mm. 3. /year, with no significant differences between head size or material. Osteolysis was not present in any of the hips. Conclusion. The use of HXLPE in THA for patients aged 50 years and younger has performed exceptionally well without evidence of significant wear causing mechanical loosening or necessitating revision. The radiolucent lines of the acetabular component must be followed to determine the prognostic significance. This investigation represents the longest clinical follow-up of a large, consecutive cohort of patients aged 50 years or younger with THA using HXLPE. This long-term analysis found negligible polyethylene wear, no incidence of aseptic loosening, and excellent clinical outcomes at and beyond 15 years of follow-up. Cite this article: Bone Joint J 2021;103-B(7 Supple B):78–83

Aims. This study aimed to determine outcomes of isolated tibial insert exchange (ITIE) during revision total knee arthroplasty (TKA). Methods. From 1985 to 2016, 270 ITIEs were performed at one institution for instability (55%, n = 148), polyethylene wear (39%, n = 105), insert fracture/dissociation (5%, n = 14), or stiffness (1%, n = 3). Patients with component loosening, implant malposition, infection, and extensor mechanism problems were excluded. Results. Survivorship free of any re-revision was 68% at ten years. For the indication of insert wear, survivorship free of any re-revision at ten years was 74%. Re-revisions were more frequent for index diagnoses other than wear (hazard ratio (HR) 1.9; p = 0.013), with ten-year survivorships of 69% for instability and 37% for insert fracture/dissociation. Following ITIE for wear, the most common reason for re-revision was aseptic loosening (33%, n = 7). For other indications, the most common reason for re-revision was recurrence of the original diagnosis. Mean Knee Society Scores improved from 54 (0 to 94) preoperatively to 77 (38 to 94) at ten years. Conclusion. After ITIE, the risk and reasons for re-revision correlated with preoperative indications. The best results were for polyethylene wear. For other diagnoses, the re-revision rate was higher and the failure mode was most commonly recurrence of the original indication for the revision TKA. Cite this article: Bone Joint J 2021;103-B(6):1103–1110

Aims. The purpose of this study was to assess mid-term survivorship following primary total knee arthroplasty (TKA) with Optetrak Logic components and identify the most common revision indications at a single institution. Methods. We identified a retrospective cohort of 7,941 Optetrak primary TKAs performed from January 2010 to December 2018. We reviewed the intraoperative findings of 369 TKAs that required revision TKA from January 2010 to December 2021 and the details of the revision implants used. Kaplan-Meier analysis was used to determine survivorship. Cox regression analysis was used to examine the impact of patient variables and year of implantation on survival time. Results. The estimated survivorship free of all-cause revision was 98% (95% confidence interval (CI) 97% to 98%), 95% (95% CI 95% to 96%), and 86% (95% CI 83% to 88%) at two, five, and ten years, respectively. In 209/369 revisions there was a consistent constellation of findings with varying severity that included polyethylene wear and associated synovitis, osteolysis, and component loosening. This failure mode, which we refer to as aseptic mechanical failure, was the most common revision indication. The mean time from primary TKA to revision for aseptic mechanical failure was five years (5 months to 11 years). Conclusion. In this series of nearly 8,000 primary TKAs performed with a specific implant, we identified a lower-than-expected mid-term survivorship and a high number of revisions with a unique presentation. This study, along with the recent recall of the implant, confirms the need for frequent monitoring of patients with Optetrak TKAs given the incidence of polyethylene failure, osteolysis, and component loosening. Cite this article: Bone Joint J 2023;105-B(3):277–283

Objectives. Unicompartmental knee arthroplasty (UKA) is an alternative to total knee arthroplasty with isolated medial or lateral compartment osteoarthritis. However, polyethylene wear can significantly reduce the lifespan of UKA. Different bearing designs and materials for UKA have been developed to change the rate of polyethylene wear. Therefore, the objective of this study is to investigate the effect of insert conformity and material on the predicted wear in mobile-bearing UKA using a previously developed computational wear method. Methods. Two different designs were tested with the same femoral component under identical kinematic input: anatomy mimetic design (AMD) and conforming design inserts with different conformity levels. The insert materials were standard or crosslinked ultra-high-molecular-weight polyethylene (UHMWPE). We evaluated the contact pressure, contact area, wear rate, wear depth, and volumetric wear under gait cycle loading conditions. Results. Conforming design inserts had the lower contact pressure and larger contact area. However, they also had the higher wear rate and volumetric wear. The improved wear performance was found with AMD inserts. In addition, the computationally predicted volumetric wear of crosslinked UHMWPE inserts was less than half that of standard UHMWPE inserts. Conclusion. Our results showed that increasing conformity may not be the sole predictor of wear performance; highly crosslinked mobile-bearing polyethylene inserts can also provide improvement in wear performance. These results provide improvements in design and materials to reduce wear in mobile-bearing UKA. Cite this article: Bone Joint Res 2019;8:563–569