Aims

Long-term clinical outcomes for ceramic-on-ceramic (CoC) bearings are encouraging. However, there is a risk of squeaking. Guidelines for the orientation of the acetabular component are defined from static imaging, but the position of the pelvis and thus the acetabular component during activities associated with edge-loading are likely to be very different from those measured when the patient is supine. We assessed the functional orientation of the acetabular component.

Objectives

Studies reporting specifically on squeaking in total hip arthroplasty have focused on cementless, and not on hybrid, fixation. We hypothesised that the cement mantle of the femur might have a damping effect on the sound transmitted through the metal stem. The objective of this study was to test the effect of cement on sound propagation along different stem designs and under different fixation conditions.

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm³/year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications.

Aims

We evaluated the short-term functional outcome and prevalence of bearing-specific generation of audible noise in 301 patients (336 hips) operated on with fourth generation (Delta) medium diameter head, ceramic-on-ceramic (CoC) total hip arthroplasties (THAs).

Aims. This study reports the mid-term results of total hip arthroplasty (THA) performed using a monoblock acetabular component with a large-diameter head (LDH) ceramic-on-ceramic (CoC) bearing. Patients and Methods. Of the 276 hips (246 patients) included in this study, 264 (96%) were reviewed at a mean of 67 months (48 to 79) postoperatively. Procedures were performed with a mini posterior approach. Clinical and radiological outcomes were recorded at regular intervals. A noise assessment questionnaire was completed at last follow-up. Results. There were four re-operations (1%) including one early revision for insufficient primary fixation (0.4%). No hip dislocation was reported. The mean University of California, Los Angeles (UCLA) activity score, 12-Item Short-Form Health Survey (SF-12) Mental Component Summary (MCS) score, SF-12 Physical Component Summary (PCS) score, Western Ontario and McMaster Universities Osteoarthritis Index (WOMAC) score, and Forgotten Joint Score (FJS) were 6.6 (2 to 10), 52.8 (25.5 to 65.7), 53.0 (27.2 to 66.5), 7.7 (0 to 63), and 88.5 (23 to 100), respectively. No signs of loosening or osteolysis were observed on radiological review. The incidence of squeaking was 23% (n = 51/225). Squeaking was significantly associated with larger head diameter (p < 0.001), younger age (p < 0.001), higher SF-12 PCS (p < 0.001), and UCLA scores (p < 0.001). Squeaking did not affect patient satisfaction, with 100% of the squeaking hips satisfied with the surgery. Conclusion. LDH CoC THAs have demonstrated excellent functional outcomes at medium-term follow-up, with very low revision rate and no dislocations. The high incidence of squeaking did not affect patient satisfaction or function. LDH CoC with a monoblock acetabular component has the potential to provide long term implant survivorship with unrestricted activity, while avoiding implant impingement, liner fracture at insertion, and hip instability. Cite this article: Bone Joint J 2018;100-B:1434–41

Squeaking arising from a ceramic-on-ceramic (CoC) total hip replacement (THR) may cause patient concern and in some cases causes patients to seek revision surgery. We performed a meta-analysis to determine the incidence of squeaking and the incidence of revision surgery for squeaking. A total of 43 studies including 16 828 CoC THR that reported squeaking, or revision for squeaking, were entered into the analysis. The incidence of squeaking was 4.2% and the incidence of revision for squeaking was 0.2%. The incidence of squeaking in patients receiving the Accolade femoral stem was 8.3%, and the incidence of revision for squeaking in these patients was 1.3%. Cite this article: Bone Joint J 2014;96-B:181–7

We investigated factors that were thought to be associated with an increased incidence of squeaking of ceramic-on-ceramic total hip replacements. Between June 1997 and December 2008 the three senior authors implanted 2406 primary total hip replacements with a ceramic-on-ceramic bearing surface. The mean follow-up was 10.6 years. The diagnosis was primary osteoarthritis in each case, and no patient had undergone previous surgery to the hip. We identified 74 squeaking hips (73 patients) giving an incidence of 3.1% at a mean follow-up of 9.5 years (4.1 to 13.3). Taller, heavier and younger patients were significantly more likely to have hips that squeaked. Squeaking hips had a significantly higher range of post-operative internal (p = 0.001) and external rotation (p = 0.003) compared with silent hips. Patients with squeaking hips had significantly higher activity levels (p = 0.009). A squeaking hip was not associated with a significant difference in patient satisfaction (p = 0.24) or Harris hip score (p = 0.34). Four implant position factors enabled good prediction of squeaking. These were high acetabular component inclination, high femoral offset, lateralisation of the hip centre and either high or low acetabular component anteversion. This is the largest study to date to examine patient factors and implant position factors that predispose to squeaking of a ceramic-on-ceramic hip. The results suggest that factors which increase the mechanical forces across the hip joint and factors which increase the risk of neck-to-rim impingement, and therefore edge-loading, are those that predispose to squeaking

Aims

The benefit of a dual-mobility acetabular component (DMC) for primary total hip arthroplasties (THAs) is controversial. This study aimed to compare the dislocation and complication rates when using a DMC compared to single-mobility (SM) acetabular component in primary elective THA using data collected at a single centre, and compare the revision rates and survival outcomes in these two groups.

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

Noise generation has been reported with ceramic-on-ceramic articulations in total hip replacement (THR). This study evaluated 208 consecutive Delta Motion THRs at a mean follow-up of 21 months (12 to 35). There were 141 women and 67 men with a mean age of 59 years (22 to 84). Patients were reviewed clinically and radiologically, and the incidence of noise was determined using a newly described assessment method. Noise production was examined against range of movement, ligamentous laxity, patient-reported outcome scores, activity level and orientation of the acetabular component. There were 143 silent hips (69%), 22 (11%) with noises other than squeaking, 17 (8%) with unreproducible squeaking and 26 (13%) with reproducible squeaking. Hips with reproducible squeaking had a greater mean range of movement (p < 0.001) and mean ligament laxity (p = 0.004), smaller median head size (p = 0.01) and decreased mean acetabular component inclination (p = 0.02) and anteversion angle (p = 0.02) compared with the other groups. There was no relationship between squeaking and age (p = 0.13), height (p = 0.263), weight (p = 0.333), body mass index (p = 0.643), gender (p = 0.07) or patient outcome score (p = 0.422). There were no revisions during follow-up. Despite the surprisingly high incidence of squeaking, all patients remain satisfied with their hip replacement.

Cite this article: Bone Joint J 2013;95-B:160–5.

Objectives

Our study aimed to examine not only the incidence but also the impact of noise from two types of total hip replacement articulations: ceramic-on-ceramic and ceramic-on-polyethylene.

The April 2014 Hip & Pelvis Roundup³⁶⁰ looks at: Recent arthroplasty and flight; whether that squeak could be a fracture; diagnosing early infected hip replacement; impaction grafting at a decade; whether squeaking is more common than previously thought; femoral offset associated with post THR outcomes; and periprosthetic fracture stabilisation.

We report the clinical and radiological outcomes of a series of contemporary cementless ceramic-on-ceramic total hip replacements (THRs) at ten years in patients aged ≤ 55 years of age. Pre- and post-operative activity levels are described. A total of 120 consecutive ceramic cementless THRs were performed at a single centre in 110 patients from 1997 to 1999. The mean age of the patients at operation was 45 years (20 to 55). At ten years, four patients had died and six were lost to follow-up, comprising ten hips. The mean post-operative Harris hip score was 94.7 (55 to 100). Radiological analysis was undertaken in 90 available THRs of the surviving 106 hips at final review: all had evidence of stable bony ingrowth, with no cases of osteolysis. Wear was undetectable. There were four revisions. The survival for both components with revision for any cause as an endpoint was 96.5% (95% confidence interval 94.5 to 98.7). The mean modified University of California, Los Angeles activity level rose from a mean of 6.4 (4 to 10) pre-operatively to 9.0 (6 to 10) at the ten-year post-operative period.

Alumina ceramic-on-ceramic bearings in cementless primary THR in this series have resulted in good clinical and radiological outcomes with undetectable rates of wear and excellent function in the demanding younger patient group at ten years.

Cite this article: Bone Joint J 2013;95-B:1603–9.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

This multicentre study analysed 12 alumina ceramic-on-ceramic components retrieved from squeaking total hip replacements after a mean of 23 months in situ (11 to 61). The rates and patterns of wear seen in these squeaking hips were compared with those seen in matched controls using retrieval data from 33 ‘silent’ hip replacements with similar ceramic bearings. All 12 bearings showed evidence characteristic of edge-loading wear. The median rate of volumetric wear was 3.4 mm³/year for the acetabular component, 2.9 mm³/year on the femoral heads and 6.3 mm³/year for head and insert combined. This was up to 45 times greater than that of previously reported silent ceramic-on-ceramic retrievals. The rate of wear seen in ceramic components revised for squeaking hips appears to be much greater than in that seen in retrievals from ‘silent’ hips.

Large femoral heads have become popular in total hip replacement (THR) as a method of reducing the risk of dislocation. However, if large heads are used in ceramic-on-ceramic THR, the liner must be thinner, which may increase the risk of fracture. To compare the rates of ceramic fracture and dislocation between 28 mm and 32 mm ceramic heads, 120 hips in 109 patients (51 men and 58 women, mean age 49.2 years) were randomised to THR with either a 28 mm or a 32 mm ceramic articulation. A total of 57/60 hips assigned to the 28 mm group and 55/60 hips assigned to the 32 mm group were followed for at least five years. No ceramic component fractures occured in any patient in either group. There was one dislocation in the 32 mm group and none in the 28 mm group (p = 0.464). No hip had detectable wear, focal osteolysis or prosthetic loosening. In our small study the 32 mm ceramic articulation appeared to be safe in terms of ceramic liner fracture.

Cite this article: Bone Joint J 2014;96-B:1459–63.

A total of 219 hips in 192 patients aged between 18 and 65 years were randomised to 28-mm metal-on-metal uncemented total hip replacements (THRs, 107 hips) or hybrid hip resurfacing (HR, 112 hips). At a mean follow-up of eight years (6.6 to 9.3) there was no significant difference between the THR and HR groups regarding rate of revision (4.0% (4 of 99) vs 5.8% (6 of 104), p = 0.569) or re-operation rates without revision (5.1% (5 of 99) vs 2.9% (3 of 104), p = 0.428). In the THR group one recurrent dislocation, two late deep infections and one peri-prosthetic fracture required revision, whereas in the HR group five patients underwent revision for femoral head loosening and one for adverse reaction to metal debris. The mean University of California, Los Angeles activity scores were significantly higher in HR (7.5 (sd 1.7) vs 6.9 (sd 1.7), p = 0.035), but similar mean Western Ontario and McMaster Universities Osteoarthritis Index scores were obtained (5.8 (sd 9.5) in HR vs 5.1 (sd 8.9) in THR, p = 0.615) at the last follow-up. Osteolysis was found in 30 of 81 THR patients (37.4%), mostly in the proximal femur, compared with two of 83 HR patients (2.4%) (p < 0.001). At five years the mean metal ion levels were < 2.5 μg/l for cobalt and chromium in both groups; only titanium was significantly higher in the HR group (p = 0.001). Although revision rates and functional scores were similar in both groups at mid-term, long-term survival analysis is necessary to determine whether one procedure is more advantageous than the other.

Cite this article: Bone Joint J 2013;95-B:1464–73.

Metallosis is a rare cause of failure after total knee replacement and has only previously been reported when there has been abnormal metal-on-metal contact. We describe 14 patients (15 knees) whose total knee replacement required revision for a new type of early failure caused by extensive metallosis. A modification of a cementless rotating platform implant, which had previously had excellent long-term survival, had been used in each case. The change was in the form of a new porous-beaded surface on the femoral component to induce cementless fixation, which had been used successfully in the fixation of acetabular and tibial components. This modification appeared to have resulted in metallosis due to abrasive two-body wear. The component has subsequently been recalled and is no longer in use. The presentation, investigation, and findings at revision are described and a possible aetiology and its implications are discussed.